Process of producing lightweight and corrosion-resistant heat exchanger
Assignee: Furukawa Aluminum Co Ltd
•
Filing: 1987-01-21
•
Granted: 1988-03-22
•
Expires: 2007-01-21
Abstract
Abstract A method of producing a lightweight and corrosion-resistant heat exchanger is disclosed. An aluminum tube with a plurality of passage bores therein is formed by extrusion. A layer of a brazing material comprising an aluminum alloy having an electrode potential value lower than that of the tube material is formed on the tube surface with the aid of a non-corrosive flux. The tube is bent into a zigzag winding form so as to have a plurality of substantially parallel runs. Corrugated fin members of aluminum or aluminum alloy are placed between respective adjacent runs of the tube. The tube and the fin members are heated together up to the melting point of the brazing material so that they are bonded together by the brazing material to form the heat exchanger.
Inventors
- 👤 Yoshiharu Hasegawa
- 👤 Yutaka Murakami
- 👤 Toshio Ohara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:57
CPC Classifications
F; F28; F28D; F28D1/00; F28D1/02; F28D1/04; F28D1/047; F28D1/0477; F28D1/0478; B; B23; B23K; B23K1/00; B23K1/0008; B23K1/0012; F28F; F28F1/00; F28F1/10; F28F1/12; F28F1/126
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
235 words
A method of producing a lightweight and corrosion-resistant heat exchanger, comprising the steps of: forming a tube having a plurality of passage bores by extrusion form one of aluminum and an aluminum alloy; coating at least a part of the outer periphery of said tube, as viewed in cross-section, with a layer of a brazing material with the aid of a non-corrosive flux applied to one of said tube and said layer such that said layer of brazing material extends over the entire length of said tube, said brazing material comprising an aluminum alloy including zinc silicon and having an electrode potential value lower than that of the material of said tube; bending said tube into a substantially zigzag winding form such that the bent tube has a plurality of substantially parallel runs and a plurality of bent portions each interconnecting an adjacent pair of said runs; placing corrugated fin members of one of aluminum and an aluminum alloy between adjacent runs of said tube, respectively, such that said fin members are not in contact with said bent portions of said tube, said fin members being uncoated with any layer of brazing material and each having a thickness of less than 0.12 mm; and heating said tube and said corrugated fin members at least to the melting point of said brazing material to bond said corrugated fin members to said tube by said brazing material.
Claim 2
Independent Claim
235 words
A method of producing a lightweight and corrosion-resistant heat exchanger, comprising the steps of: forming a tube having a plurality of passage bores by extrusion form one of aluminum and an aluminum alloy; coating at least a part of the outer periphery of said tube, as viewed in cross-section, with a layer of a brazing material with the aid of a non-corrosive flux applied to one of said tube and said layer such that said layer of brazing material extends over the entire length of said tube, said brazing material comprising an aluminum alloy including zinc silicon and having an electrode potential value lower than that of the material of said tube; bending said tube into a substantially zigzag winding form such that the bent tube has a plurality of substantially parallel runs and a plurality of bent portions each interconnecting an adjacent pair of said runs; placing corrugated fin members of one of aluminum and an aluminum alloy between adjacent runs of said tube, respectively, such that said fin members are not in contact with said bent portions of said tube, said fin members being uncoated with any layer of brazing material and each having a thickness of less than 0.12 mm; and heating said tube and said corrugated fin members at least to the melting point of said brazing material to bond said corrugated fin members to said tube by said brazing material.
Claim 3
Dependent Claim
22 words
A process as claimed in claim 1, wherein said coating step includes spraying said brazing material in molten state on said tube.
Claim 4
Dependent Claim
16 words
A rpocess as claimed in claim 1, wherein said non-corrosive flux is of potassium fluoroaluminate type.
Claim 5
Dependent Claim
33 words
A process as claimed in claim 1, wherein said brazing material essentially consists of 10.0 wt % of silicon, 1.0 wt % of zinc and the balance formed by aluminum and inevitable impurities.
