Aluminum material for brazing, method of manufacturing same, and method of manufacturing heat exchanger made of aluminum alloy
Assignee: Denso Corp
•
Filing: 1988-09-06
•
Granted: 1990-02-20
•
Expires: 2008-09-06
Abstract
Abstract An aluminum material for brazing, comprising a core made of aluminum or an aluminum alloy, and a layer coated on the surface of the core. The layer is made of zinc or an alloy of zinc-and-aluminum and a brazing alloy having a melting point which is lower than that of the core by a predetermined value. The zinc or the alloy of zinc-and-aluminum and the brazing alloy have different melting points. Also disclosed are a method of manufacturing an aluminum material for brazing and a method of manufacturing an aluminum alloy heat exchanger by use of the Al material for brazing.
Inventors
- 👤 Kengi Negura
- 👤 Ken Yamamoto
- 👤 Shigeo Ito
- 👤 Masahiro Shimoya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:40
CPC Classifications
F; F28; F28F; F28F21/00; F28F21/08; F28F21/089; B; B23; B23K; B23K1/00; B23K1/0008; B23K1/0012; B23K1/19; B23K35/00; B23K35/001; B23K35/002; B23K35/22; B23K35/24; B23K35/28; B23K35/286; B23K35/288; F28F21/081; F28F21/084; Y; Y10; Y10S; Y10S165/00; Y10S165/905; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12021; Y10T428/12229
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
132 words
A method of manufacturing a brazing aluminum material comprising: a first step of forming a core having a predetermined shape by extruding aluminum or an alloy of aluminum; a second step of forming a first coated layer by spraying zinc or an alloy of zinc-and-aluminum on the surface of the just extruded core; and a third step of forming a second coated layer by spraying a brazing alloy of aluminum and silicon or a brazing alloy of aluminum, silicon, and zinc on the surface of said first coated layer forming a coating having a zinc concentration gradient, wherein said second layer has a melting point higher than said first layer and wherein the outer surface of said second layer has a zinc concentration lower than the inner surface of said first layer.
Claim 2
Independent Claim
132 words
A method of manufacturing a brazing aluminum material comprising: a first step of forming a core having a predetermined shape by extruding aluminum or an alloy of aluminum; a second step of forming a first coated layer by spraying zinc or an alloy of zinc-and-aluminum on the surface of the just extruded core; and a third step of forming a second coated layer by spraying a brazing alloy of aluminum and silicon or a brazing alloy of aluminum, silicon, and zinc on the surface of said first coated layer forming a coating having a zinc concentration gradient, wherein said second layer has a melting point higher than said first layer and wherein the outer surface of said second layer has a zinc concentration lower than the inner surface of said first layer.
Claim 3
Independent Claim
212 words
A method of manufacturing an aluminum alloy heat exchanger comprising: a first step of forming a tube through which a heat exchange fluid is made to flow by extruding aluminum or an alloy of aluminum; a second step of forming a first coated layer by spraying zinc or an alloy of zinc-and-aluminum on the surface of the just extruded core; a third step of forming a second coated layer by spraying a brazing alloy on the surface of said first coated layer forming a coating having a zinc concentration gradient, wherein said second layer has a melting point higher than said first layer and wherein the outer surface of said second layer has a zinc concentration lower than the inner surface of said first layer. a fourth step of forming fins made of aluminum alloy which fins are to be bonded to said tube; a fifth step of forming an assembly by contacting said fins with said tube with said first and second coated layers being formed thereon; and a sixth step of brazing said tube and said fins by heating said assembly in a furnace to a temperature which is the melting point of said second coated layer or above and which is less than the melting point of said tube.
Claim 4
Independent Claim
212 words
A method of manufacturing an aluminum alloy heat exchanger comprising: a first step of forming a tube through which a heat exchange fluid is made to flow by extruding aluminum or an alloy of aluminum; a second step of forming a first coated layer by spraying zinc or an alloy of zinc-and-aluminum on the surface of the just extruded core; a third step of forming a second coated layer by spraying a brazing alloy on the surface of said first coated layer forming a coating having a zinc concentration gradient, wherein said second layer has a melting point higher than said first layer and wherein the outer surface of said second layer has a zinc concentration lower than the inner surface of said first layer. a fourth step of forming fins made of aluminum alloy which fins are to be bonded to said tube; a fifth step of forming an assembly by contacting said fins with said tube with said first and second coated layers being formed thereon; and a sixth step of brazing said tube and said fins by heating said assembly in a furnace to a temperature which is the melting point of said second coated layer or above and which is less than the melting point of said tube.
Claim 5
Dependent Claim
39 words
A method of manufacturing an aluminum alloy heat exchanger according to claim 5, wherein said tube is a multi-hole tube having a plurality of holes through which a heat exchange fluid flows, said tube being bent in zigzag shape.
Claim 6
Dependent Claim
141 words
An aluminum material for brazing, comprising: an extruded core made of aluminum or an aluminum alloy; a first layer sprayed on the surface of said core, said first layer being made of zinc or an alloy of zinc and aluminum; and a second layer sprayed on the surface of said first layer said second layer being made of a brazing alloy of aluminum and silicon or another brazing alloy of aluminum, silicon and zinc and having a melting point higher than said first layer, said first layer and said second layer forming a coated layer which has a gradient of concentration of zinc so that the concentration of zinc existing in the viCinity of the outer surface of the layer is lower than that of zinc existing in the vicinity of an interface defined between the core and the coated layer.
Claim 7
Dependent Claim
141 words
An aluminum material for brazing, comprising: an extruded core made of aluminum or an aluminum alloy; a first layer sprayed on the surface of said core, said first layer being made of zinc or an alloy of zinc and aluminum; and a second layer sprayed on the surface of said first layer said second layer being made of a brazing alloy of aluminum and silicon or another brazing alloy of aluminum, silicon and zinc and having a melting point higher than said first layer, said first layer and said second layer forming a coated layer which has a gradient of concentration of zinc so that the concentration of zinc existing in the viCinity of the outer surface of the layer is lower than that of zinc existing in the vicinity of an interface defined between the core and the coated layer.
References Cited (Backward Citations)
JPS51950A
Cited
JPS54641A
Cited
JPS5732872A
Cited
JPS58204169A
Cited
JPS5910467A
Cited
JPS59229280A
Cited
JPS6021176A
Cited
US4732311A
Cited
JPS613662A
Cited
JPS6174771A
Cited
JPS62858A
Cited
JPS61232060A
Cited
JPS61235072A
Cited
US4757934A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-19 | 1993-08-21 | 1994-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-19 | 1997-08-21 | 1998-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-19 | 2001-08-21 | 2002-02-20 | $7700.00 | Window Closed / Lapsed |