Method for making infrared polarizing glasses
Assignee: Corning Inc
•
Filing: 1989-02-21
•
Granted: 1990-03-13
•
Expires: 2009-02-21
Abstract
Abstract This invention is directed to the preparation of glass articles exhibiting a relatively broad band of high contrast polarizing properties in the infrared region of the radiation spectrum from glasses containing silver halide particles selected from the group consisting of AgCl, AgBr, and AgI. The inventive method comprises the following five general steps: (a) melting a batch for a glass containing silver and at least one halide selected from the group consisting of chloride, bromide, and iodide; (b) cooling and shaping said melt into a glass article of a desired configuration; (c) subjecting said glass article to a temperature at least above the strain point, but not in excess of 75° C. above the softening point of the glass, for a sufficient length of time to cause the generation of silver halide particles therein selected from the group consisting of AgCl, AgBr, and AgI, said particles ranging in size between about 200-5000 Å; (d) elongating said glass article under stress at a temperature above the annealing point, but below that where said glass exhibits a viscosity of about 10 8 poises, such that said silver halide particles are elongated to an aspect ratio of at least 5:1 and aligned in the direction of the stress; and, thereafter, (e) exposing said elongated glass article to a reducing environment at a pressure greater than atmospheric pressure and at a temperature above about 250° C., but no higher than about 25° C. above the annealing point of the glass, for a period of time sufficient to develop a reducing surface layer on said glass article having a thickness of at least 10 microns wherein at least a portion of said elongated silver halide particles are reduced to elemental silver particles having aspect ratios greater than 2:1 which are deposited in and/or upon said elongated particles.
Inventors
- 👤 Kelly E. Jones
- 👤 Frederick E. Noll
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:57
CPC Classifications
C; C03; C03C; C03C4/00; C03C3/00; C03C3/04; C03C3/076; C03C3/11; C03C4/04; C03C4/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
338 words
A method for making a glass article exhibiting a relatively broad band of high contrast polarizing properties in the infrared region of the radiation spectrum from glasses which will be phase separable or will exhibit photochromic properties through the presence of silver halide particles therein selected from the group consisting of AgCl, AgBr, and AgI, which method comprises the steps of: (a) melting a batch for a glass containing silver and at least one halide selected from the group consisting of chloride, bromide, and iodide; (b) cooling and shaping said melt into a glass article of a desired configuration; (c) subjecting said glass article to a temperature at least above the strain point, but not in excess of 75° C. above the softening point of the glass, for a sufficient length of time to cause the generation of silver halide particles therein selected from the group consisting of AgCl, AgBr, and AgI, said particles ranging in size between about 200-5000 Å; (d) elongating said glass article under stress at a temperature above the annealing point, but below that where said glass exhibits a viscosity of about 10 8 poises, such that said silver halide particles are elongated to an aspect ratio of at least 5:1 and aligned in the direction of the stress; and, thereafter, (e) exposing said elongated glass article to a reducing environment at a pressure at least one atmosphere greater than atmospheric pressure and at a temperature above about 250° C., but no higher than about 25° C. above the annealing point of the glass, for a period of time sufficient to develop a reducing surface layer on said glass article having a thickness of at least 10 microns wherein at least a portion of said elongated silver halide particles are reduced to elemental silver particles having aspect ratios greater than 2:1 which are deposited in and/or upon said elongated particles, whereby said glass article exhibiting a relatively broad range of high contrast polarizing properties in the infrared region of the radiation spectrum is formed.
Claim 2
Independent Claim
338 words
A method for making a glass article exhibiting a relatively broad band of high contrast polarizing properties in the infrared region of the radiation spectrum from glasses which will be phase separable or will exhibit photochromic properties through the presence of silver halide particles therein selected from the group consisting of AgCl, AgBr, and AgI, which method comprises the steps of: (a) melting a batch for a glass containing silver and at least one halide selected from the group consisting of chloride, bromide, and iodide; (b) cooling and shaping said melt into a glass article of a desired configuration; (c) subjecting said glass article to a temperature at least above the strain point, but not in excess of 75° C. above the softening point of the glass, for a sufficient length of time to cause the generation of silver halide particles therein selected from the group consisting of AgCl, AgBr, and AgI, said particles ranging in size between about 200-5000 Å; (d) elongating said glass article under stress at a temperature above the annealing point, but below that where said glass exhibits a viscosity of about 10 8 poises, such that said silver halide particles are elongated to an aspect ratio of at least 5:1 and aligned in the direction of the stress; and, thereafter, (e) exposing said elongated glass article to a reducing environment at a pressure at least one atmosphere greater than atmospheric pressure and at a temperature above about 250° C., but no higher than about 25° C. above the annealing point of the glass, for a period of time sufficient to develop a reducing surface layer on said glass article having a thickness of at least 10 microns wherein at least a portion of said elongated silver halide particles are reduced to elemental silver particles having aspect ratios greater than 2:1 which are deposited in and/or upon said elongated particles, whereby said glass article exhibiting a relatively broad range of high contrast polarizing properties in the infrared region of the radiation spectrum is formed.
