Photographic film antistatic backing layer with auxiliary layer having improved properties
Assignee: Agfa Gevaert NV
•
Filing: 1989-04-14
•
Granted: 1990-01-02
•
Expires: 2009-04-14
Abstract
Abstract As part of a photographic film, a backing antistatic layer is coated at a pH of 3 to 12 with an auxiliary layer consisting essentially of at least one crosslinkable conductive polymer and a crosslinking agent for the conductive polymer dispersed in a binder, e.g., gelatin, to conduct the antistatic properties from the antistatic underlayer to the surface of the backing layer. The crosslinkable conductive polymer and crosslinking agent can be present in separate layers on the backing layer. The film is useful in the areas of graphic arts, printing, medical and information systems.
Inventors
- 👤 Thomas B. Cho
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:13
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/76; G03C1/7614; G03C1/85; G03C1/89; G03C2001/7628
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
187 words
A photographic element consisting essentially of a support, at least one silver halide emulsion layer on one side of said support, and on the opposite side of said support in order are (a) a layer containing an antistatic agent and (b) an auxiliary layer consisting essentially of at least one crosslinkable conductive polymer having frunctionally attached carboxylic acid groups selected from the group consisting of poly(sodium styrene sulfonate-maleic anhydride), hexadecyl betaine, alkyldimethyl betaines, carboxylated imidazolines, coco amido betaines, and mixtures thereof and a crosslinking agent for the conductive polymer selected from the group consisting of a polyfunctional aziridine, chrome alum, carbodiimides, and isoxazolinium salts dispersed in a gelatin binder, the auxiliary layer coated from an aqueous solution on said antistatic layer at a pH of 3 to 12, the crosslinkable conductive polymer being present in an amount of 0.5 to 30% by weight based on the weight of the gelatin binder, and the crosslinking agent being present in an amount of 0.5 to 5% by weight based on the weight of gelatin binder, whereby the antistatic properties of the antistatic layer are conducted through the auxiliary layer.
Claim 2
Dependent Claim
187 words
A photographic element consisting essentially of a support, at least one silver halide emulsion layer on one side of said support, and on the opposite side of said support in order are (a) a layer containing an antistatic agent and (b) an auxiliary layer consisting essentially of at least one crosslinkable conductive polymer having frunctionally attached carboxylic acid groups selected from the group consisting of poly(sodium styrene sulfonate-maleic anhydride), hexadecyl betaine, alkyldimethyl betaines, carboxylated imidazolines, coco amido betaines, and mixtures thereof and a crosslinking agent for the conductive polymer selected from the group consisting of a polyfunctional aziridine, chrome alum, carbodiimides, and isoxazolinium salts dispersed in a gelatin binder, the auxiliary layer coated from an aqueous solution on said antistatic layer at a pH of 3 to 12, the crosslinkable conductive polymer being present in an amount of 0.5 to 30% by weight based on the weight of the gelatin binder, and the crosslinking agent being present in an amount of 0.5 to 5% by weight based on the weight of gelatin binder, whereby the antistatic properties of the antistatic layer are conducted through the auxiliary layer.
Claim 3
Dependent Claim
39 words
A photographic film according to claim 1 wherein the auxiliary layer is replaced by two separately coated gelatin-containing layers, the first coated layer containing at least one crosslinkable conductive polymer and the second coated layer containing a crosslinking agent.
Claim 4
Dependent Claim
17 words
A photographic film according to claim 1 wherein the crosslinkable conductive polymer is poly(sodium polystyrene sulfonate-maleic anhydride).
Claim 5
Dependent Claim
17 words
A photographic film according to claim 2 wherein the crosslinkable conductive polymer is poly(sodium polystyrene sulfonate-maleic anhydride).
Claim 6
Dependent Claim
15 words
A photographic film according to claim 1 wherein the crosslinking agent is a polyfunctional aziridine.
Claim 7
Dependent Claim
15 words
A photographic film according to claim 2 wherein the crosslinking agent is a polyfunctional aziridine.
Claim 8
Dependent Claim
14 words
A photographic film according to claim 5 wherein the polyfunctional aziridine is pentaerythritol-tri-beta-(2-methyl aziridine).
