Sensor and method for indicating the presence of a low magnetic field using high critical temperature superconductor ceramic material to absorb electromagnetic energy
Assignee: Drexel University
•
Filing: 1988-04-06
•
Granted: 1990-03-06
•
Expires: 2008-04-06
Abstract
Abstract A sensor and method for indicating the presence of a low magnetic field using high critical temperature superconductor ceramic material is comprised of a sensing element consisting essentially of the high critical temperature superconductor ceramic material without the need for further processing. The sensing element is cooled to a temperature below the critical temperature of the superconductor material, whereby the sensing element becomes superconducting. Electromagnetic energy is applied to the sensing element, a first portion of the energy being absorbed by the sensing element. The amount of the energy absorbed by the sensing element is detected. The sensing element is modulated to provide a reference signal and is biased to a predetermined absorption reference value, whereby a magnetic field of about 10 -10 tesla or less near the sensing element results in a change in the absorption of the magnetic energy by the sensing element, the change being detected to indicate the presence of the magnetic field.
Inventors
- 👤 Som Dev Tyagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:34
CPC Classifications
G; G01; G01R; G01R33/00; G01R33/02; G01R33/035; Y; Y10; Y10S; Y10S505/00; Y10S505/70; Y10S505/701
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
198 words
A sensor for use with a source of electromagnetic energy for indicating the presence of a low magnetic field with a sensitivity of at least 10 -10 tesla, the sensor comprising: a sensing element consisting essentially of a high critical temperature superconductor ceramic oxide material without the need for further processing, said critical temperature being above 77° Kelvin; means for cooling the sensing element to a temperature below the critical temperature of the superconductor material whereby the sensing element becomes superconducting; means for applying electromagnetic energy from the source to the sensing element whereby a first portion of the applied energy is absorbed by the sensing element; means for detecting the amount of the energy absorbed by the sensing element; and means modulating the sensing element for providing a reference signal for phase-sensitive detection and for biasing the electromagnetic energy absorption characteristics of the sensing element to a predetermined absorption reference value whereby a magnetic field of about 10 -10 tesla or less near the sensing element results in a change in the absorption of the electromagnetic energy by the sensing element, the change being detected by the detecting means to indicate the presence of the magnetic field.
Claim 2
Dependent Claim
198 words
A sensor for use with a source of electromagnetic energy for indicating the presence of a low magnetic field with a sensitivity of at least 10 -10 tesla, the sensor comprising: a sensing element consisting essentially of a high critical temperature superconductor ceramic oxide material without the need for further processing, said critical temperature being above 77° Kelvin; means for cooling the sensing element to a temperature below the critical temperature of the superconductor material whereby the sensing element becomes superconducting; means for applying electromagnetic energy from the source to the sensing element whereby a first portion of the applied energy is absorbed by the sensing element; means for detecting the amount of the energy absorbed by the sensing element; and means modulating the sensing element for providing a reference signal for phase-sensitive detection and for biasing the electromagnetic energy absorption characteristics of the sensing element to a predetermined absorption reference value whereby a magnetic field of about 10 -10 tesla or less near the sensing element results in a change in the absorption of the electromagnetic energy by the sensing element, the change being detected by the detecting means to indicate the presence of the magnetic field.
Claim 3
Dependent Claim
24 words
The sensor as recited in claim 1, wherein the sensing element consists of a single one milligram sample of high critical temperature superconductor material.
Claim 4
Dependent Claim
21 words
The sensor as recited in claim 1, wherein the sensing element consists of high critical temperature superconductor material in powder form.
Claim 5
Dependent Claim
17 words
The sensor as recited in claim 3, wherein the superconductor powder is embedded in non-magnetic epoxy resin.
Claim 6
Dependent Claim
28 words
The sensor as recited in claim 1, further including magnetic shielding means at least partially surrounding the sensing element for shielding the sensing element from spurious magnetic fields.
Claim 7
Dependent Claim
19 words
The sensor as recited in claim 5, wherein the magnetic shielding means is comprised of a mu metal housing.
Claim 8
Dependent Claim
28 words
The sensor as recited in claim 1, wherein the modulating and biasing means comprises an air core coil for creating a biasing magnetic field proximate the sensing element.