Claim 6
Dependent Claim
33 words
A process as claimed in claim 1, wherein said brazing material essentially consists of 10.0 wt % of silicon, 0.7 wt % of zinc and the balance formed by aluminum and inevitable impurities.
Claim 7
Dependent Claim
23 words
A process as claimed in claim 1, wherein said corrugated fin members each have a thickness of from 0.07 mm to 0.16 mm.
Claim 8
Dependent Claim
37 words
A process as claimed in claim 1, wherein the material of said corrugated fin members essentially consists of 1.2 wt % of Mn, 1.0 wt % of Zn and the balance formed by aluminum and inevitable impurities.
Claim 9
Dependent Claim
37 words
A process as claimed in claim 1, wherein the material of said corrugated fin members essentially consists of 1.2 wt % of Mn, 0.5 wt % of Zn and the balance formed by aluminum and inevitable impurities.
Claim 10
Dependent Claim
53 words
A process as claimed in claim 1, wherein the step of heating said corrugated fin members to bond them to said tube is conducted by heating said tube, said layer of said brazing material and said corrugated fin members at 590° to 605° C. for about 10 minutes in a nitrogen gas atmosphere.
Claim 11
Dependent Claim
42 words
A process as claimed in claim 1, further including a step of applying an additional layer of the same kind as the first said flux to the outer surface of said layer of said brazing material in advance of said heating step.
Claim 12
Dependent Claim
43 words
A process as claimed in claim 1, wherein said layer of brazing material is formed by preparing a foil of said brazing material and applying said foil to said tube with the aid of said non-corrosive flux in advance of said bending step.
Claim 13
Dependent Claim
22 words
A process as claimed in claim 11, wherein said foil of brazing material has a thickness ranging from 20 to 200 μm.
Claim 14
Dependent Claim
34 words
A process as claimed in claim 11, wherein said tube has a generally planar cross-section having two major surfaces and each of said major surfaces is covered by said foil of said brazing material.
Claim 15
Dependent Claim
36 words
A process as claimed in claim 11, wherein said tube has a generally planar cross-section and substantially the entire circumferential surface of said tube is covered by a pair of such foils of said brazing material.
Claim 16
Dependent Claim
17 words
A process as claimed in claim 1, wherein said tube-bending step is conducted after said coating step.
Claim 17
Dependent Claim
17 words
A process as claimed in claim 2, wherein said tube-bending step is conducted before said coating step.
Claim 18
Dependent Claim
17 words
A process as claimed in claim 2, wherein said tube-bending step is conducted after said spraying step.
Claim 19
Dependent Claim
17 words
A process as claimed in claim 2, wherein said tube-bending step is conducted before said spraying step.
Claim 20
Dependent Claim
33 words
A process as claimed in claim 1, wherein said brazing material essentially consists of 10.0 wt % of silicon, 5.0 wt % of zinc and the balance formed by aluminium and inevitable impurities.
Claim 21
Dependent Claim
33 words
A process as claimed in claim 1, wherein said brazing material essentially consists of 10.0 wt % of silicon, 10.0 wt % of zinc and the balance formed by aluminium and inevitable impurities.
Claim 22
Dependent Claim
50 words
A process as claimed in claim 11, wherein said foil is applied to said tube and then said tube with said foil thereon is heated in an anti-oxidating atmosphere to a temperature at which said foil is molten and fixed to said tube with the aid of said non-corrosive flux.
References Cited (Backward Citations)
GB917296A
Cited
US3440712A
Cited
US3748729A
Cited
US3951328A
Cited
US3889745A
Cited
US3985283A
Cited
US3971501A
Cited
JPS5237457A
Cited
US4233719A
Cited
JPS5777683A
Cited
JPS5784826A
Cited
JPS58128384A
Cited
JPS58173079A
Cited
US4477011A
Cited
JPS59173530A
Cited
JPS60145268A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-03-22 | 1991-09-21 | 1992-03-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-03-22 | 1995-09-21 | 1996-03-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-03-22 | 1999-09-21 | 2000-03-22 | $7700.00 | Window Closed / Lapsed |