US4895769A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preparing light polarizer
Assignee: 3M Innovative Properties Co
•
Filing: 1988-08-09
•
Granted: 1990-01-23
•
Expires: 2008-08-09
Abstract
Abstract A stainable polymeric sheet material adapted to the production of a light polarizer therefrom is provided by a method, according to which, a support sheet of amorphous polymeric material is uniaxially stretched in a first direction (at or above the glass transition temperature of the polymeric support material), a layer of polyvinyl alcohol (PVA) is coated from an aqueous PVA-containing composition onto the uniaxially stretched support material, and the PVA-coated uniaxially stretched polymeric sheet material is stretched along a second direction, at an angle within about ±60 degrees to a normal to the first direction of stretch. The method provides a material which can be converted, by incorporation of visible dichroism into the PVA layer, to a light polarizer which combines efficient light polarizing properties and good mechanical strength and resistance to fracture along the stretch directions.
Inventors
- 👤 Edwin H. Land
- 👤 Anthony J. DiRocco
- 👤 Leonard Polizzotto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:02
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/30; G02B5/3025; G02B5/3033; G02B1/00; G02B1/08; Y; Y10; Y10S; Y10S359/00; Y10S359/90; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
220 words
A method for preparing a stainable polymeric sheet article adapted to the production of a light polarizer therefrom, the method comprising the steps of: providing a support sheet of amorphous polymeric material; uniaxially stretching the amorphous polymeric support sheet in a first direction and at a temperature at or above the glass transition temperature of the polymeric support sheet material, to partially orient the molecules of the polymeric support sheet material along said first direction; applying a coating of an aqueous polyvinyl alcohol-containing composition to the surface of the uniaxially stretched polymeric support sheet; and stretching the polyvinyl alcohol-coated uniaxially stretched polymeric support sheet at a temperature at or above the glass transition temperature of the polymeric support sheet material and in a second direction of stretch; said second direction of stretch being at an angle within about ±60 degrees from a normal to said first direction of stretch; the amount of stretch along said first direction being sufficient to impart to the polymeric support sheet, resistance to stress-induced fracture along said first direction, and the amount of stretch along said second direction being sufficient to simultaneously orient the molecules of said polyvinyl alcohol layer to thereby adapt the layer to incorporation of visible dichroism, and to impart to the support layer, resistance to stress-induced fracture along said second direction.
Claim 2
Independent Claim
220 words
A method for preparing a stainable polymeric sheet article adapted to the production of a light polarizer therefrom, the method comprising the steps of: providing a support sheet of amorphous polymeric material; uniaxially stretching the amorphous polymeric support sheet in a first direction and at a temperature at or above the glass transition temperature of the polymeric support sheet material, to partially orient the molecules of the polymeric support sheet material along said first direction; applying a coating of an aqueous polyvinyl alcohol-containing composition to the surface of the uniaxially stretched polymeric support sheet; and stretching the polyvinyl alcohol-coated uniaxially stretched polymeric support sheet at a temperature at or above the glass transition temperature of the polymeric support sheet material and in a second direction of stretch; said second direction of stretch being at an angle within about ±60 degrees from a normal to said first direction of stretch; the amount of stretch along said first direction being sufficient to impart to the polymeric support sheet, resistance to stress-induced fracture along said first direction, and the amount of stretch along said second direction being sufficient to simultaneously orient the molecules of said polyvinyl alcohol layer to thereby adapt the layer to incorporation of visible dichroism, and to impart to the support layer, resistance to stress-induced fracture along said second direction.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein said amorphous polymeric support sheet is stretched along said first direction to about 175% to about 350% of its original dimension.
Claim 4
Dependent Claim
30 words
The method of claim 2 wherein said polyvinyl alcohol-coated uniaxially stretched polymeric support sheet is stretched in said second direction to about 300% to about 700% of its original dimension.
Claim 5
Dependent Claim
30 words
The method of claim 2 wherein said polyvinyl alcohol-coated uniaxially stretched polymeric support sheet is stretched in said second direction to about 400% to about 600% of its original dimension.
Claim 6
Dependent Claim
27 words
The method of claim 1 wherein second direction of stretch is at an angle of about ±45 degrees with respect to a normal to said first direction.
Claim 7
Dependent Claim
23 words
The method of claim 5 wherein said angle is within about ± ten degrees with respect to a normal to said first direction.
Claim 8
Dependent Claim
11 words
The method of claim 6 wherein said angle is zero degrees.
Claim 9
Dependent Claim
16 words
The method of claim 1 wherein said support sheet of amorphous polymeric material comprises a polyester.
Claim 10
Dependent Claim
34 words
The method of claim 8 wherein said polyester is polyethylene terephthalate and each of said first and second stretching steps is conducted at a temperature in the range of 80° C. to 125° C.
Claim 11
Dependent Claim
32 words
The method of claim 1 wherein said polyvinyl alcohol-containing composition is applied to said uniaxially stretched polymeric support sheet to a dry thickness of from about 0.0064 mm to about 0.0762 mm.
