Abstract Polyimide polymer composites having a combination of enhanced thermal and mechanical properties even when subjected to service temperatures as high as 700° F. are described. They comprise (a) from 10 to 50 parts by weight of a thermoplastic polyimide resin prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane and (b) from 90 to 50 parts by weight of continuous reinforcing fibers, the total of (a) and (b) being 100 parts by weight. Composites based on polyimide resin formed from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane and pyromellitic dianhydride and continuous carbon fibers retained at least about 50% of their room temperature shear strength after exposure to 700° F. for a period of 16 hours in flowing air. Preferably, the thermoplastic polyimide resin is formed in situ in the composite material by thermal imidization of a corresponding amide-acid polymer prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane. It is also preferred to initially size the continuous reinforcing fibers with up to about one percent by weight of an amide-acid polymer prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane. In this way imidization at a suitable elevated temperature results in the in-situ formation of a substantially homogeneous thermoplastic matrix of the polyimide resin tightly and intimately bonded to the continuous fibers. The resultant composites tend to have optimum thermo-mechanical properties.
A process of forming a fiber-reinforced composite which comprises (a) forming a prepreg thermoplastic lay-up made of a stack of plies composed of a (i) thermoplastic polyimide resin prepared from the imidization of a polyamic acid of the formula ##STR3## where R is an organic group of 5 to 22 carbon atoms which may be an aliphatic radical, including alicyclic, or an aromatic radical having one or more benzene or fused polynuclear rings and (ii) continuous reinforcing fibers, the composite having from 10 to 50 parts by weight of said resin and from 90 to 50 parts by weight of said fibers; (b) compression molding said thermoplastic polyimide lay-up by applying thereto progressively increased pressure and temperature in stages; (c) cooling said compression molded thermoplastic polyimide lay-up while under pressure; (d) heating the lay-up resulting from step (c) while unrestrained in air at a temperature of at least 700° F.
Claim 2
Dependent Claim
150 words
A process of forming a fiber-reinforced composite which comprises (a) forming a prepreg thermoplastic lay-up made of a stack of plies composed of a (i) thermoplastic polyimide resin prepared from the imidization of a polyamic acid of the formula ##STR3## where R is an organic group of 5 to 22 carbon atoms which may be an aliphatic radical, including alicyclic, or an aromatic radical having one or more benzene or fused polynuclear rings and (ii) continuous reinforcing fibers, the composite having from 10 to 50 parts by weight of said resin and from 90 to 50 parts by weight of said fibers; (b) compression molding said thermoplastic polyimide lay-up by applying thereto progressively increased pressure and temperature in stages; (c) cooling said compression molded thermoplastic polyimide lay-up while under pressure; (d) heating the lay-up resulting from step (c) while unrestrained in air at a temperature of at least 700° F.
Claim 3
Dependent Claim
23 words
A process of claim 1 further characterized in that the continuous reinforcing fibers in said prepreg lay-up are composed substantially of carbon fibers.
Claim 4
Dependent Claim
28 words
A process of claim 1 further characterized in that the thermoplastic polyimide resin in said prepreg lay-up is a thermoplastic polyimide resin prepared from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane and pyromellitic dianhydride.
Claim 5
Dependent Claim
26 words
A process of claim 1 still characterized by sizing the continuous reinforcing fiber with said polyimide prior to impregnating the fiber with the amide-acid polymeric precursor.
Claim 6
Dependent Claim
54 words
A process of claim 1, further characterized in that the plies of said stack of plies are produced by impregnating continuous reinforcing carbon fiber with an amide-acid polymeric polyimide precursor produced from 2,2-bis[4-(4-aminophenoxylphenyl]hexafluoropropane and pyromellitic dianhydride and heating the resultant prepreg to a temperature high enough to cause the amide-acid polymer to be imidized.
Claim 7
Dependent Claim
32 words
A process of claim 5 still further characterized by sizing the continous reinforcing fiber with a polyimide produced from 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane and pyromellitic dianhydride and thereafter impregnating the sized fiber with said precursor.