US4900646A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Electrophotographic recording material and method of producing it
Assignee: AEG AG
•
Filing: 1988-05-24
•
Granted: 1990-02-13
•
Expires: 2008-05-24
Abstract
Abstract A method of producing an electrophotographic recording material, in which an aluminum substrate is coated with a blocking layer. The blocking layer is coated with a layer of amorphous silicon by direct current magnetron cathode sputtering. At least one sputter target containing silicon is used, and a power density of from about 2.0 W/cm 2 to about 30 W/cm 2 is used for the sputtering. The sputtering is performed in an atmosphere containing hydrogen and an inert gas, with a total pressure of inert gas and hydrogen being in a range from about 1×10 -3 to about 10×10 -3 mbar. This produces a layer of amorphous silicon having a hydrogen content of more than 40 atom %, an inert gas content in a range of 0.01 to 10 atom %, and in which the relative peak heights of the low and high temperature peaks during hydrogen effusion are approximately equal. The amorphous silicon layer is then coated with a cover layer.
Inventors
- 👤 Wilhelm Senske
- 👤 Ekkehard Niemann
- 👤 Roland Herkert
- 👤 Guido Blang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:09
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/02; G03G5/04; G03G5/08; G03G5/082; G03G5/08214; G03G5/08278; G03G5/08285
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
144 words
A method of producing an electrophotographic recording material, comprising: a first step of coating an aluminum substrate with a blocking layer which is a member of the group consisting of SiO x , SiC x , amorphous carbon and doped, amorphous silicon; a second step of coating said blocking layer with a layer of amorphous silicon by direct current magnetron cathode sputtering using at least one sputter target containing silicon, wherein a power density of from about 2.0 W/cm 2 to about 30 W/cm 2 is used for said sputtering, and wherein said second step is performed in an atmosphere containing hydrogen and at least one inert gas, wherein the total pressure of inert gas and hydrogen lies in a range from about 1×10 -3 to about 10×10 -3 mbar; and a third step of coating said amorphous silicon layer with a cover layer.
Claim 2
Independent Claim
144 words
A method of producing an electrophotographic recording material, comprising: a first step of coating an aluminum substrate with a blocking layer which is a member of the group consisting of SiO x , SiC x , amorphous carbon and doped, amorphous silicon; a second step of coating said blocking layer with a layer of amorphous silicon by direct current magnetron cathode sputtering using at least one sputter target containing silicon, wherein a power density of from about 2.0 W/cm 2 to about 30 W/cm 2 is used for said sputtering, and wherein said second step is performed in an atmosphere containing hydrogen and at least one inert gas, wherein the total pressure of inert gas and hydrogen lies in a range from about 1×10 -3 to about 10×10 -3 mbar; and a third step of coating said amorphous silicon layer with a cover layer.
Claim 3
Dependent Claim
23 words
A method as defined in claim 1, wherein said atmosphere has a hydrogen content in a range from about 30 to about 60%.
Claim 4
Dependent Claim
21 words
A method as defined in claim 1, wherein the substrate temperature is in a range between 20° C. and 300° C.
Claim 5
Dependent Claim
34 words
A method as defined in claim 1, wherein at least one sputter target is composed of one of p-conductive and n-conductive crystalline silicon having a resistance lower than or equal to 10 Ω cm.
Claim 6
Dependent Claim
31 words
A method as defined in claim 1, wherein the power density for direct current cathode sputtering is in a range from about 2.0 W/cm 2 to about 13 W/cm 2 .
Claim 7
Dependent Claim
31 words
A method as defined in claim 1, wherein the inert gas is argon and the argon content in the amorphous silicon is in a range from 0.01 to 0.1 atom %.
Claim 8
Dependent Claim
72 words
An electrophotographic recording material, disposed on an aluminum substrate, comprising: a blocking layer, disposed on the aluminum substrate; an amorphous silicon layer disposed on said blocking layer, said amorphous silicon layer containing argon at 0.01 to 10 atom %, hydrogen at more than 40 atom %, and relative peak heights of low and high temperature peaks during hydrogen effusion which are approximately equal; and a cover layer disposed on said silicon layer.
