US4892637A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Plastic-bound gas diffusion electrode containing a manganese oxide catalyst and process for preparing same
Assignee: VARTA Microbattery GmbH
•
Filing: 1988-06-23
•
Granted: 1990-01-09
•
Expires: 2008-06-23
Abstract
Abstract A process which comprises thermally decomposing in an electrically heated vibrating helical conveyor, manganese carbonate (MnCO3x H2O) into a manganese oxide (predominantly of Mn2O3 x Mn5O8) catalyst at about 500 DEG C., and processing this catalyst into a highly active electrode paste by dry intensive mixing with a carbon-containing conductive material (carbon black, graphite or activated carbon) and PTFE as the binder. The resulting electrode paste can be rolled into a supporting net made from Ni or Ag. Also a two-step mixing process in which the catalyst powder is first premixed with small amounts of a conductive agent and a binder, compacted and granulated, and then combined with the larger residual amount of the intended amounts of conductive agent and binder in a second mixing step. The finished gas diffusion electrode has a biporous structure consisting of hydrophilic and hydrophobic pore canals, which is highly favorable for the transport processes and the electrochemical reaction. The electrode is useful in fuel cells, alkali chloride electrolyzers and air cells.
Inventors
- 👤 Hans Sauer
- 👤 August Winsel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:13
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/8663; H01M4/8668; C; C25; C25B; C25B11/00; C25B11/04; C25B11/051; C25B11/073; C25B11/091; C25B11/095; H01M4/88; H01M4/8825; H01M4/8828; H01M4/90; H01M4/9016; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
146 words
A process for preparing a plastic-bound gas diffusion electrode, especially for fuel cells, alkali chloride electrolyzers, and air cells, which electrode contains a manganese oxide catalyst predominantly of the composition Mn 2 O 3 ×Mn 5 O 8 , and which process comprises completely thermally decomposing and oxidizing manganese carbonate (MnCO 3 ) at a temperature in the range of about 450° C. to about 550° C. in the presence of air, producing a catalytic manganese oxide decomposition product constituted of Mn 2 O 3 ×Mn 5 O 8 ; adding polytetrafluoroethylene (PTFE) and a conductive material to the manganese oxide decomposition product; mixing and compacting the PTFE, conductive material and manganese oxide decomposition product, thereby forming a granulated first mixture; mixing with the first mixture a prepared second mixture of conductive material and PTFE, thereby forming an electrode paste mixture suitable for forming an electrode.
Claim 2
Dependent Claim
146 words
A process for preparing a plastic-bound gas diffusion electrode, especially for fuel cells, alkali chloride electrolyzers, and air cells, which electrode contains a manganese oxide catalyst predominantly of the composition Mn 2 O 3 ×Mn 5 O 8 , and which process comprises completely thermally decomposing and oxidizing manganese carbonate (MnCO 3 ) at a temperature in the range of about 450° C. to about 550° C. in the presence of air, producing a catalytic manganese oxide decomposition product constituted of Mn 2 O 3 ×Mn 5 O 8 ; adding polytetrafluoroethylene (PTFE) and a conductive material to the manganese oxide decomposition product; mixing and compacting the PTFE, conductive material and manganese oxide decomposition product, thereby forming a granulated first mixture; mixing with the first mixture a prepared second mixture of conductive material and PTFE, thereby forming an electrode paste mixture suitable for forming an electrode.
Claim 3
Dependent Claim
17 words
The process of claim 1 wherein the temperature range is between about 510° C. and 530° C.
Claim 4
Dependent Claim
34 words
The process of claim 2 wherein the product mixture contains an amount of manganese oxide in the range of about 15 to 65 weight percent and about 15 to 35 weight percent of PTFE.
Claim 5
Dependent Claim
53 words
The process of claim 2 wherein the first mixture comprises smaller portions of the total amount of conductive agent and PTFE which are mixed and compacted with the manganese oxide decomposition product to yield a granulated first mixture and wherein the second mixture comprises a greater residual amount of conductive agent and PTFE.
Claim 6
Dependent Claim
19 words
The process of claim 4 wherein the first mixture is compacted and granulated prior to adding the residual amounts.
Claim 7
Dependent Claim
33 words
The process of claim 4 wherein the larger residual amounts of conductive agent and PTFE are intensively mixed separately and then are charged into the granulated first mixture in a short mixing process.
Claim 8
Dependent Claim
35 words
The process of claim 4 wherein the electrode mixture contains about 15 weight percent to about 65 weight percent manganese oxide catalyst and 15 to 35 weight percent PTFE, the balance being carbon-containing conductive agent.
Claim 9
Dependent Claim
18 words
The process of claim 1 wherein the decomposition time is between about 30 minutes and about 2 hours.
Claim 10
Dependent Claim
27 words
The process of claim 8 wherein finely ground potassium hydroxide powder or potassium permanganate powder is added to the manganese carbonate powder during mixing with the PTFE.
Claim 11
Dependent Claim
20 words
The process of claim 1 wherein the temperature is above about 500° C. and the manganese carbonate is completely decomposed.
Claim 12
Dependent Claim
21 words
The process of claim 1 wherein the thermal decomposition of the manganese carbonate is carried out in a vibrating helical conveyer.
Claim 13
Dependent Claim
19 words
The process of claim 1 wherein the electrode paste mixture is formed into a foil on a metal screen.
Claim 14
Dependent Claim
27 words
The process of claim 1 wherein the particle size of the manganese oxide decomposition product catalyst is in the range of about 10 um to 40 um.
Claim 15
Dependent Claim
63 words
A biporous gas diffusion electrode of improved cathodic load potential which is gas and liquid permeable and which consists essentially of from about 15 to about 65 percent of catalytic manganese oxide as, Mn 2 O 3 ×Mn 5 O 8 with Mn 2 O 3 being predominate, and from about 15 to 35 percent of polytetrafluoroethylene (PTFE) and a carbon-containing conductive agent.
Claim 16
Dependent Claim
63 words
A biporous gas diffusion electrode of improved cathodic load potential which is gas and liquid permeable and which consists essentially of from about 15 to about 65 percent of catalytic manganese oxide as, Mn 2 O 3 ×Mn 5 O 8 with Mn 2 O 3 being predominate, and from about 15 to 35 percent of polytetrafluoroethylene (PTFE) and a carbon-containing conductive agent.
Claim 17
Dependent Claim
14 words
The electrode of claim 14 which is a film supported by a metal screen.
Claim 18
Dependent Claim
15 words
The electrode of claim 14 wherein the electrode material is free of MnO 2 .
Claim 19
Dependent Claim
20 words
The electrode of claim 14 wherein the electrode material contains also ground potassium hydrate powder or potassium per manganate powder.
Claim 20
Dependent Claim
35 words
The electrode of claim 14 wherein the pores of the electrode are contiguous hydrophilic pores containing electrolyte and contiguous hydrophobic pores containing a gaseous phase, said hydrophilic and hydrophobic pores being interconnected with each other.
References Cited (Backward Citations)
US3978007A
Cited
US4060476A
Cited
JPS5258821A
Cited
US4256545A
Cited
US4269691A
Cited
US4595643A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-08 | 1993-07-10 | 1994-01-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-08 | 1997-07-10 | 1998-01-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-08 | 2001-07-10 | 2002-01-09 | $7700.00 | Window Closed / Lapsed |