US4476189A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Copolyester primed polyester film
Assignee: Mitsubishi Chemical America Inc
•
Filing: 1983-05-16
•
Granted: 1984-10-09
•
Expires: 2003-05-16
Abstract
Abstract A primer coated, oriented polyester film material is provided wherein the primer is applied in an aqueous medium comprising a water dispersible copolyester consisting essentially of the condensation product of components A, B, C, and D or their polyester forming equivalents as follows: (A) about 60 to 75 mole percent of terephthalic acid; (B) about 15 to 25 mole percent of at least one dicarboxylic acid of the formula HOOC(CH2)nCOOH, wherein n ranges from about 1-11; (C) greater than from about 6 up to about 15 mole percent of at least one sulfomonomer containing an alkali metal sulfonate group attached to a dicarboxylic aromatic nucleus, and (D) stoichiometric quantities, i.e., about 100 mole percent of at least one aliphatic or cycloaliphatic alkylene glycol copolymerizable therewith having about from 2 to 11 carbon atoms. The copolyester priming layer may be applied to the polyester film at any suitable stage during manufacture of the film, i.e., before or during the stretching operations. The resultant primed polyester film is found to provide excellent adhesion to many aqueous or organic solvent based coatings subsequently applied thereto.
Inventors
- 👤 Robert G. Posey
- 👤 Edwin C. Culbertson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:19
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C55/00; B29C55/02; B29C55/023; B29C55/026; C08J7/00; C08J7/04; C08J7/042; C08J7/043; C08J2367/00; C08J2367/02; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31504; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
195 words
An oriented self-supporting polyester film having a continuous copolyester primer coating on one or both sides thereof, said polyester film prepared by melt extruding a substantially amorphous polyester film and thereafter orienting the film by stretching in one or two directions and heat setting the film, said copolyester primer coating being applied to said film as an aqueous dispersion prior to stretching in one direction or subsequent to stretching in one direction but prior to stretching in a mutually perpendicular direction, said copolyester primer coating consisting essentially of the polyester condensation product of the following monomers or their polyester forming equivalents: (A) about 60 to 75 mole percent of terephthalic acid; (B) about 15 to 25 mole percent of at least one aliphatic dicarboxylic acid of the formula HOOC(CH 2 ) n COOH, wherein n ranges from about 1-11; (C) greater than from about 6 up to about 15 mole percent of at least one sulfomonomer containing an alkali metal sulfonate group attached to a dicarboxylic aromatic nucleus, and (D) stoichiometric quantities of about 100 mole percent of at least one copolymerizable aliphatic or cycloaliphatic alkylene glycol having about from 2 to 11 carbon atoms.
Claim 2
Dependent Claim
195 words
An oriented self-supporting polyester film having a continuous copolyester primer coating on one or both sides thereof, said polyester film prepared by melt extruding a substantially amorphous polyester film and thereafter orienting the film by stretching in one or two directions and heat setting the film, said copolyester primer coating being applied to said film as an aqueous dispersion prior to stretching in one direction or subsequent to stretching in one direction but prior to stretching in a mutually perpendicular direction, said copolyester primer coating consisting essentially of the polyester condensation product of the following monomers or their polyester forming equivalents: (A) about 60 to 75 mole percent of terephthalic acid; (B) about 15 to 25 mole percent of at least one aliphatic dicarboxylic acid of the formula HOOC(CH 2 ) n COOH, wherein n ranges from about 1-11; (C) greater than from about 6 up to about 15 mole percent of at least one sulfomonomer containing an alkali metal sulfonate group attached to a dicarboxylic aromatic nucleus, and (D) stoichiometric quantities of about 100 mole percent of at least one copolymerizable aliphatic or cycloaliphatic alkylene glycol having about from 2 to 11 carbon atoms.
Claim 3
Dependent Claim
24 words
The film of claim 1 wherein said primer coating has a dry thickness within the range of about 10 -7 to 10 -5 inch.
Claim 4
Dependent Claim
17 words
The film of claim 2 wherein said self supporting polyester film is biaxially oriented polyethylene terephthalate film.
Claim 5
Dependent Claim
12 words
The film of claim 2 wherein said alkylene glycol is ethylene glycol.
Claim 6
Dependent Claim
51 words
The film of claim 2 wherein said sulfomonomer is present at a level of from about 7 to about 10 mole percent and is selected from the group consisting of sodium sulfoterephthalic acid, sodium 5-sulfoisophthalic acid, sodium sulfophthalic acid, 5(p-sodiosulfophenoxy)-isophthalic acid, 5-(sulfopropoxy) isophthalic acid, sodium salt; and their polyester forming equivalents.
Claim 7
Dependent Claim
25 words
The film of claim 5 wherein said copolyester primer coating further contains up to about 15 mole percent of isophthalic acid or its polyester-forming equivalents.
Claim 8
Dependent Claim
24 words
The film of claim 5 wherein said primer coating has a dry thickness within the range of about 8.0×10 -7 to 2.0×10 -6 inch.
Claim 9
Dependent Claim
20 words
The film of claim 5 wherein the acid monomers A, B and C are employed as the lower alkyl diesters.
Claim 10
Dependent Claim
13 words
The film of claim 5 wherein said aliphatic dicarboxylic acid is adipic acid.
Claim 11
Dependent Claim
12 words
The film of claim 9 wherein said sulfomonomer is dimethyl-5-sulfoisophthalate, sodium salt.
Claim 12
Dependent Claim
12 words
The film of claim 10 wherein said alkylene glycol is ethylene glycol.
Claim 13
Dependent Claim
36 words
The film of claim 2 wherein said copolyester has an acid number of less than about 10, a number average molecular weight of less than about 50,000; and a relative viscosity of greater than about 300.
Claim 14
Dependent Claim
33 words
The film of claim 11 wherein said copolyester has an acid number within the range of about 0 to 3 and a relative viscosity within the range of about 350 to about 650.
Claim 15
Dependent Claim
50 words
The film of claim 2 wherein said copolyester consists essentially of the polyester condensation product of about 70 to 73 mole percent of dimethyl terephthalate; about 20 mole percent of dimethyl adipate; about 7 to 10 mole percent of dimethyl-5-sulfoisophthalate; sodium salt; and about 100 mole percent of ethylene glycol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |