Method for preparing a dental prosthesis
Assignee: Individual
•
Filing: 1978-08-30
•
Granted: 1981-04-28
•
Expires: 1998-08-30
Abstract
Abstract Two dispersant compositions are disclosed for use in the fabrication of a dental prosthesis, the compositions serving for the dispersion and deposition of an opacifier layer and a porcelain color layer over the opacifier layer. The dispersants are so formulated that only a single firing is used to produce both the opaque and porcelain bisque simultaneously, whereas prior methods required firing of the opaque layer prior to application of the porcelain color layer. A method of application to insure effective hiding of the metallic substrate, especially near the gingival portion, is disclosed.
Inventors
- 👤 Samuel J. Infante
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:59
CPC Classifications
A; A61; A61C; A61C13/00; A61C13/08; A61C13/083; A61C13/0835; A61K; A61K6/00; A61K6/15; A61K6/16; A61K6/20; A61K6/80; A61K6/831; A61K6/836; A61K6/84
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
67 words
A method of preparing a dental prosthesis, comprising coating a metal base with a ceramic opaque coat dispersed in a first organic binder, drying the coat, scraping away said coat at the gum line to expose said metal base, coating the dried ceramic opaque coat and exposed base at the gum line with a porcelain coat dispersed in a second organic binder, drying and firing the prosthesis.
Claim 2
Independent Claim
67 words
A method of preparing a dental prosthesis, comprising coating a metal base with a ceramic opaque coat dispersed in a first organic binder, drying the coat, scraping away said coat at the gum line to expose said metal base, coating the dried ceramic opaque coat and exposed base at the gum line with a porcelain coat dispersed in a second organic binder, drying and firing the prosthesis.
Claim 3
Dependent Claim
62 words
The method of preparing a dental prosthesis of claim 1, comprising the steps of adding flux to said ceramic opaque coat prior to applying same, adjusting said porcelain coat after the first firing and carrying out a second firing to produce a glaze, said first firing being effected at about 1770° F. and said second firing being effected at about 1800° F.
Claim 4
Dependent Claim
83 words
The method of claim 1, including the step of dispersing a ceramic opaque in the first organic binder, which comprises a solution of a copolymer of ethyl acrylate and acrylic acid neutralized with ammonia and a solution of a first terpolymer of styrene, butylacrylate and acrylic acid and a second terpolymer of styrene, methylmethacrylate and methacrylic acid, both of said terpolymers being neutralized with ammonia and dilute ammonia, the acid contents of said copolymer and terpolymers being great enough to provide aqueous solubility.
Claim 5
Dependent Claim
56 words
The method of claim 3, further including the step of preparing said first organic binder by mixing from about 20 to 30 parts by volume of said copolymer solution, 20 to 30 parts by volume of said terpolymer solution and 40 to 60 parts by volume of about 0.65 to 0.95 weight percent dilute aqueous ammonia.
Claim 6
Dependent Claim
34 words
The method of claim 4, further comprising the step of including from about 0.3 to 0.5 weight percent powdered borosilicate glass in said first organic binder for lowering the firing temperature of the dispersant.
Claim 7
Dependent Claim
110 words
The method of claim 3, including forming the copolymer solution by mixing an aqueous solution of about 19 to 25 weight percent copolymer of about 93 to 97 parts by volume ethyl acrylate and 3 to 7 parts by volume acrylic acid and forming the aqueous terpolymer solution by mixing an aqueous solution of about 20 to 24 weight percent of the first terpolymer of about 10 weight percent styrene, 85 weight percent butylacrylate and 5 weight percent acrylic acid and an aqueous solution of 13 to 17 weight percent of the second terpolymer of about 10 weight percent styrene, 85 weight percent methylmethacrylate and 5 weight percent methacrylic acid.
Claim 8
Dependent Claim
31 words
The method of claim 1, including the step of forming the second organic binder by mixing an aqueous solution of a copolymer of methylmethacrylic and vinyl acetate with polyvinylalcohol and methanol.
Claim 9
Dependent Claim
64 words
The method of claim 7, wherein said second organic binder comprises from about 8 to 12 parts by volume of copolymer of about 88 to 91 weight percent methylmethacrylate and 9 to 12 weight percent vinylacetate, from about 6 to 8 parts by volume polyvinylalcohol, from about 800 to 865 parts by volume water and from about 130 to 170 parts by volume methanol.
Claim 10
Dependent Claim
24 words
The method of claim 8, further including from about 90 to 112 parts by volume water and 350 to 450 parts by volume isopropanol.
Claim 11
Dependent Claim
23 words
The method of claim 7, further including the step of adding an effective amount of 1,3-butanediol for increasing the solubility of the copolymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-04-27 | 1984-10-27 | 1985-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-04-27 | 1988-10-27 | 1989-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-04-27 | 1992-10-27 | 1993-04-28 | $7700.00 | Window Closed / Lapsed |