Claim 9
Dependent Claim
72 words
An electrophotographic recording material, disposed on an aluminum substrate, comprising: a blocking layer, disposed on the aluminum substrate; an amorphous silicon layer disposed on said blocking layer, said amorphous silicon layer containing argon at 0.01 to 10 atom %, hydrogen at more than 40 atom %, and relative peak heights of low and high temperature peaks during hydrogen effusion which are approximately equal; and a cover layer disposed on said silicon layer.
Claim 10
Dependent Claim
29 words
A recording material as defined in claim 5, wherein the amorphous silicon contains at least one of oxygen and carbon in a range from 0 to 10 atom %.
Claim 11
Dependent Claim
33 words
A recording material as defined in claim 7, wherein the blocking layer is composed of one from the group consisting of SiO x , SiC x , amorphous carbon and doped, amorphous silicon.
Claim 12
Dependent Claim
33 words
A recording material as defined in claim 7, wherein the cover layer is composed of one from the group consisting of SiO x , SiC x , amorphous carbon and SiN x .
Claim 13
Dependent Claim
18 words
A recording material as defined in claim 7, wherein the amorphous silicon layer is thicker than 10 μm.
Claim 14
Dependent Claim
60 words
An electrophotographic recording material, which is deposited on a substrate by means of direct current magnetron sputtering, comprising: a blocking layer, disposed on the substrate; an amorphous silicon layer disposed on the blocking layer which contains more than 40 atom % of hydrogen and 0.01 to 10 atom % of argon; and a cover layer disposed on the amorphous layer.
Claim 15
Dependent Claim
60 words
An electrophotographic recording material, which is deposited on a substrate by means of direct current magnetron sputtering, comprising: a blocking layer, disposed on the substrate; an amorphous silicon layer disposed on the blocking layer which contains more than 40 atom % of hydrogen and 0.01 to 10 atom % of argon; and a cover layer disposed on the amorphous layer.
Claim 16
Dependent Claim
20 words
A recording material of claim 12, wherein about half of the hydrogen in the amorphous silicon layer is chemically bound.
Claim 17
Dependent Claim
19 words
A recording material of claim 12, wherein about half of the hydrogen fills voids in the amorphous silicon layer.
Claim 18
Dependent Claim
21 words
A recording material of claim 12, wherein the amorphous silicon layer has a microstructure which is substantially free of columnar growth.
Claim 19
Dependent Claim
25 words
The method of claim 1, wherein the coating of the blocking layer with amorphous silicon is at a deposition rate of greater than 10 μm/h.
Claim 20
Dependent Claim
71 words
In a method for the production of an electrophotographic recording material by depositing amorphous silicon on a blocking layer on a substrate by means of direct current magnetron cathode sputtering, the improvement which comprises: depositing amorphous silicon in a hydrogen- and argon-containing atmosphere at a total hydrogen and argon pressure in the range of 10 -2 to 10 -3 mbar and an effective density of 2 to 30 W/cm 2 .
Claim 21
Dependent Claim
71 words
In a method for the production of an electrophotographic recording material by depositing amorphous silicon on a blocking layer on a substrate by means of direct current magnetron cathode sputtering, the improvement which comprises: depositing amorphous silicon in a hydrogen- and argon-containing atmosphere at a total hydrogen and argon pressure in the range of 10 -2 to 10 -3 mbar and an effective density of 2 to 30 W/cm 2 .
References Cited (Backward Citations)
EP0038221A2
Cited
DE3117035A1
Cited
EP0045204A2
Cited
US4412900A
Cited
DE3245500A1
Cited
US4738913A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-12 | 1993-08-14 | 1994-02-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-12 | 1997-08-14 | 1998-02-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-12 | 2001-08-14 | 2002-02-13 | $7700.00 | Window Closed / Lapsed |