Two-stage ferrosilicon smelting process
Assignee: Dow Silicones Corp
•
Filing: 1989-03-20
•
Granted: 1990-02-06
•
Expires: 2009-03-20
Abstract
Abstract The present invention relates to a process for the production of ferrosilicon in a closed two-stage reduction furnace. In the present invention, carbon monoxide released as a result of the smelting process, in the first stage of the furnace, is used to prereduce higher oxides of iron, for example Fe 2 O 3 and Fe 3 O 4 , contained in a second stage of a furnace, to iron monoxide (FeO). The iron monoxide is then used as a feed material to the first stage of the furnace. The use of a closed furnace and a pre-reduction process results in substantial energy savings in the production of ferrosilicon alloy.
Inventors
- 👤 Vishu D. Dosaj
- 👤 James B. May
- 👤 Robert D. Jeffress
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 14:01
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/003
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
205 words
A process for preparing ferrosilicon in a closed two-stage furnace, the first stage of the furnace containing an energy source and the second stage being attached to the first stage by a means suitable for retaining solid particles in the second stage and allowing gases from the first stage to pass through the contained particles, said process comprising: a. combining into the first stage of the furnace a feed mixture consisting essentially of a source of iron, a source of carbon, and silicon dioxide; b. loading the second stage of the furnace with particles containing higher oxides of iron; c. applying energy to the first stage sufficient to effect conversion of the feed mixture to molten silicon and iron and to gaseous carbon monoxide; the gaseous carbon monoxide contacting the particles contained in the second stage and reducing the higher oxides of iron; d. recovering the molten silicon and iron from the first stage as a ferrosilicon alloy; e. loading the reduced higher oxides of iron formed in the second stage, along with silicon dioxide and a source of carbon to the first stage; f. loading the second stage of the furnace with particles containing higher oxides of iron; g. repeating steps c through f.
Claim 2
Dependent Claim
205 words
A process for preparing ferrosilicon in a closed two-stage furnace, the first stage of the furnace containing an energy source and the second stage being attached to the first stage by a means suitable for retaining solid particles in the second stage and allowing gases from the first stage to pass through the contained particles, said process comprising: a. combining into the first stage of the furnace a feed mixture consisting essentially of a source of iron, a source of carbon, and silicon dioxide; b. loading the second stage of the furnace with particles containing higher oxides of iron; c. applying energy to the first stage sufficient to effect conversion of the feed mixture to molten silicon and iron and to gaseous carbon monoxide; the gaseous carbon monoxide contacting the particles contained in the second stage and reducing the higher oxides of iron; d. recovering the molten silicon and iron from the first stage as a ferrosilicon alloy; e. loading the reduced higher oxides of iron formed in the second stage, along with silicon dioxide and a source of carbon to the first stage; f. loading the second stage of the furnace with particles containing higher oxides of iron; g. repeating steps c through f.
Claim 3
Dependent Claim
13 words
The process of claim 1, where the energy source is a transferred-arc plasma.
Claim 4
Dependent Claim
19 words
The process of claim 2, where the particles containing higher oxides of iron are tailings from iron ore concentration.
Claim 5
Dependent Claim
24 words
The process of claim 3, where the iron ore source for the tailings is selected from a group comprising taconite, magnetite, hematite, and limonite.
Claim 6
Dependent Claim
20 words
The process of claim 4, where the tailings have a particle size of less than about 0.25 inch by down.
Claim 7
Dependent Claim
23 words
The process of claim 5, where the concentration of higher oxides of iron in the tailings is greater than about 5 weight percent.
Claim 8
Dependent Claim
23 words
The process of claim 6, where the concentration of higher oxides of iron in the tailings is about 10 to 20 weight percent.
Claim 9
Dependent Claim
14 words
The process of claim 7, where the tailings are from the concentration of taconite.
Claim 10
Dependent Claim
17 words
The process of claim 8, where the higher oxide of iron is Fe 2 O 3 .
Claim 11
Dependent Claim
14 words
The process of claim 1, where the energy source is an open electric arc.
Claim 12
Dependent Claim
19 words
The process of claim 10, where the particles containing higher oxides of iron are tailings from iron ore concentration.
Claim 13
Dependent Claim
24 words
The process of claim 11, where the iron ore source for the tailings is selected from a group comprising taconite, magnetite, hematite, and limonite.
Claim 14
Dependent Claim
20 words
The process of claim 12, where the tailings have a particle size of less than about 0.25 inch by down.
Claim 15
Dependent Claim
23 words
The process of claim 13, where the concentration of higher oxides of iron in the tailings is greater than about 5 weight percent.
Claim 16
Dependent Claim
23 words
The process of claim 14, where the concentration of higher oxides of iron in the tailings is about 10 to 20 weight percent.
Claim 17
Dependent Claim
14 words
The process of claim 15, where the tailings are from the concentration of taconite.
Claim 18
Dependent Claim
17 words
The process of claim 16, where the higher oxide of iron is Fe 2 O 3 .
Claim 19
Dependent Claim
28 words
The process of claim 1, where at least a part of the silicon dioxide is provided as a component of the particles containing the higher oxides of iron.
Claim 20
Dependent Claim
24 words
The process of claim 18, where about 50 to 100 percent of the silicon dioxide is provided as a component of the iron source.
Claim 21
Dependent Claim
32 words
The process of claim 1, where the carbon is present at a quantity stoichiometrically sufficient to essentially fully reduce the silicon and iron oxides present in the first stage of the furnace.
Claim 22
Dependent Claim
50 words
The process of claim 20, where about 50 to 100 weight percent of the stoichiometric quantity of carbon is present in the first stage of the furnace and the remaining 0 to 50 weight percent of the stoichiometric quantity of carbon is present in the second stage of the furnace.
Claim 23
Dependent Claim
58 words
The process of claim 21, where the carbon present in the second stage of the furnace is separate from the particles containing the higher oxides of iron and the carbon is placed in a position to contact the gases from the first stage of the furnace before the gases contact the particles containing the higher oxides of iron.
Claim 24
Dependent Claim
47 words
The process of claim 22, where about 90 weight percent of the stoichiometric quantity of carbon is present in the first stage of the furnace and the remaining about 10 weight percent of the stoichiometric quantity of carbon is present in the second stage of the furnace.
Claim 25
Dependent Claim
17 words
The process of claim 1, where the ferrosilicon alloy is about 45 to 90 weight percent silicon.
Claim 26
Dependent Claim
15 words
The process of claim 24, where the ferrosilicon alloy is about 50 weight percent silicon.
Claim 27
Dependent Claim
15 words
The process of claim 24, where the ferrosilicon alloy is about 75 weight percent silicon.
Claim 28
Dependent Claim
14 words
The process of claim 1, where the energy source is a submerged electric arc.
Claim 29
Dependent Claim
13 words
The process of claim 1, where the energy source is a direct current.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-02-05 | 1993-08-07 | 1994-02-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-02-05 | 1997-08-07 | 1998-02-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-02-05 | 2001-08-07 | 2002-02-06 | $7700.00 | Window Closed / Lapsed |