US4894296A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cathode for zinc air cells
Assignee: Gillette Co LLC
•
Filing: 1987-10-27
•
Granted: 1990-01-16
•
Expires: 2007-10-27
Abstract
Abstract The invention relates to an improved hydrophobic cathode for use in a zinc-air cell, and to a method for making said cathode. The cathode comprises an admixture of discrete particles of gamma manganese dioxide and carbon and a polymeric halogenated hydrocarbon. The method includes the step of intensively milling the manganese dioxide to reduce the particle size thereof and homogeneously admixing the manganese dioxide with the carbon particles.
Inventors
- 👤 Alex Borbely
- 👤 Jaynal Molla
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 08:56
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/9016; H01M4/96; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
43 words
A zinc-air electrochemical cell having an anode comprised of zinc, an alkaline electrolyte, and a hydrophobic cathode; wherein hydrophobic the cathode comprises an admixture of discrete particles of gamma manganese dioxide and carbon and at least 20% of a polymeric halogenated hydrocarbon binder.
Claim 2
Dependent Claim
43 words
A zinc-air electrochemical cell having an anode comprised of zinc, an alkaline electrolyte, and a hydrophobic cathode; wherein hydrophobic the cathode comprises an admixture of discrete particles of gamma manganese dioxide and carbon and at least 20% of a polymeric halogenated hydrocarbon binder.
Claim 3
Dependent Claim
19 words
The electrochemical cell of claim 1 wherein said manganese dioxide is present in an amount of at least 20%.
Claim 4
Dependent Claim
20 words
The electrochemical cell of claim 1 wherein aid manganese dioxide has an average particle size of 10 microns or less.
Claim 5
Dependent Claim
24 words
The electrochemical cell of claim 1 wherein said carbon is selected from the group consisting of carbon black, activated carbon, graphite, and mixtures thereof.
Claim 6
Dependent Claim
19 words
The electrochemical cell of claim 4 wherein said carbon has a surface area greater than 600 m 2 /gram.
Claim 7
Dependent Claim
33 words
The electrochemical cell of claim 1 wherein said manganese dioxide has an average particle size less than 7 microns and said carbon has a surface area of at least 100 m 2 /gram.
Claim 8
Dependent Claim
22 words
The electrochemical cell of claim 1 wherein said manganese dioxide comprises electrolytic gamma manganese dioxide and said polymeric halogenated hydrocarbon comprises polytetrafluoroethylene.
Claim 9
Independent Claim
53 words
A method of making a hydrophobic cathode for use in a zinc-air cell, comprising the steps of intensively milling gamma manganese dioxide particles, admixing the milled manganese dioxide particles and carbon particles, blending a polymeric halogenated hydrocarbon into the admixture to form a cathode mix, and fabricating the cathode mix into a cathode.
Claim 10
Independent Claim
53 words
A method of making a hydrophobic cathode for use in a zinc-air cell, comprising the steps of intensively milling gamma manganese dioxide particles, admixing the milled manganese dioxide particles and carbon particles, blending a polymeric halogenated hydrocarbon into the admixture to form a cathode mix, and fabricating the cathode mix into a cathode.
Claim 11
Dependent Claim
42 words
The method of claim 8 wherein said milling comprises dispersing, grinding, beating, and rubbing manganese dioxide particles having a particle size greater than about 10 microns until said manganese dioxide has an average particle size which is less than about 10 microns.
Claim 12
Dependent Claim
19 words
The method of claim 8 wherein said manganese dioxide being intensively milled is an aqueous dispersion of manganese dioxide.
Claim 13
Dependent Claim
20 words
The method of claim 9 wherein said carbon particles are admixed with the manganese dioxide before the milling is completed.
Claim 14
Dependent Claim
26 words
The method of claim 8 wherein said milling is carried out until said manganese dioxide has an average particle size not greater than about 7 microns.
Claim 15
Dependent Claim
23 words
The method of claim 8 wherein said carbon is selected from the group consisting of carbon black, activated carbon, graphite, and mixtures thereof.
Claim 16
Dependent Claim
19 words
The method of claim 13 wherein said carbon has a surface area greater than about 600 m 2 /gram.
Claim 17
Dependent Claim
20 words
The method of claim 8 wherein said polymeric halogenated hydrocarbon comprises polytetrafluoroethylene and said manganese dioxide comprises electrolytic manganese dioxide.
Claim 18
Dependent Claim
60 words
The method of claim 8 wherein said cathode is fabricated by heating the cathode mix between 100° and 250° C. to remove the water; pulverizing and sieving the dried cathode mix to obtain agglomerates of polytetrafluoroethylene, manganese dioxide particles, and carbon particles; applying a uniform layer of said clusters onto a metal grid; and pressing to form a cathode sheet.
Claim 19
Independent Claim
103 words
A method of making a hydrophobic cathode for use in a zinc-air cell comprising the steps of attrition milling an aqueous dispersion of gamma manganese dioxide until the average particle size is less than about 7 microns; then forming an admixture of discrete particles of the milled manganese dioxide and particles of carbon, wherein said carbon comprises carbon having a surface area of at least 1000 m 2 /gram; then blending polytetrafluoroethylene into said admixture to form a cathode mix; and then fabricating the cathode mix into a cathode; wherein said cathode mix comprises at least 20% said manganese dioxide and 20% polytetrafluoroethylene.
Claim 20
Independent Claim
103 words
A method of making a hydrophobic cathode for use in a zinc-air cell comprising the steps of attrition milling an aqueous dispersion of gamma manganese dioxide until the average particle size is less than about 7 microns; then forming an admixture of discrete particles of the milled manganese dioxide and particles of carbon, wherein said carbon comprises carbon having a surface area of at least 1000 m 2 /gram; then blending polytetrafluoroethylene into said admixture to form a cathode mix; and then fabricating the cathode mix into a cathode; wherein said cathode mix comprises at least 20% said manganese dioxide and 20% polytetrafluoroethylene.
Claim 21
Dependent Claim
19 words
The method of claim 17 wherein said cathode mix is fabricated into a cathode by pressing said cathode mix.
Claim 22
Dependent Claim
13 words
The method of claim 17 wherein said manganese dioxide is electrolytic manganese dioxide.
References Cited (Backward Citations)
US3925100A
Cited
US4172183A
Cited
US4248744A
Cited
US4317789A
Cited
US4280973A
Cited
US4604336A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-15 | 1993-07-17 | 1994-01-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-15 | 1997-07-17 | 1998-01-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-15 | 2001-07-17 | 2002-01-16 | $7700.00 | Window Closed / Lapsed |