US4172183A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Alkaline primary cell
Assignee: Leclanche SA
•
Filing: 1978-04-26
•
Granted: 1979-10-23
•
Expires: 1998-04-26
Abstract
Abstract An alkaline primary cell comprising a positive electrode having an upper layer, facing the negative electrode, of electrolytic γ-manganese dioxide to which 6-16% of graphite powder having a broad grain-size range has been added as a conducting additive. Disposed beneath this upper layer is at least one further layer containing γ-manganese dioxide, mercuric oxide, or monovalent silver oxide having a higher apparent specific gravity than the upper layer. A separator comprising at least one membrane layer is situated above the positive electrode.
Inventors
- 👤 Paul Ruetschi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:34
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/62; H01M4/36; H01M50/00; H01M50/10; H01M50/116; H01M50/117; H01M50/119; H01M50/124; H01M50/183; H01M50/184; H01M50/186; H01M50/19; H01M50/193; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/42; H01M50/429; H01M50/449; H01M50/50; H01M50/543; H01M50/545; H01M6/00; H01M6/04; H01M6/06; H01M6/08; H01M2300/00; H01M2300/0002; H01M2300/0014; H01M50/4295; H01M50/44
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
134 words
In a primary cell of the type having an alkaline electrolyte, a positive electrode containing γ-manganese dioxide as active material, and a negative electrode containing amalgamated zinc powder or finely divided cadmium as active material, the improvement comprising a positive electrode having a first depolarizer layer, facing said negative electrode and made of electrolytic γ-manganese dioxide to which 6-16% of graphite powder having a broad grain-size range has been admixed, and at least one further depolarizer layer disposed adjacent to said first depolarizer layer and remote from said negative electrode, having a higher apparent specific gravity (g/cc) than said first depolarizer layer, and containing γ-manganese dioxide, mercuric oxide, or monovalent silver oxide; and a separator containing one or more membrane layers unattackable by and substantially impervious to any manganese ions dissolved in said electrolyte.
Claim 2
Dependent Claim
134 words
In a primary cell of the type having an alkaline electrolyte, a positive electrode containing γ-manganese dioxide as active material, and a negative electrode containing amalgamated zinc powder or finely divided cadmium as active material, the improvement comprising a positive electrode having a first depolarizer layer, facing said negative electrode and made of electrolytic γ-manganese dioxide to which 6-16% of graphite powder having a broad grain-size range has been admixed, and at least one further depolarizer layer disposed adjacent to said first depolarizer layer and remote from said negative electrode, having a higher apparent specific gravity (g/cc) than said first depolarizer layer, and containing γ-manganese dioxide, mercuric oxide, or monovalent silver oxide; and a separator containing one or more membrane layers unattackable by and substantially impervious to any manganese ions dissolved in said electrolyte.
Claim 3
Dependent Claim
93 words
A primary cell in accordance with claim 1 in the form of a button-type cell comprising a cup in which said positive electrode is accommodated and a cover in which said negative electrode is accommodated, wherein said cup is of nickel-plated sheet steel, pure nickel, or a nickel alloy containing at least 65% nickel, and said cover is made of a laminate having an outer side of pure nickel or of a non-rusting nickel alloy and an inner side of copper or an alloy thereof with amalgamable metals having a high hydrogen overvoltage.
Claim 4
Dependent Claim
51 words
A primary cell in accordance with claim 2, wherein said cover is elastically resilient and after closure of said cell is elastically deformed in the finished said cell so that the diameter of said cover is smaller by 0.2-2% than after a possible subsequent elastic relaxation following removal of radial pressure.
Claim 5
Dependent Claim
37 words
A primary cell in accordance with claim 2, further comprising a sealing ring of nylon disposed between said cover and the rim of said cup, and an annular member of neoprene against which said sealing ring rests.
Claim 6
Dependent Claim
18 words
A primary cell in accordance with claim 1, wherein non-fibrous cellulose films are used as said membrane layers.
Claim 7
Dependent Claim
21 words
A primary cell in accordance with claim 1, wherein films of polyethylene-methacrylic acid graft polymer are used as said membrane layers.
Claim 8
Dependent Claim
26 words
A primary cell in accordance with claim 1, further comprising an electronically conductive filter electrode covering the surface of said positive electrode facing said negative electrode.
Claim 9
Dependent Claim
26 words
A primary cell in accordance with claim 1, further comprising an electronically conductive inert network covering the surface of said positive electrode facing said negative electrode.
Claim 10
Dependent Claim
45 words
A primary cell in accordance with claim 1, wherein said graphite powder of said first depolarizer layer comprises a mixture of 25-75% of powdered graphite having a grain-size of predominantly 0.05-5 microns and 75-25% of flaky graphite having a flake diameter of predominantly 10-1000 microns.
Claim 11
Dependent Claim
18 words
A primary cell in accordance with claim 1, wherein said first depolarizer layer contains 0.25-2.5% of polyvinyl pyrrolidone.
Claim 12
Dependent Claim
21 words
A primary cell in accordance with claim 1, wherein said first depolarizer layer has an apparent specific gravity of 2.4-2.9 g/cc.
Claim 13
Dependent Claim
17 words
A primary cell in accordance with claim 1, wherein said first depolarizer layer is 0.2-6 mm thick.
Claim 14
Dependent Claim
30 words
A primary cell in accordance with claim 1, wherein said further depolarizer layer contains a greater weight of γ-manganese dioxide per unit of volume than does said first depolarizer layer.
Claim 15
Dependent Claim
41 words
A primary cell in accordance with claim 1, wherein said further depolarizer layer comprises for the most part γ-manganese dioxide and has an apparent specific gravity which is higher by at least 0.1 g/cc than that of said first depolarizer layer.
Claim 16
Dependent Claim
29 words
A primary cell in accordance with claim 1, wherein said further depolarizer layer contains monovalent silver oxide or mercuric oxide and has an apparent specific gravity of 4-10 g/cc.
Claim 17
Dependent Claim
17 words
A primary cell in accordance with claim 1, wherein said further depolarizer layer is 0.2-6 mm thick.
Claim 18
Dependent Claim
42 words
A primary cell in accordance with claim 1, wherein said further depolarizer layer comprises a plurality of different strata, each of said strata having a different apparent specific gravity which is higher than the apparent specific gravity of said first depolarizer layer.
References Cited (Backward Citations)
US2591532A
Cited
US3657018A
Cited
US3600231A
Cited
US3961985A
Cited
US3920478A
Cited
US3956018A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-10-22 | 1983-04-23 | 1983-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-10-22 | 1987-04-23 | 1987-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-10-22 | 1991-04-23 | 1991-10-23 | $7700.00 | Window Closed / Lapsed |