Silver-copper-titanium brazing alloy containing crust inhibiting element
Assignee: Osram Sylvania Inc
•
Filing: 1988-11-07
•
Granted: 1989-11-28
•
Expires: 2008-11-07
Abstract
Abstract A silver-copper-titanium brazing alloy contains a small amount of tin, indium, silicon, aluminum or manganese as a crust inhibiting element.
Inventors
- 👤 Howard Mizuhara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 06:25
CPC Classifications
B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3006; C; C22; C22C; C22C5/00; C22C5/06; C22C5/08; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12431
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
79 words
A brazing alloy having a composition consisting essentially of titanium in an amount of 0.5 to 5 weight percent, silver in an amount of 55 to 73 weight percent, from 0.1 to less than 2 weight percent of at least one crust eliminating element, selected from the group consisting of tin, indium, silicon, aluminum and manganese which inhibits crust formation of the brazing alloy when the brazing alloy is melted and cooled, the balance of the composition being copper.
Claim 2
Dependent Claim
79 words
A brazing alloy having a composition consisting essentially of titanium in an amount of 0.5 to 5 weight percent, silver in an amount of 55 to 73 weight percent, from 0.1 to less than 2 weight percent of at least one crust eliminating element, selected from the group consisting of tin, indium, silicon, aluminum and manganese which inhibits crust formation of the brazing alloy when the brazing alloy is melted and cooled, the balance of the composition being copper.
Claim 3
Dependent Claim
21 words
The brazing alloy of claim 1 having a composition of, in weight percent, 71 Ag, 1.5 Ti, 0.5 Sn, 27 Cu.
Claim 4
Dependent Claim
21 words
The brazing alloy of claim 1 having a composition of, in weight percent, 63 Ag, 1.5 Ti, 0.5 Sn, 35 Cu.
Claim 5
Dependent Claim
21 words
The brazing alloy of claim 1 having a composition of, in weight percent, 63 Ag, 1.5 Ti, 1.0 In, 34.5 Cu.
Claim 6
Dependent Claim
21 words
The brazing alloy of claim 1 having a composition of, in weight percent, 65 Ag, 1.5 Ti, 1 Si, 32.5 Cu.
Claim 7
Dependent Claim
22 words
The brazing alloy of claim 1 having a composition of, in weight percent, 63 Ag, 1.5 Ti, 0% 0.55 Al, 35 Cu.
Claim 8
Dependent Claim
21 words
The brazing alloy of claim 1 having a composition of, in weight percent, 63 Ag, 1.5 Ti, 0.5 Mn, 35 Cu.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-27 | 1993-05-29 | 1993-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-27 | 1997-05-29 | 1997-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-27 | 2001-05-29 | 2001-11-28 | $7700.00 | Window Closed / Lapsed |