Polarizers based on polyacetylene, and the production thereof

Claim 2

Polarizers based on a polymer matrix which is constructed from polar or nonpolar monomer units or mixtures thereof, characterized in that polyacetylene is included as light-polarizing substance, said polyacetylene being obtained by polymerizing acetylene in solutions of said polymer matrix and thereafter processing the resultant polyacetylene/polymer solutions into polarizers.

Claim 3

Polarizers according to claim 1, characterized in that the polymer matrix is constructed from polar monomer units.

Claim 4

Polarizers according to claim 1, characterized in that the polymer matrix is constructed from a mixture of polar and nonpolar units.

Claim 5

Polarizers according to claim 1, characterized in that polyacetylene is distributed homogeneously in the matrix.

Claim 6

Polarizers according to claim 1, characterized in that less than 50% by weight of polyacetylene is included.

Claim 7

Polarizers according to claim 1, characterized in that processing results in moulded articles of films wherein further a privileged direction is generated.

Claim 8

Polarizers according to claim 6, characterized in that processing results in films.

Claim 9

Polarizers according to claim 6, characterized in that the privileged direction is generated by stretching or drawing.

Claim 10

Polarizers according to claim 1, characterized in that acetylene polymerization is carried out in the presence of acetylene polymerization catalysts which are not deactivated by the matrix polymer solution.

Claim 11

Polarizers according to claim 9, characterized in that the acetylene polymerization is carried out in the presence of nickel compounds as catalysts.

Claim 12

Polarizers according to claim 10, characterized in that the acetylene polymerization is carried out in the presence of nickel compounds which can be prepared by reaction of nickel-(0) compound, or a compound which can be converted into a nickel-(0) compound in situ, with compounds of the formula (I) or of the formula (I) and (II) ##STR3## in which R 1 , R 2 and R 3 , independently of one another, denote C 1 -C 20 -alkyl, C 6 -C 12 -aryl, or C 3 -C 8 -cycloalkyl unsubstituted or substituted by halogen, hydroxyl, C 1 -C 20 -alkoxy, C 6 C 12 -aryloxy or nitro, or R 1 , R 2 and R 3 are C 6 -C 12 -aryl- C 1 -C 20 -alkyl, C 1 -C 20 -alky-C 6 -C 12 -aryl, C 1 -C 20 -alkyl-C 3 -C 8 -cycloalkyl, C 6 -C 12 -aryl-C 3 -C 8 -cyclo-alkyl, C 2 -C 6 -alkenyl, C 6 -C 12 -aryl-C 2 -C 6 -alkenyl, di-C 1 -C 4 -alkylamino, phenoxy, substituted phenoxy or alkoxy, X denotes O, NR 9 or ##STR4## n denotes zero or one, R 4 , R 5 , R 6 , R 7 and R 8 ,independently of one another, denote C 1 -C 20 -alkyl, C 6 -C 12 -aryl, C 2 -C 30 -alkenyl or C 3 -C 8 -cycloalkyl unsubstituted or substituted by halogen, hydroxyl, C 1 -C 20 -alkoxy or C 6 -C 12 -aryloxy, C.sub. 6-C 12 -aryl, or R 4 , R 5 , R 6 , R 7 and R 8 are halogen, hydroxyl, C 1 -C 20 -alkoxy or C 6 -C 12 -aryloxy, R 7 denotes hydrogen R 8 denotes hydrogen or sulphonate, acyl, and R 9 , R 10 and R 11 , independently of one another, denote hydrogen, acyl, silyl, nitrophenyl, halogen, cyano or R 1 , or by reaction of nickel compounds which can be prepared by reaction of a nickel-(0) compound, or a compound which can be converted into a nickel-(0) compound in situ, with an adduct or a mixture of maleic anhydride, a compound of the formula II where n=0 and a compound of the formula II where n=0 or 1, in which R 1 , R 2 and R 3 have the above-mentioned meaning, or nickel compounds which can be prepared by reaction of a nickel-(0) compound, or a compound which can be converted into a nickel-(0) compound in situ, with an adduct or a mixture of a quinoid compound and a compound of the formula II where n=0 and a compound of the formula II where n=0 or 1, in which R 1 , R 2 and R 3 have the above-mentioned meaning.

Claim 13

Polarizers according to claim 10, characterized in that the acetylene polymerization is carried out at a temperature of 60°-100° C.

Claim 14

Polarizers according to claim 12, characterized in that the nickel compound is present in a concentration of 10 -2 -10 -4 mole per liter.

Claim 15

Polarizers according to claim 10, characterized in that the nickel compound is present in an amount of 0.1-10% be weight, relative to the amount of acetylene.

Claim 16

Polarizers according to claim 14, characterized in that the nickel compound is present in an amount of 0.5-5% be weight, relative to the amount of acetylene.

Claim 17

Polarizers according to claim 1, characterized in that the acetylene polymerization is carried out at a temperature of 0°-140° C.

Claim 18

Polarizers according to claim 16, characterized in that the acetylene polymerization is carried out at a temperature of 60°-100° C.

Claim 19

Polarizers which comprise a polymer matrix with polyacetylene homogeneously distributed therein as a light-polarizing substance.

Claim 20

Polarizers which comprise a polymer matrix with polyacetylene homogeneously distributed therein as a light-polarizing substance.

Claim 21

Polarizers according to claim 18, characterized in that the matrix contains less than 50% by weight of polyacetylene.

Claim 22

Polarizers according to claim 18 wherein the polymer matrix comprises copolymerized polar monomers and non-polar monomers.