Metal recovery
Assignee: VISTATECH PARTNERSHIP
•
Filing: 1986-07-03
•
Granted: 1990-02-06
•
Expires: 2006-07-03
Abstract
Abstract A relatively solid, stable biomass reaction product is provided produced from microorganisms having metal uptake properties when contacted by an aqueous solution containing metal cations. The biomass reaction product is produced by treating cells thereof with a caustic solution, whereby the biomass reaction product after drying is characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake property of the microorganism before treatment. The biomass reaction product in the particulate state is preferably immobilized in an insoluble binder.
Inventors
- 👤 James A. Brierley
- 👤 Corale L. Brierley
- 👤 Raymond F. Decker
- 👤 George M. Goyak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 23:44
CPC Classifications
C; C02; C02F; C02F1/00; C02F1/28; C02F1/286; C12; C12N; C12N1/00; C12N1/20; C12N1/205; C12N1/005; C22; C22B; C22B3/00; C22B3/18; C12R; C12R2001/00; C12R2001/01; C12R2001/07; C12R2001/125; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y10; Y10S; Y10S435/00; Y10S435/8215; Y10S435/822; Y10S435/832; Y10S435/839; Y10S435/911; Y10S435/913; Y10S435/939; Y10S435/94
Claims Analysis
Total Claims: 40
Claim 1
Independent Claim
142 words
A process for enhancing the metal uptake properties of Bacillus subtilis from aqueous solutions containing metal cations, which comprises: treating cells of said Bacillus subtilis characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product consisting essentially of material derived from the cell walls thereof having enhanced metal uptake properties, and thereafter recovering, washing to remove excess caustic and drying said treated biomass to form a relatively solid, stable product thereof, immobilizing said biomass reaction product in the particulate state in an insoluble organic binder said immobilized biomass reaction product in said particulate state being characterized by substantially enhanced metal uptake as compared to the metal uptake of the Bacillus subtilis in the untreated state.
Claim 2
Dependent Claim
142 words
A process for enhancing the metal uptake properties of Bacillus subtilis from aqueous solutions containing metal cations, which comprises: treating cells of said Bacillus subtilis characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product consisting essentially of material derived from the cell walls thereof having enhanced metal uptake properties, and thereafter recovering, washing to remove excess caustic and drying said treated biomass to form a relatively solid, stable product thereof, immobilizing said biomass reaction product in the particulate state in an insoluble organic binder said immobilized biomass reaction product in said particulate state being characterized by substantially enhanced metal uptake as compared to the metal uptake of the Bacillus subtilis in the untreated state.
Claim 3
Dependent Claim
18 words
The process of claim 1, wherein the amount of binder by weight ranges from about 0.5% to 10%.
Claim 4
Dependent Claim
40 words
The process of claim 1, wherein the caustic solution is selected from the group consisting of NaOH and KOH, and wherein said treatment in the solution is carried out at a temperature of about 50° C. to about 100° C.
Claim 5
Dependent Claim
123 words
A biomass reaction product produced from Bacillus subtilis having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said Bacillus subtilis characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after washing and drying being immobilized in an insoluble organic binder and being relatively solid, and being further characterized in the particulate state in aqueous solutions of having substantially enhanced uptake of metal cations as compared to the metal uptake properties of said Bacillus subtilis before treatment.
Claim 6
Dependent Claim
123 words
A biomass reaction product produced from Bacillus subtilis having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said Bacillus subtilis characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after washing and drying being immobilized in an insoluble organic binder and being relatively solid, and being further characterized in the particulate state in aqueous solutions of having substantially enhanced uptake of metal cations as compared to the metal uptake properties of said Bacillus subtilis before treatment.
Claim 7
Dependent Claim
20 words
The biomass product of claim 4, wherein the amount of insoluble binder by weight ranges from about 0.5% to 10%.
Claim 8
Dependent Claim
38 words
The biomass reaction product of claim 4, said product having been produced by caustic treatment in a solution selected from the group consisting of NaOH and KOH at a temperature of about 50° C. to about 100° C.
Claim 9
Dependent Claim
125 words
A process for enhancing the metal uptake properties of a Bacillus species from aqueous solutions containing metal cations, which comprises, treating cells of a Bacillus species characterized by cell walls and having metal uptake properties with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, and thereafter recovering and drying said treated biomass to form a relatively solid stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble organic binder and being further characterized in aqueous solutions by substantially enhanced metal uptake as compared to the metal uptake of the Bacillus species in the untreated state.
Claim 10
Dependent Claim
125 words
A process for enhancing the metal uptake properties of a Bacillus species from aqueous solutions containing metal cations, which comprises, treating cells of a Bacillus species characterized by cell walls and having metal uptake properties with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, and thereafter recovering and drying said treated biomass to form a relatively solid stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble organic binder and being further characterized in aqueous solutions by substantially enhanced metal uptake as compared to the metal uptake of the Bacillus species in the untreated state.
Claim 11
Dependent Claim
41 words
The process of claim 7, wherein the caustic solution is selected from the group consisting of NaOH and KOH and wherein said treatment in the solution is carried out at a temperature ranging from about 50° C. to about 100° C.