Claim 3
Dependent Claim
115 words
A method according to claim 1 wherein said photochromic glass consists essentially, expressed in terms of weight percent on the oxide basis, of 6-20% R 2 O, wherein R 2 O consists of 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, and 0-6% Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.004-0.02% CuO, 0.15-0.3% Ag, 0.1-0.25% Cl, and 0.1-0.2% Br, the molar ratio R 2 O:B 2 O 3 ranging between about 0.55-0.85, where the composition is essentially free from divalent metal oxides other than CuO, and the weight ratio Ag:(Cl+Br) ranging about 0.65-0.95.
Claim 4
Dependent Claim
117 words
A method according to claim 1 wherein said phase separable glass is essentially free from CuO and consists essentially, expressed in terms of weight percent on the oxide basis, of 6-20% R 2 O, wherein R 2 O consists of 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, and 0-6% Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.15-0.3% Ag, 0.1-0.25% Cl, and 0.1-0.2% Br, the molar ratio R 2 O:B 2 O 3 ranging between about 0.55-0.85, where the composition is essentially free from divalent metal oxides, and the weight ratio Ag:(Cl+Br) ranging about 0.65-0.95.
Claim 5
Dependent Claim
129 words
A method according to claim 1 wherein said phase separable glass consists essentially, expressed in terms of weight percent on the oxide basis, of 6-20% R 20 , wherein R 20 consists of 0-2.5% Li 2 O, 0-9% Na 2 O, 0-17% K 2 O, and 0-6% Cs 2 O, 14-23% B 2 O 3 , 5-25% Al 2 O 3 , 0-25% P 2 O 5 , 20-65% SiO 2 , 0.004-0.02% CuO, 0.15-0.3% Ag, 0.1-0.25% Cl, and 0.1-0.2% Br, the molar ratio R 2 O: B 2 O 3 ranging about 0.55-0.85, where the composition is essentially free from divalent metal oxides other than CuO, the weight ratio Ag:(Cl+Br) ranging about 0.65-0.95, and the molar ratio (R 2 O--Al 2 O 3 ):B 2 O 3 <0.25.
Claim 6
Dependent Claim
54 words
A method according to claim 1 wherein said phase separable glass contains silver halide particles and copper and consists essentially, expressed in terms of weight percent on the oxide basis, of about 5-12% alkali metal oxides, 27-35% B 2 O 3 , 1-15% Al 2 O 3 , and the remainder SiO 2 .
Claim 7
Dependent Claim
45 words
A method according to claim 5 wherein said glass consists essentially, expressed in terms of weight percent on the oxide basis, of ______________________________________
SiO.sub.2
51.8 Na.sub.2 O
9.8 Br 1.2
B.sub.2 O.sub.3
31.0 Ag 0.18 F 1.2
Al.sub.2 O.sub.3
7.8 Cl 0.52 CuO 0.03.
______________________________________
Claim 8
Dependent Claim
57 words
A method according to claim 1 wherein said photochromic glass contains silver halide particles and copper and consists essentially, expressed in terms of weight percent on the oxide basis, of about 5-12% alkali metal oxides, 27-35% B 2 O 3 , 1-15% Al 2 O 3 , at least 0.01% CdO, and the remainder SiO 2 .
Claim 9
Dependent Claim
22 words
A method according to claim 1 wherein said band of polarizing properties extends over a range of wavelengths of at least 2000Å.
Claim 10
Dependent Claim
15 words
A method according to claim 1 wherein said reducing environment consists of a hydrogen-containing atmosphere.
Claim 11
Dependent Claim
27 words
A method according to claim 9 wherein said period of time sufficient to develop a reducing surface layer on said glass article is at least two hours.
References Cited (Backward Citations)
US3653863A
Cited
US3892582A
Cited
US4190451A
Cited
US4304584A
Cited
US4549795A
Cited
US4390592A
Cited
US4479819A
Cited
US4486213A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-12 | 1993-09-11 | 1994-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-12 | 1997-09-11 | 1998-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-12 | 2001-09-11 | 2002-03-13 | $7700.00 | Window Closed / Lapsed |