Magneto-optical recording medium
Assignee: Ricoh Co Ltd
•
Filing: 1987-10-28
•
Granted: 1989-11-28
•
Expires: 2007-10-28
Abstract
Abstract A magneto-optical recording medium is disclosed, which comprises a substrate, and a magnetic layer supported on the substrate, the magnetic layer comprising (1) a first magnetic layer comprising a magnetic oxide with perpendicular magnetic characteristics, having a saturation magnetization Ms of 100 Gauss or less and a coercive force Hc1 of 1 KOe or less, and (2) a second magnetic layer comprising a magnetic oxide having a thermal conductivityxof less than 0.3 cal/cm.sec. DEG C. and a light absorption coefficient alpha of 5x103 cm-1 or more. This magneto-optical recording medium may further comprises an auxiliary production layer comprising a magnetic material, which is overlaid adjacent to the first magnetic layer.
Inventors
- 👤 Hajime Machida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:14
CPC Classifications
G; G11; G11B; G11B11/00; G11B11/10; G11B11/105; G11B11/10582; G11B11/10586; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
91 words
A magneto-optical recording medium comprising a substrate, and a magnetic layer supported on said substrate, said magnetic layer comprising: a first magnetic layer comprising a magnetic oxide with perpendicular magnetic characteristics, having a saturation magnetization Ms of 100 Gauss or less and a coercive force Hc 1 of 1 KOe or more, and a second magnetic layer adjacent to said first magnetic layer comprising a magnetic oxide having a thermal conductivity x of less than 0.3 cal/cm.sec.° C. and a light absorption coefficient α of 5×10 3 cm -1 or more.
Claim 2
Dependent Claim
91 words
A magneto-optical recording medium comprising a substrate, and a magnetic layer supported on said substrate, said magnetic layer comprising: a first magnetic layer comprising a magnetic oxide with perpendicular magnetic characteristics, having a saturation magnetization Ms of 100 Gauss or less and a coercive force Hc 1 of 1 KOe or more, and a second magnetic layer adjacent to said first magnetic layer comprising a magnetic oxide having a thermal conductivity x of less than 0.3 cal/cm.sec.° C. and a light absorption coefficient α of 5×10 3 cm -1 or more.
Claim 3
Dependent Claim
28 words
The magneto-optical recording medium as claimed in claim 1, further comprising an auxiliary production layer comprising a magnetic material, which is directly adjacent to said first magnetic layer.
Claim 4
Dependent Claim
75 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said first magnetic layer is a magnetoplumbite hexagonal ferrite consisting of Fe and Me, in which Me is at least one element selected from the group consisting of Ba, Sr, Pb, La and Ca, and the Fe atoms are partly replaced by at least one element other than the Fe atoms, and the atomic ratio of Fe to Me is 10˜12.
Claim 5
Dependent Claim
22 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said first magnetic layer is cobalt spinel ferrite.
Claim 6
Dependent Claim
20 words
The magneto-optical recording medium as claim in claim 1, wherein said magnetic oxide of said first magnetic layer is iron-garnet.
Claim 7
Dependent Claim
22 words
The magneto-optical recording medium as claim in claim 1, wherein said magnetic oxide of said second magnetic layer is cobalt spinel ferrite.
Claim 8
Dependent Claim
22 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said second magnetic layer is nickel spinel ferrite.
Claim 9
Dependent Claim
79 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said first magnetic layer is a magnetoplumbite hexagonal ferrite having formula, Me[Ma.sub.x Mb.sub.y Fe.sub.12- x-y]O.sub.19 wherein Me represents one element selected from the group consisting of Ba, Sr, Pb, Ca and La; Ma represents one element selected from the group consisting of Al, Ga, Cr and Rh; Mb represents one element selected from the group consisting of Ti, In, Sc and Zn; 2≦x≦6; and 1≦y≦3.
Claim 10
Dependent Claim
24 words
The magneto-optical recording medium as claimed in claim 1, wherein said first magnetic layer has a thickness ranging from 0.1 μm to 5 μm.
Claim 11
Dependent Claim
38 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said second magnetic layer has a coercive force Hc 2 which is smaller than the coercive force Hc 1 of said first magnetic layer.
Claim 12
Dependent Claim
73 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said second magnetic layer is a cobalt spinel ferrite having general formula, Co.sub.x M.sub.y Fe.sub.3-(x +y) O.sub.4 wherein M represents one element selected from the group consisting of Al, Cr, Mn, Ni, Zn, Ga, Si, Sc, In, Ti, V, Cu, W, Ge, Sb, Sn, Mg, Rh, Ru, Ca, Mo, Nb, Zr and Co 3+ ; 0<x<2.0; 0<y<2.5; and 0<x+y≦2.5.
Claim 13
Dependent Claim
72 words
The magneto-optical recording medium as claimed in claim 1, wherein said magnetic oxide of said second magnetic layer is a nickel spinel ferrite having general formula, Ni.sub.x M.sub.y Fe.sub.3-(x+y) O.sub.4 wherein M represents one element selected from the group consisting of Al, Cr, Mn, Ni, Zn, Ga, Si, Sc, In, Ti, V, Cu, W, Ge, Sb, Sn, Mg, Rh, Ru, Ca, Mo, Nb, Zr and Co 3+ ; 0<x<2.0; 0<y<2.5; and 0<x+y≦2.5.
Claim 14
Dependent Claim
24 words
The magneto-optical recording medium as claimed in claim 1, wherein said second magnetic layer has a thickness ranging from 0.1 μm to 0.5 μm.
Claim 15
Dependent Claim
67 words
The magneto-optical recording medium as claimed in claim 2, wherein said magnetic material of said auxiliary production layer has general formula, [R.sub.3 ][M.sub.x Fe.sub.5-x ]O.sub.12 wherein R represents an element having a larger ionic radius larger than that of Fe, M represents an element having almost the same ionic radius as that of Fe, and x is the substitution number for Fe in the range of 0≦x<3.
Claim 16
Dependent Claim
57 words
The magneto-optical recording medium as claimed in claim 14, wherein the element represented by R is selected from the group consisting of Y, Bi, Dy, Er, Ho, Yb, Lu, Nd, Pr, Sm, Eu, Gd, Tb and La, and the element represented by M is selected from the group consisting of Al, Ga, Ti, Zn, Ni and Co.
Claim 17
Dependent Claim
28 words
The magneto-optical recording medium as claimed in claim 1, wherein the first magnetic layer has a higher Curie point that the Curie point of said second magnetic layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-27 | 1993-05-29 | 1993-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-27 | 1997-05-29 | 1997-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-27 | 2001-05-29 | 2001-11-28 | $7700.00 | Window Closed / Lapsed |