Abstract This invention relates to a method for controlling or limiting the formation of an oxide layer on a metallic substrate such as nickel or nickel alloy, over which a polymeric plating resist has been placed, then selectively removed by a focussed excimer laser beam applied thereto. The method comprises the steps of applying a carbon-containing polymeric plating resist to a metal substrate having an oxide layer thereon of a thickness between about 20 to 40 ANGSTROM . Thereafter, a selected area of said resist coated metal substrate is subjected to a single shot from an excimer laser to ablate said resist from within said area, wherein the laser energy is absorbed primarily at the metallic substrate and the energy density of the said laser is in excess of that required to ablate so as to produce a thin uniform layer of oxide over said substrate, said oxide layer, principally nickel oxide, having a thickness no greater than about 7 ANGSTROM . Ancillary features of this method include improved substrate surface characteristics by the development of a carbon enriched sub-surface layer beneath the ablated area.
A method for controlling the formation of an oxide layer on a metallic substrate over which a polymeric plating resist has been placed, then selectively removed by a focussed excimer laser beam applied thereto, comprising the steps of applying a carbon-containing polymeric plating resist to a metal substrate having a natural oxide layer thereon of a thickness between about 20 to 40 Å, subjecting a selected area of said resist coated metal substrate to a single shot from an excimer laser to ablate said resist from within said area, wherein the laser energy is absorbed primarily at the metallic substrate and the energy density of the said laser is in excess of that required to ablate so as to produce a thin uniform layer of oxide having a thickness no greater than about 7 Å over said substrate, said substrate exhibiting a carbon enriched sub-surface layer beneath the ablated area to improve the surface characteristics thereof.
Claim 2
Independent Claim
156 words
A method for controlling the formation of an oxide layer on a metallic substrate over which a polymeric plating resist has been placed, then selectively removed by a focussed excimer laser beam applied thereto, comprising the steps of applying a carbon-containing polymeric plating resist to a metal substrate having a natural oxide layer thereon of a thickness between about 20 to 40 Å, subjecting a selected area of said resist coated metal substrate to a single shot from an excimer laser to ablate said resist from within said area, wherein the laser energy is absorbed primarily at the metallic substrate and the energy density of the said laser is in excess of that required to ablate so as to produce a thin uniform layer of oxide having a thickness no greater than about 7 Å over said substrate, said substrate exhibiting a carbon enriched sub-surface layer beneath the ablated area to improve the surface characteristics thereof.
Claim 3
Dependent Claim
16 words
The method according to claim 1 wherein said metallic substrate is a nickel plated copper alloy.
Claim 4
Dependent Claim
24 words
The method according to claim 2 wherein said energy density is from 10 to 100% greater than the energy required to effect such ablation.
Claim 5
Dependent Claim
23 words
The method according to claim 3 wherein said energy density is a value between about 2.0 J/cm 2 and 2.50 J/cm 2 .