Claim 9
Dependent Claim
23 words
The sensor as recited in claim 7, wherein the magnetic field generated by the coil is in the range of 0-10 -4 tesla.
Claim 10
Dependent Claim
48 words
The sensor as recited in claim 1, further including means for indicating the absorption characteristics of the sensing element and the change in the absorption characteristics of the sensing element as a result of the magnetic field to provide an indication of the strength of the magnetic field.
Claim 11
Dependent Claim
21 words
The sensor as recited in claim 1, wherein the frequency of the electromagnetic energy source is in the radio frequency range.
Claim 12
Dependent Claim
21 words
The sensor as recited in claim 1, wherein the frequency of the electromagnetic energy source is in the microwave frequency range.
Claim 13
Dependent Claim
19 words
The sensor as recited in claim 11, wherein the frequency of the microwave energy is within the X band.
Claim 14
Dependent Claim
19 words
The sensor as recited in claim 11, wherein the frequency of the microwave energy is within the K band.
Claim 15
Dependent Claim
19 words
The sensor as recited in claim 1, wherein the sensing element is supported by a carrier of non-magnetic material.
Claim 16
Dependent Claim
14 words
The sensor as recited in claim 14 wherein the carrier is a quartz tube.
Claim 17
Independent Claim
182 words
A method for indicating the presence of a low magnetic field with a sensitivity of at least 10 - tesla, comprising the steps of: providing a sensing element consisting essentially of a high critical temperature superconductor ceramic oxide material without the need for further processing, said critical temperature being above 77° Kelvin; cooling the sensing element to a temperature below the critical temperature of the superconductor material, whereby the sensing element becomes superconducting; applying electromagnetic energy to the sensing element whereby a first portion of the energy is absorbed ,by the sensing element; detecting the amount of energy absorbed by the sensing element; modulating the sensing element to provide a reference signal for phase-sensitive detection; biasing the electromagnetic energy absorption characteristics of the sensing element to a predetermined absorption reference value; subjecting the sensing element to a magnetic field of about 10 -10 or less, resulting in a change in the absorption of the electromagnetic energy by the sensing element; and detecting the change in the absorption of the energy by the sensing element to indicate the presence of the magnetic field.
Claim 18
Independent Claim
182 words
A method for indicating the presence of a low magnetic field with a sensitivity of at least 10 - tesla, comprising the steps of: providing a sensing element consisting essentially of a high critical temperature superconductor ceramic oxide material without the need for further processing, said critical temperature being above 77° Kelvin; cooling the sensing element to a temperature below the critical temperature of the superconductor material, whereby the sensing element becomes superconducting; applying electromagnetic energy to the sensing element whereby a first portion of the energy is absorbed ,by the sensing element; detecting the amount of energy absorbed by the sensing element; modulating the sensing element to provide a reference signal for phase-sensitive detection; biasing the electromagnetic energy absorption characteristics of the sensing element to a predetermined absorption reference value; subjecting the sensing element to a magnetic field of about 10 -10 or less, resulting in a change in the absorption of the electromagnetic energy by the sensing element; and detecting the change in the absorption of the energy by the sensing element to indicate the presence of the magnetic field.
Claim 19
Dependent Claim
49 words
The method as recited in claim 16 further including the step of indicating the absorption characteristics of the sensing element and the change in the absorption characteristics of the sensing element as a result of the magnetic field to provide an indication of the strength of the magnetic field.
Claim 20
Dependent Claim
22 words
The method as recited in claim 16 further including the steps of shielding the sensing element from exposure to spurious magnetic fields.
Claim 21
Dependent Claim
20 words
The method as recited in claim 16 wherein the frequency of the electromagnetic energy is in the radio frequency range.
Claim 22
Dependent Claim
20 words
The method as recited in claim 16 wherein the frequency of the electromagnetic energy is in the microwave frequency range.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-03-05 | 1993-09-04 | 1994-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-03-05 | 1997-09-04 | 1998-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-03-05 | 2001-09-04 | 2002-03-06 | $7700.00 | Window Closed / Lapsed |