Claim 12
Dependent Claim
19 words
The process of claim 7, wherein the amount of insoluble binder by weight ranges from about 0.5% to 10%.
Claim 13
Dependent Claim
124 words
A biomass reaction product produced from a Bacillus species having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said Bacillus species characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being immobilized in an insoluble organic binder and being relatively solid and stable, and being further characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake properties of said Bacillus species before treatment.
Claim 14
Dependent Claim
124 words
A biomass reaction product produced from a Bacillus species having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said Bacillus species characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being immobilized in an insoluble organic binder and being relatively solid and stable, and being further characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake properties of said Bacillus species before treatment.
Claim 15
Dependent Claim
21 words
The biomass reaction product of claim 10, wherein the amount of insoluble binder by weight ranges from about 0.5% to 10%.
Claim 16
Dependent Claim
39 words
The biomass reaction product of claim 10, said product having been produced by caustic treatment in a solution selected from the group consisting of NaOH and KOH at a temperature ranging from about 50° C. to about 10° C.
Claim 17
Dependent Claim
147 words
A process for enhancing the metal uptake properties of a Gram-positive bacterium from aqueous solutions containing metal cations, which comprises, selecting a Gram-positive bacterium characterized by cell walls and having mucopeptide strands cross-linked with transpeptide bonds and having metal uptake properties, and which when treated with a caustic solution forms a biomass reaction product, treating cells of said Gram-positive bacterium with an amount of said caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form said biomass reaction product, and thereafter recovering and drying said treated biomass to provide a relatively solid, stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble organic binder and being characterized by substantially enhanced metal uptake properties as compared to the metal uptake properties of the Grampositive bacterium before said treatment.
Claim 18
Dependent Claim
147 words
A process for enhancing the metal uptake properties of a Gram-positive bacterium from aqueous solutions containing metal cations, which comprises, selecting a Gram-positive bacterium characterized by cell walls and having mucopeptide strands cross-linked with transpeptide bonds and having metal uptake properties, and which when treated with a caustic solution forms a biomass reaction product, treating cells of said Gram-positive bacterium with an amount of said caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form said biomass reaction product, and thereafter recovering and drying said treated biomass to provide a relatively solid, stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble organic binder and being characterized by substantially enhanced metal uptake properties as compared to the metal uptake properties of the Grampositive bacterium before said treatment.
Claim 19
Dependent Claim
19 words
The process of claim 13, wherein the amount of insoluble binder ranges by weight from about 0.5% to 10%.
Claim 20
Dependent Claim
40 words
The process of claim 13, wherein the caustic solution is selected from the group consisting of NaOH and KOH, and wherein the treatment in the solution is carried out at a temperature of about 50° C. to about 100° C.
Claim 21
Dependent Claim
135 words
A biomass reaction product produced from a Gram-positive bacterium characterized by cell walls and having mucopeptide strands cross-linked with transpeptide bonds and having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said Gram-positive bacterium with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being relatively solid and stable and being immobilized in an insoluble organic binder, said biomass reaction product in the particulate state being characterized of having substantially enhanced uptake of metal cations from aqueous solutions are compared to the metal uptake properties of said Grampositive bacterium before treatment.
Claim 22
Dependent Claim
135 words
A biomass reaction product produced from a Gram-positive bacterium characterized by cell walls and having mucopeptide strands cross-linked with transpeptide bonds and having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said Gram-positive bacterium with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being relatively solid and stable and being immobilized in an insoluble organic binder, said biomass reaction product in the particulate state being characterized of having substantially enhanced uptake of metal cations from aqueous solutions are compared to the metal uptake properties of said Grampositive bacterium before treatment.
Claim 23
Dependent Claim
20 words
The biomass reaction product of claim 16, wherein the amount of binder by weight ranges from about 0.5% to 10%.
Claim 24
Dependent Claim
38 words
The biomass reaction product of claim 16, said product having been produced by caustic treatment in a solution selected from the group consisting of NaOH and KOH at a temperature of about 50° C. to about 100° C.
Claim 25
Dependent Claim
135 words
A process for enhancing the metal uptake properties of a bacterium from aqueous solutions containing metal cations, which comprises, selecting a bacterium characterized by cell walls and having metal uptake properties and which when treated with a caustic solution forms a biomass reaction product, treating cells of said bacterium with an amount of said caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form said biomass reaction product, and thereafter recovering and drying said treated biomass to provide a relatively solid, stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble organic binder and being characterized by substantially enhanced metal uptake properties as compared to the metal uptake properties of the bacterium before said treatment.
Claim 26
Dependent Claim
135 words
A process for enhancing the metal uptake properties of a bacterium from aqueous solutions containing metal cations, which comprises, selecting a bacterium characterized by cell walls and having metal uptake properties and which when treated with a caustic solution forms a biomass reaction product, treating cells of said bacterium with an amount of said caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form said biomass reaction product, and thereafter recovering and drying said treated biomass to provide a relatively solid, stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble organic binder and being characterized by substantially enhanced metal uptake properties as compared to the metal uptake properties of the bacterium before said treatment.
