Assignee: ExxonMobil Chemical Patents Inc
•
Filing: 1988-12-02
•
Granted: 1990-01-30
•
Expires: 2008-12-02
Abstract
Abstract An olefin polymerization supported catalyst comprising a support and the reaction product of a metallocene of Group 4b, 5b or 6b of the Periodic Table and an alumoxane, said reaction product formed in the presence of a support.
Inventors
- 👤 Howard C. Welborn, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 03:19
CPC Classifications
C; C08; C08F; C08F210/00; C08F210/16; C08F210/18; C08F10/00; C08F210/02; C08F4/00; C08F4/42; C08F4/44; C08F4/60; C08F4/62; C08F4/64; C08F4/659; C08F4/65912; C08F4/6592; C08F4/65922; C08F4/65925; Y; Y10; Y10S; Y10S526/00; Y10S526/943
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
113 words
A method for preparing polymers of ethylene and copolymers of ethylene and alpha olefins or diolefins, said method comprising effecting the polymerization in the presence of a supported catalyst comprising the supported reaction product of at least one metallocene of a metal of Group 4b of the Periodic Table and an alumoxane, the aluminum to transition metal molar ratio being in the range of 100:1 to 1:1, said product being formed in the presence of the support, said support being a porous inorganic metal oxide of Group 2a, 3a, 4a, or 4b metal, and wherein the metallocene is employed in the amount of about 0.001 to about 10 millimoles per gram of support.
Claim 2
Independent Claim
113 words
A method for preparing polymers of ethylene and copolymers of ethylene and alpha olefins or diolefins, said method comprising effecting the polymerization in the presence of a supported catalyst comprising the supported reaction product of at least one metallocene of a metal of Group 4b of the Periodic Table and an alumoxane, the aluminum to transition metal molar ratio being in the range of 100:1 to 1:1, said product being formed in the presence of the support, said support being a porous inorganic metal oxide of Group 2a, 3a, 4a, or 4b metal, and wherein the metallocene is employed in the amount of about 0.001 to about 10 millimoles per gram of support.
Claim 3
Dependent Claim
10 words
The method of claim 1 wherein the support is silica.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein the metallocene is selected from titanium and zirconium metallocenes and mixtures thereof.
Claim 5
Dependent Claim
11 words
The method of claim 1 wherein the alumoxane is methyl alumoxane.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the molar ratio is in the range of 50:1 to 5:1.
Claim 7
Dependent Claim
264 words
The method of claim 1 wherein the metallocene is represented by the formulas (I) (Cp) m MR n X q , (II) (C 5 R' k ) g R" s (C 5 R' k )MQ 3-g and (III) R" s (C 5 R' k ) 2 MQ' wherein Cp is a cyclopentadienyl ring, M is a group 4b transition metal, R is a hydrocarbyl group or hydrocarboxy having from 1 to 20 carbon atoms, X is a halogen, m=1-3, n=0-3, q=0-3 and the sum of m+n+q is equal to the oxidation state of M, (C 5 R' k ) is a cyclopentadienyl or a substituted cyclopentadienyl; each R' is the same or different and is hydrogen or a hydrocarbyl radical selected from alkyl, alkenyl aryl, alkylaryl or arylalky radicals containing from 1 to 20 carbon atoms, or two carbon atoms are joined together to form a C 4 -C 6 ring, R" is a C 1 -C 4 alkylene radical, a dialkyl germanium or silicon or an alkyl phosphine or amine radical bridging two (C 5 R' k ) rings; Q is a hydrocarbyl radical selected from aryl, alkyl, alkenyl, alkylaryl, or arylalkyl radicals having from 1-20 carbon atoms, hydrocarboxy radical having from 1-20 carbon atoms or halogen and can be the same or different from each other; Q' is an alkylidiene radical having from 1 to about 20 carbon atoms; s is 0 or 1; g is 0, 1, or 2; s is 0 when g is 0; k is 4 when s is 1 and k is 5 when s is 0.
Claim 8
Dependent Claim
99 words
The method of claim 6 wherein the metallocene is selected from bis(cyclopentadienyl) zirconium dichloride, bis(cyclopentadienyl) zirconium methyl chloride, bis(cyclopentadienyl) zirconium dimethyl, bis(methylcyclopentadienyl) zirconium dichloride, bis(methylcyclopentadienyl) zirconium dimethyl, bis(pentamethylcyclopentadienyl) zirconium dichloride, bis(pentamethylcyclopentadienyl) zirconium dichloride, bis(pentamethylcyclopentadienyl)zirconium methyl chloride, bis(pentamethylcyclopentadienyl) zirconium dimethyl, bis(n-butyl-cyclopentadienyl)zirconium dichloride, bis(n-butylcyclopentadienyl) zirconium methyl chloride, bis(n-butyl-cyclopentadienyl) zirconium dimethyl, bis(cyclopentadienyl) titanium diphenyl, bis(cyclopentadienyl) titanium dichloride, bis(cyclopentadienyl) titanium methyl chloride, bis(cyclopentadienyl) titanium dimethyl, bis(methylcyclopentadienyl) titanium diphenyl, bis(methylcyclopentadienyl) titanium dichloride, bis(methylcyclopentadienyl)titanium diphenyl, bis(methylcyclopentadienyl)titanium methyl chloride, bis(methylcyclo-pentadienyl) titanium dimethyl, bis(pentamethylcyclopentadienyl) titanium dichloride, bis(pentamethylcyclopentadienyl) titanium diphenyl, bis(pentamethylcyclopentadienyl) titanium methyl chloride, bis (pentamethylcyclopentadienyl) titanium dimethyl, bis (n-butyl-cyclopentadienyl) titanium diphenyl, bis(n-butyl-cyclopentadienyl) titanium dichloride and mixtures thereof.
