Method of applying opaque dental ceramic material to a metal structure
Assignee: Dentsply GmbH
•
Filing: 1987-10-15
•
Granted: 1989-11-07
•
Expires: 2007-10-15
Abstract
Abstract A method of building a dental appliance and a kit for use in the method are provided. In the method, metal copings are coated with an opaque ceramic paste, and a coarse ceramic powder, having structural stability under the conditions needed to fire the ceramic paste, is dusted on the coating of ceramic paste, and the coping is fired. A coated metal coping with a rough, sandpaper like surface is produced, and subsequent layers of ceramic paste are applied to the rough surface to build up the dental appliance. The kit of the invention provides at least one preformed opaque ceramic paste, dusting powders, and other ingredients needed to build a dental appliance.
Inventors
- 👤 M. H. Polz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:46
CPC Classifications
A; A61; A61C; A61C13/00; A61C13/0003; A61C5/00; A61C5/70; A61C5/77; A61K; A61K6/00; A61K6/15; A61K6/16; A61K6/17; A61K6/20; A61K6/70; A61K6/78; A61K6/80; A61K6/802; A61K6/816; A61K6/818; A61K6/822; A61K6/84
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
137 words
A method for coating a metal structure for a dental appliance consisting essentially of the steps of: preparing an opaque ceramic paste by mixing an opaque ceramic powder with an organic liquid having a boiling point below about 300° C., coating said metal structure with said opaque ceramic paste to prepare a coating of opaque ceramic paste on said metal structure, dusing said coating with a coarse ceramic powder having an average grain size of from about 40 um to about 100 um said powder having thermal stability such that at least a substantial part of grain structure of said powder is maintained under conditions of firing said dental appliance, applying at least one additional layer of ceramic opaque paste, applying a stain paste to an additional layer of ceramic opaque paste, and firing said dental appliance.
Claim 2
Independent Claim
137 words
A method for coating a metal structure for a dental appliance consisting essentially of the steps of: preparing an opaque ceramic paste by mixing an opaque ceramic powder with an organic liquid having a boiling point below about 300° C., coating said metal structure with said opaque ceramic paste to prepare a coating of opaque ceramic paste on said metal structure, dusing said coating with a coarse ceramic powder having an average grain size of from about 40 um to about 100 um said powder having thermal stability such that at least a substantial part of grain structure of said powder is maintained under conditions of firing said dental appliance, applying at least one additional layer of ceramic opaque paste, applying a stain paste to an additional layer of ceramic opaque paste, and firing said dental appliance.
Claim 3
Dependent Claim
22 words
The method according to claim 1 in which said organic liquid is selected from the group consisting of glycerol, glycol, or dimethylsulfoxide.
Claim 4
Dependent Claim
13 words
A method according to claim 2 in which said organic liquid is glycerol.
Claim 5
Dependent Claim
45 words
The method according to claim 1 in which said ceramic paste further contains about 10% to 20% by weight SnO 2 , CeO 2 , TiO 2 , ArO 2 , ZrSiO 4 or mixtures thereof, having a particle size less than about 2 um.
Claim 6
Dependent Claim
29 words
A method according to claim 1 in which said ceramic powder used in said first opaque paste comprises grains having a particle diameter of less than about 40 um.
Claim 7
Dependent Claim
46 words
The method according to claim 1 which comprises the further step of preparing the ceramic opaque paste used for at least one of said additional layers of ceramic by mixing a dental ceramic powder with an organic liquid having a boiling point below about 300° C.
Claim 8
Dependent Claim
36 words
The method according to claim 1 which comprises the further step of loading said ceramic paste into a package in which it can be stored and from which said paste can be put directly into use.
Claim 9
Dependent Claim
13 words
The method according to claim 7 in which said package is a syringe.
Claim 10
Dependent Claim
35 words
The method according to claim 1 which comprises the step of applying said additional layer of opaque paste in such a manner that the gaps between projecting grains of coarse ceramic material are totally filled.
Claim 11
Dependent Claim
35 words
The method according to claim 1 which comprises the step of preparing a stain paste by mixing a dry preparation of stain powder with an organic liquid having a boiling point below about 300° C.
Claim 12
Dependent Claim
37 words
The method according to claim 1 which comprises the step of preparing a stain paste by mixing a dry preparation of stain powder with an organic liquid selected from the group consisting of glycerol, glycol, or dimethylsulfoxide.
Claim 13
Dependent Claim
14 words
The method according to claim 1 in which said firing is a vacuum firing.
Claim 14
Dependent Claim
191 words
A kit for preparing a dental appliance comprising: a first component (a) at least one pre-formed, shelf stable, ready to use opaque ceramic paste prepared by mixing an opaque ceramic powder comprising a mixture of SiO 2 , Al 2 O 3 , K 2 O, Na 2 O, Li 2 O, CaO, B 2 O 3 , ZrO 2 and SnO 2 having a grain size iof about 5-40 um with an organic liquid selected from the group consisting of glycerol, glycol or dimethylsulfoxide, wherein said ceramic paste further contains about 10% to 20% by weight SnO 2 , CeO 2 , TiO 2 , ZrO 2 , ZrSiO 4 or mixtures thereof, having a particle size of less than about 2 um and a second component (b) a coarse ceramic powder comprising SiO 2 , Al 2 O 3 , K 2 O, Na 2 O and CeO 2 having an average grain size of from about 40 um to 100 um, in which said coarse ceramic powder has a thermal stability such that at least a portion of said grain structure is maintained under the conditions of firing.
Claim 15
Dependent Claim
191 words
A kit for preparing a dental appliance comprising: a first component (a) at least one pre-formed, shelf stable, ready to use opaque ceramic paste prepared by mixing an opaque ceramic powder comprising a mixture of SiO 2 , Al 2 O 3 , K 2 O, Na 2 O, Li 2 O, CaO, B 2 O 3 , ZrO 2 and SnO 2 having a grain size iof about 5-40 um with an organic liquid selected from the group consisting of glycerol, glycol or dimethylsulfoxide, wherein said ceramic paste further contains about 10% to 20% by weight SnO 2 , CeO 2 , TiO 2 , ZrO 2 , ZrSiO 4 or mixtures thereof, having a particle size of less than about 2 um and a second component (b) a coarse ceramic powder comprising SiO 2 , Al 2 O 3 , K 2 O, Na 2 O and CeO 2 having an average grain size of from about 40 um to 100 um, in which said coarse ceramic powder has a thermal stability such that at least a portion of said grain structure is maintained under the conditions of firing.
Claim 16
Dependent Claim
25 words
The kit according to claim 13 in which said pre-formed opaque paste component (a) is packaged in a syringe for easy dispensing of said paste.
Claim 17
Dependent Claim
13 words
The kit according to claim 13 in which said organic liquid is glycerol.
References Cited (Backward Citations)
US3338732A
Cited
US3880662A
Cited
US4064311A
Cited
US4021915A
Cited
US4010048A
Cited
US4198244A
Cited
US4264640A
Cited
US4468251A
Cited
US4426404A
Cited
US4556389A
Cited
US4461618A
Cited
US4645488A
Cited
EP0119062A2
Cited
US4557691A
Cited
US4559191A
Cited
EP0152337A2
Cited
US4645454A
Cited
DE3524783A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-06 | 1993-05-08 | 1993-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-06 | 1997-05-08 | 1997-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-06 | 2001-05-08 | 2001-11-07 | $7700.00 | Window Closed / Lapsed |