Claim 27
Dependent Claim
18 words
The process of claim 19, wherein the amount of binder by weight ranges from about 0.5% to 10%.
Claim 28
Dependent Claim
41 words
The process of claim 19, wherein the caustic solution is selected from the group consisting of NaOH and KOH, and wherein the treatment in the solution is carried out at a temperature ranging from about 50° C. to about 100° C.
Claim 29
Dependent Claim
121 words
A biomass reaction product produced from a bacterium having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said bacterium characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being immobilized in an insoluble organic binder and being relatively solid and stable, and being further characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake properties of said bacterium before treatment.
Claim 30
Dependent Claim
121 words
A biomass reaction product produced from a bacterium having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said bacterium characterized by cell walls with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being immobilized in an insoluble organic binder and being relatively solid and stable, and being further characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake properties of said bacterium before treatment.
Claim 31
Dependent Claim
20 words
The biomass reaction product of claim 22, wherein the amount of binder by weight ranges from about 0.5% to 10%.
Claim 32
Dependent Claim
38 words
The biomass reaction product of claim 22, said product having been produced by caustic treatment in a solution selected from the group consisting of NaOH and KOH at a temperature of about 50° C. to about 100° C.
Claim 33
Dependent Claim
145 words
A process for enhancing the metal uptake properties of microorganisms from aqueous solutions containing metal cations, which comprises, selecting a microorganism selected from the group consisting of Saccharomyces, Neurospora, Rhizopus and Aspergillus having a cell wall structure and having metal uptake properties and which when treated with a caustic solution forms a biomass reaction product, treating cells of said microorganism with an amount of said caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form said biomass reaction product, and thereafter recovering and drying said treated biomass to provide a relatively solid, stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble binder and further characterized by substantially enhanced metal uptake properties as compared to the metal uptake properties of the microorganism before said treatment.
Claim 34
Dependent Claim
145 words
A process for enhancing the metal uptake properties of microorganisms from aqueous solutions containing metal cations, which comprises, selecting a microorganism selected from the group consisting of Saccharomyces, Neurospora, Rhizopus and Aspergillus having a cell wall structure and having metal uptake properties and which when treated with a caustic solution forms a biomass reaction product, treating cells of said microorganism with an amount of said caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form said biomass reaction product, and thereafter recovering and drying said treated biomass to provide a relatively solid, stable product thereof, said biomass reaction product in the particulate state being immobilized in an insoluble binder and further characterized by substantially enhanced metal uptake properties as compared to the metal uptake properties of the microorganism before said treatment.
Claim 35
Dependent Claim
18 words
The process of claim 25, wherein the amount of binder by weight ranges from about 0.5% to 10%.
Claim 36
Dependent Claim
41 words
The process of claim 25, wherein the caustic solution is selected from the group consisting of NaOH and KOH, and wherein the treatment in the solution is carried out at a temperature ranging from about 50° C. to about 100° C.
Claim 37
Dependent Claim
134 words
A biomass reaction product produced from a microorganism selected from the group consisting of Saccharomyces, Neurospora, Rhizopus and Aspergillus having a cell wall structure and having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said microorganism with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being immobilized in an insoluble organic binder and being relatively solid and stable, and being further characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake properties of said microorganism before treatment.
Claim 38
Dependent Claim
134 words
A biomass reaction product produced from a microorganism selected from the group consisting of Saccharomyces, Neurospora, Rhizopus and Aspergillus having a cell wall structure and having metal uptake properties when contacted by an aqueous solution containing metal cations, said biomass reaction product having been produced by treating cells of said microorganism with an amount of caustic solution maintained at an elevated temperature above ambient and ranging up to boiling at a pH in excess of 9 sufficient to form a causticized biomass reaction product, said biomass reaction product after drying being immobilized in an insoluble organic binder and being relatively solid and stable, and being further characterized in the particulate state of having substantially enhanced uptake of metal cations from aqueous solutions as compared to the metal uptake properties of said microorganism before treatment.
Claim 39
Dependent Claim
20 words
The biomass reaction product of claim 28, wherein the amount of binder by weight ranges from about 0.5% to 10%.
Claim 40
Dependent Claim
38 words
The biomass reaction product of claim 28, said product having been produced by caustic treatment in a solution selected from the group consisting of NaOH and KOH at a temperature of about 50° C. to about 100° C.
References Cited (Backward Citations)
US3406114A
Cited
US3346463A
Cited
US3725291A
Cited
US3684706A
Cited
US4021368A
Cited
US4067821A
Cited
US4288552A
Cited
US4320093A
Cited
US4289531A
Cited
US4293334A
Cited
US4293333A
Cited
US4456532A
Cited
US4690894A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-05 | 1993-08-07 | 1994-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-05 | 1997-08-07 | 1998-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-05 | 2001-08-07 | 2002-02-06 | $7700.00 | Window Closed / Lapsed |