Claim 12
Dependent Claim
29 words
The method of claim 10 wherein the solids level of polyvinyl alcohol in said aqueous polyvinyl alcohol-containing composition is in the range of from about 5% to about 15%.
Claim 13
Dependent Claim
20 words
The method of claim 11 wherein said solids content is in the range of from about 8.5% to about 12%.
Claim 14
Dependent Claim
29 words
The method of claim 12 wherein the degree of hydrolysis of said polyvinyl alcohol in said aqueous polyvinyl alcohol-containing composition is in the range of from 98.5% to 99.5%.
Claim 15
Dependent Claim
40 words
The method of claim 1 wherein after said step of uniaxially stretching the amorphous polymeric support sheet, and before said step of applying said coating of polyvinyl alcohol, an adhesive or primer layer is applied to said polymeric support sheet.
Claim 16
Dependent Claim
23 words
The method of claim 1 additionally including the step of incorporating visible dichroism into said polyvinyl alcohol layer to provide a light polarizer.
Claim 17
Dependent Claim
204 words
A stainable polymeric sheet article adapted to the production of a light polarizer therefrom, said polymeric sheet article comprising: a biaxially oriented polymeric support sheet carrying a coated layer of polyvinyl alcohol; said biaxially oriented polymeric support sheet having biaxial orientation resulting, in part, from the uniaxial stretching of an amorphous polymeric support sheet prior to the application of said coated polyvinyl alcohol layer thereon, said uniaxial stretching being along a first direction, and, in part, as an incident to the subsequent stretching and orientation, along a second direction, of said coated polyvinyl alcohol layer carried on said uniaxially stretched polymeric support sheet; said stretching of said coated polyvinyl alcohol layer along said second direction being at an angle within about ±60 degrees from a normal to said stretching along said first direction; the amount of stretch along said first direction being sufficient to impart to the polymeric support sheet, resistance to stress-induced fracture along said first direction, and the amount of stretch along said second direction being sufficient to simultaneously orient the molecules of said polyvinyl alcohol layer and thereby adapt the layer to incorporation of visible dichroism, and to impart to the support layer, resistance to stress-induced fracture along said second direction.
Claim 18
Dependent Claim
204 words
A stainable polymeric sheet article adapted to the production of a light polarizer therefrom, said polymeric sheet article comprising: a biaxially oriented polymeric support sheet carrying a coated layer of polyvinyl alcohol; said biaxially oriented polymeric support sheet having biaxial orientation resulting, in part, from the uniaxial stretching of an amorphous polymeric support sheet prior to the application of said coated polyvinyl alcohol layer thereon, said uniaxial stretching being along a first direction, and, in part, as an incident to the subsequent stretching and orientation, along a second direction, of said coated polyvinyl alcohol layer carried on said uniaxially stretched polymeric support sheet; said stretching of said coated polyvinyl alcohol layer along said second direction being at an angle within about ±60 degrees from a normal to said stretching along said first direction; the amount of stretch along said first direction being sufficient to impart to the polymeric support sheet, resistance to stress-induced fracture along said first direction, and the amount of stretch along said second direction being sufficient to simultaneously orient the molecules of said polyvinyl alcohol layer and thereby adapt the layer to incorporation of visible dichroism, and to impart to the support layer, resistance to stress-induced fracture along said second direction.
Claim 19
Dependent Claim
51 words
The stainable polymeric sheet article of claim 16 wherein said biaxial orientation of said support is the result of stretching along first direction to about 175% to about 350% of the original first dimension and stretching along said second direction to about 300% to about 700% of the original second dimension.
Claim 20
Dependent Claim
32 words
The stainable polymeric sheet article of claim 17 wherein said first stretching is to about 200% of said first dimension and said second stretching is to about 500% of said second dimension.
Claim 21
Dependent Claim
17 words
The stainable polymeric sheet article of claim 18 wherein said biaxially oriented support material comprises polyethylene terephthalate.
Claim 22
Dependent Claim
31 words
The stainable polymeric sheet article of claim 17 wherein said second direction of stretch is at an angle of about 45 degrees to a normal to said first direction of stretch.
Claim 23
Dependent Claim
32 words
The stainable polymeric sheet article of claim 17 wherein said second direction of stretch is at an angle of zero degrees with respect to a normal to said first direction of stretch.
Claim 24
Dependent Claim
16 words
The stainable polymeric sheet article of claim 16 wherein said polyvinyl alcohol layer is visibly dichroic.
References Cited (Backward Citations)
US23297A
Cited
USRE23297E
Cited
US2328219A
Cited
US2237567A
Cited
US2375963A
Cited
US2445555A
Cited
US3627579A
Cited
US4166871A
Cited
US4293585A
Cited
US4388375A
Cited
US4592623A
Cited
US4476189A
Cited
US4659523A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-22 | 1993-07-24 | 1994-01-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-22 | 1997-07-24 | 1998-01-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-22 | 2001-07-24 | 2002-01-23 | $7700.00 | Window Closed / Lapsed |