Composition and process for making porous articles from ultra high molecular weight polyethylene

Assignee: CNA Holdings LLC
•
Filing: 1988-03-28
•
Granted: 1989-11-14
•
Expires: 2008-03-28
📄 Original PDF 🌐 Google Patents 🔄 Sync Now

Abstract

Abstract Porous shaped articles made from a molded composite of ultra high molecular weight polyethylene and polyethylene wax are disclosed. These articles are produced by free-sintering a non intensively mixed blend of UHMW-PE particles and particles of a polyethylene wax. The process involves mixing the UHMW-PE and wax both in powdered form until a heterogeneous mixture is formed, but under conditions which do not lead to any substantial fracturing of the UHMW-PE particles or melting of either component. The heterogeneous mix is then transferred to a press mold to form a shape and pressure is applied sufficient only to maintain the enclosed volume of the shape. The mold is heated to a temperature above the melting point of the UHMW-PE for a period of time to allow the particles to soften, expand, and contact one another at their surfaces. The mixture is then quickly cooled. Porous articles so produced may exhibit stiffness values in excess of about 2000 psi while at the same time showing excellent porosity values of less than about 25 inches water pressure drop.

Inventors

  • 👤 Harvey L. Stein

Bibliographic Details

Application Number —
Jurisdiction US
Data Source google_patents
Last Synchronized 2026-11-07 19:19
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/24; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/06; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; C08L2205/00; C08L2205/02; C08L2207/00; C08L2207/06; C08L2207/068; C08L91/00; C08L91/06; Y; Y10; Y10S; Y10S521/00; Y10S521/919

Claims Analysis

Total Claims: 7
Claim 1
Independent Claim 100 words
A molding powder composition comprising a uniform heterogeneous mixture of particles of polyethylene having a molecular weight within the range of about 1×10 6 to about 6×10 6 as determined by the intrinsic viscosity of a 0.5 weight percent solution in decahydronaphthalene at 135° C., and particles of polyethylene wax having a molecular weight within the range of about 1,000 to about 20,000, the particle size distribution of said particles of polyethylene polymer being within the range of at least about 95% by weight smaller than 0.5 millimeters and not greater than about 15% by weight smaller than 0.063 millimeters.
Claim 2
Dependent Claim 100 words
A molding powder composition comprising a uniform heterogeneous mixture of particles of polyethylene having a molecular weight within the range of about 1×10 6 to about 6×10 6 as determined by the intrinsic viscosity of a 0.5 weight percent solution in decahydronaphthalene at 135° C., and particles of polyethylene wax having a molecular weight within the range of about 1,000 to about 20,000, the particle size distribution of said particles of polyethylene polymer being within the range of at least about 95% by weight smaller than 0.5 millimeters and not greater than about 15% by weight smaller than 0.063 millimeters.
Claim 3
Dependent Claim 30 words
The composition of claim 1 containing from about 40 to about 95% by weight of said polyethylene polymer and from about 5 to 60% by weight of said polyethylene wax.
Claim 4
Dependent Claim 37 words
The composition of claim 2 wherein said polyethylene wax has a molecular weight within the range of about 2,000 to about 10,000, and a melting point within the range of about 100° C. to about 150° C.
Claim 5
Dependent Claim 42 words
The composition of claim 3 wherein said polyethylene wax has a particle size distribution in the range of at least about 95% by weight of particles smaller than 0.5 millimeters and not greater than about 15% by weight smaller than 0.063 millimeters.
Claim 6
Dependent Claim 30 words
The composition of claim 2 containing from about 55 to 85% by weight of said polyethylene polymer and from about 15 to about 45% by weight of said polyethylene wax.
Claim 7
Dependent Claim 23 words
The composition of claim 5 containing about 75% by weight of said polyethylene polymer and about 25% by weight of said polyethylene wax.

References Cited (Backward Citations)

US3954927A Cited
US3944536A Cited
US4237037A Cited
US4487875A Cited
EP0115192B1 Cited
US4588633A Cited

USPTO Annuity & Maintenance Windows

Annuity Stage Window Opens Payment Deadline Surcharge Period Until Estimated Fee Status
3.5 Years (Year 4) 1992-11-13 1993-05-15 1993-11-14 $2000.00 Window Closed / Lapsed
7.5 Years (Year 8) 1996-11-13 1997-05-15 1997-11-14 $3760.00 Window Closed / Lapsed
11.5 Years (Year 12) 2000-11-13 2001-05-15 2001-11-14 $7700.00 Window Closed / Lapsed