Claim 9
Independent Claim
130 words
A method for preparing polymers of ethylene and copolymers of ethylene and alpha-olefins as diolefins, said method comprising effecting the polymerization in the presence of a supported catalyst comprising the supported reaction product of at least one metallocene of a metal of Group 4b of the Periodic Table and an alumoxane, the aluminum to transition metal molar ratio being in the range of 100:1 to 1:1, said catalyst being prepared by a method comprising adding to a slurry of the support which is a porous inorganic metal oxide of a Group 2a, 3a, 4a, or 4b metal, in an inert hydrocarbon solvent, an alumoxane in an inert hydrocarbon solvent and a metallocene in an amount of from about 0.00I to about 10 millimoles of said metallocene per gram of support.
Claim 10
Independent Claim
130 words
A method for preparing polymers of ethylene and copolymers of ethylene and alpha-olefins as diolefins, said method comprising effecting the polymerization in the presence of a supported catalyst comprising the supported reaction product of at least one metallocene of a metal of Group 4b of the Periodic Table and an alumoxane, the aluminum to transition metal molar ratio being in the range of 100:1 to 1:1, said catalyst being prepared by a method comprising adding to a slurry of the support which is a porous inorganic metal oxide of a Group 2a, 3a, 4a, or 4b metal, in an inert hydrocarbon solvent, an alumoxane in an inert hydrocarbon solvent and a metallocene in an amount of from about 0.00I to about 10 millimoles of said metallocene per gram of support.
Claim 11
Dependent Claim
20 words
The method in accordance with claim 8 wherein the alumoxane is added to the support material prior to the metallocene.
Claim 12
Dependent Claim
19 words
The method in accordance with claim 8 wherein the metallocene is added to the support prior to the alumoxane.
Claim 13
Dependent Claim
19 words
The method in accordance with claim 8 wherein the metallocene and alumoxane are added to the support slurry simultaneously.
Claim 14
Dependent Claim
113 words
The method in accordance with claim 8 wherein the metallocene is selected from bis(cyclopentadienyl) zirconium dichloride, bis(cyclopentadienyl) zirconium methyl chloride, bis(cyclopentadienyl) zirconium dimethyl, bis(methylcyclopentadienyl) zirconium dichloride, bis(methylcyclopentadienyl) zirconium methyl chloride, bis (methylcyclopentadienyl) zirconium dimethyl, bis(pentamethylcyclopentadienyl) zirconium dichloride, bis(pentamethylcyclopentadienyl) zirconium methyl chloride, bis(pentamethylcyclopentadienyl) zirconium dimethyl, bis (n-butylcyclopentadienyl) zirconium dichloride, bis(n-butylcyclopentadienyl) zirconium methyl chloride, bis(n-butyl-cyclopentadienyl) zirconium dimethyl, bis(n-butylcyclopentadienyl) titanium diphenyl, bis(cyclopentadienyl) titanium dichloride, bis(cyclopentadienyl) titanium methyl chloride, bis(cyclopentadienyl) titanium dimethyl, bis(methylcyclopentadienyl) titanium diphenyl, bis(methylcyclopentadienyl) titanium dichloride, bis(methylcyclopentadienyl) titanium diphenyl, bis(methylcyclopentadienyl) titanium methyl chloride, bis(methylcyclopentadienyl) titanium dimethyl, bis(pentamethylcyclopentadienyl) titanium dichloride, bis(pentamethylcyclopentadienyl) titanium diphenyl, bis(pentamethylcyclopentadienyl) titanium methyl chloride, bis(pentamethylcyclopentadienyl) titanium dimethyl, bis(n-butyl-cyclopenta-dienyl) titanium diphenyl, bis(n-butyl-cyclopentadienyl) titanium dichloride, the alumoxane is methyl alumoxane and the support is silica.
Claim 15
Dependent Claim
22 words
The method is accordance with claim 8 wherein the metallocene is one of bis(cyclopentadienyl) zirconium dichloride, bis(n-butyl-cyclopentadienyl) zirconium dichloride and mixtures thereof.
Claim 16
Dependent Claim
14 words
The method in accordance with claim 8 wherein the metallocene is bis(n-butyl-cyclopentadienyl) zirconium dichloride.
References Cited (Backward Citations)
US2981725A
Cited
US3166542A
Cited
US4056668A
Cited
US4133944A
Cited
DE2608863A1
Cited
US4542199A
Cited
US4530914A
Cited
US4564647A
Cited
US4752597A
Cited
JPH01108610A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-29 | 1993-07-31 | 1994-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-29 | 1997-07-31 | 1998-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-29 | 2001-07-31 | 2002-01-30 | $7700.00 | Window Closed / Lapsed |