Claim 9
Dependent Claim
14 words
A photographic film according to claim 6 wherein the polyfunctional aziridine is pentaerythritol-tri-beta-(2-methyl aziridine).
Claim 10
Dependent Claim
15 words
A photographic film according to claim 1 wherein the support is a polyethylene terephthalate film.
Claim 11
Dependent Claim
19 words
A photographic film according to claim 1 wherein the silver halide emulsion is covered with a protective overcoat layer.
Claim 12
Dependent Claim
179 words
A photographic film consisting essentially of a polyethylene terephthalate film support, at least one silver halide emulsion layer on one side of the support, the emulsion layer being overcoated with a protective overcoat layer, and on the opposite side of the support in order are (a) layer containing an antistatic agent and (b) an auxiliary layer consisting essentially of a crosslinkable conductive polymer selected from the group consisting of poly(sodium styrene sulfonatemaleic anhydride, hexadecyl betaine, alkyldimethyl betaines, carboxylated imidazolines, coco amido betaines, and mixtures thereof, and a crosslinking agent selected from the group consisting of a polyfunctional aziridine, chrome alum, carbodiimides, and isoxazolinium salts, dispersed in a gelatin binder, coated from an aqueous solution on said antistatic layer at a pH of 3 to 12, wherein the crosslinkable conductive polymer is present in an amount of 0.5 to 30% by weight and the crosslinking agent is present in an amount of 0.5 to 5% by weight, both weights based on the weight of gelatin binder, whereby the antistatic properties of the antistatic layer are conducted through the auxiliary layer.
Claim 13
Dependent Claim
179 words
A photographic film consisting essentially of a polyethylene terephthalate film support, at least one silver halide emulsion layer on one side of the support, the emulsion layer being overcoated with a protective overcoat layer, and on the opposite side of the support in order are (a) layer containing an antistatic agent and (b) an auxiliary layer consisting essentially of a crosslinkable conductive polymer selected from the group consisting of poly(sodium styrene sulfonatemaleic anhydride, hexadecyl betaine, alkyldimethyl betaines, carboxylated imidazolines, coco amido betaines, and mixtures thereof, and a crosslinking agent selected from the group consisting of a polyfunctional aziridine, chrome alum, carbodiimides, and isoxazolinium salts, dispersed in a gelatin binder, coated from an aqueous solution on said antistatic layer at a pH of 3 to 12, wherein the crosslinkable conductive polymer is present in an amount of 0.5 to 30% by weight and the crosslinking agent is present in an amount of 0.5 to 5% by weight, both weights based on the weight of gelatin binder, whereby the antistatic properties of the antistatic layer are conducted through the auxiliary layer.
Claim 14
Dependent Claim
26 words
A photographic film according to claim 11 wherein the auxiliary layer (b) is replaced by a crosslinkable conductive polymer/gelatin layer followed by a crosslinking agent/gelatin layer.
Claim 15
Dependent Claim
30 words
A photographic film according to claim 11 wherein the crosslinkable conductive polymer is present in an amount of 1.5 to 2.5% by weight based on the weight of gelatin binder.
Claim 16
Dependent Claim
29 words
A photographic film according to claim 13 wherein the crosslinking agent is present in an amount of 2 to 3% by weight based on the weight of gelatin binder.
Claim 17
Dependent Claim
24 words
A photographic film according to claim 11 wherein the crosslinkable conductive polymer is poly(sodium styrene sulfonate-maleic anhydride) and the crosslinking agent is pentaerythritol-tri-beta-(2-methyl aziridine).
Claim 18
Dependent Claim
24 words
A photographic film according to claim 12 wherein the crosslinkable conductive polymer is poly(sodium styrene sulfonate-maleic anhydride) and the crosslinking agent is pentaerythritol-tri-beta-(2-methyl aziridine).
References Cited (Backward Citations)
US4225665A
Cited
US4209584A
Cited
US4396708A
Cited
US4675278A
Cited
US4585730A
Cited
US4701403A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-01-01 | 1993-07-03 | 1994-01-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-01-01 | 1997-07-03 | 1998-01-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-01-01 | 2001-07-03 | 2002-01-02 | $7700.00 | Window Closed / Lapsed |