Rapidly solidified aluminum based, silicon containing alloys for elevated temperature applications
Assignee: Honeywell International Inc
•
Filing: 1987-09-08
•
Granted: 1989-11-07
•
Expires: 2007-09-08
Abstract
Abstract A rapidly solidified aluminum-base alloy consists essentially of the formula AlbalFeaSibXc+L, wherein X is at least one element selected from the group consisting of Mn,V,Cr,Mo,W,Nb,Ta, "a" ranges from 2.0 to 7.5 atom percent, "b" ranges from 0.5 to 3.0 atom percent, "c" ranges from 0.05 to 3.5 atom percent and the balance is aluminum plus incidental impurities, with the proviso that the ratio {Fe+X}:Si ranges from about 2.0:1 to 5.0:1. The alloy exhibits high strength, ductility and fracture toughness and is especially suited for use in high temperature structural applications such as gas turbine engines, missiles, airframes and landing wheels.
Inventors
- 👤 Colin M. Adam
- 👤 Richard L. Bye
- 👤 Santosh K. Das
- 👤 David J. Skinner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 18:08
CPC Classifications
C; C22; C22C; C22C45/00; C22C45/08; B; B22; B22F; B22F9/00; B22F9/002; B22F9/008
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
130 words
A rapidly solidified aluminum-base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio (Fe+X):Si ranges from about 2.0:1 to 5.0:1, said alloy having an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100nm in any dimension thereof and having a cubic structure.
Claim 2
Dependent Claim
130 words
A rapidly solidified aluminum-base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio (Fe+X):Si ranges from about 2.0:1 to 5.0:1, said alloy having an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100nm in any dimension thereof and having a cubic structure.
Claim 3
Dependent Claim
33 words
An alloy as recited in claim 1, said alloy having been rapidly solidified in an ambient atmosphere at a quench rate of at least about 10 5 ° to 10 7 ° C./sec.
Claim 4
Independent Claim
157 words
A method for forming a consolidate metal alloy article wherein particles composed of an aluminum-base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio ranges from about 2.0:1 to 5.0:1 are heated in a vacuum to a temperature ranging from about 300 to 500° C. and compacted to form an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100 nm in any dimension thereof and having a cubic structure.
Claim 5
Independent Claim
157 words
A method for forming a consolidate metal alloy article wherein particles composed of an aluminum-base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio ranges from about 2.0:1 to 5.0:1 are heated in a vacuum to a temperature ranging from about 300 to 500° C. and compacted to form an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100 nm in any dimension thereof and having a cubic structure.
Claim 6
Dependent Claim
24 words
A method as recited in claim 3, wherein said heating step comprising heating said particles to a temperature ranging from 325° to 450° C.
Claim 7
Independent Claim
182 words
A method for forming a consolidated metal alloy article wherein: (a) particles composed of an aluminum-base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group beginning of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio :Si ranges from about 2.0:1 to 5.0:1 are placed in a container, heated to a temperature ranging from about 300 to 500° C., evacuated and sealed under vacuum, and (b) said container and contents are heated to a temperature ranging from 300 to 500° C. and compacted to form an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100 nm in any dimension thereof and having a cubic structure.
Claim 8
Independent Claim
182 words
A method for forming a consolidated metal alloy article wherein: (a) particles composed of an aluminum-base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group beginning of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, with the proviso that the ratio :Si ranges from about 2.0:1 to 5.0:1 are placed in a container, heated to a temperature ranging from about 300 to 500° C., evacuated and sealed under vacuum, and (b) said container and contents are heated to a temperature ranging from 300 to 500° C. and compacted to form an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each of said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100 nm in any dimension thereof and having a cubic structure.
Claim 9
Dependent Claim
27 words
A method as recited in claim 5, wherein said heating step comprises heating said container and contents to a temperature ranging from 325° C. to 450° C.
Claim 10
Dependent Claim
136 words
A consolidated metal article compacted from particles of an aluminum base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, the ratio {Fe+X}:Si ranging from about 2.0:1 to 5.0:1, said consolidated article being composed of an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100 nm. in any dimension thereof and having a cubic structure.
Claim 11
Dependent Claim
136 words
A consolidated metal article compacted from particles of an aluminum base alloy consisting essentially of the formula Al bal Fe a Si b X c , wherein X is at least one element selected from the group consisting of Mn, V, Cr, Mo, W, Nb, Ta, "a" ranges from 2.0 to 7.5 at %, "b" ranges from 0.5 to 3.0 at %, "c" ranges from 0.05 to 3.5 at % and the balance is aluminum plus incidental impurities, the ratio {Fe+X}:Si ranging from about 2.0:1 to 5.0:1, said consolidated article being composed of an aluminum solid solution phase containing therein a substantially uniform distribution of dispersed, intermetallic phase precipitates, each said precipitates being of approximate composition Al 12 (Fe,X) 3 Si, measuring less than about 100 nm. in any dimension thereof and having a cubic structure.
Claim 12
Dependent Claim
32 words
A consolidated metal article as recited in claim 7, wherein said article has the form of a sheet having a width of at least 0.5" and a thickness of at least 0.010".
Claim 13
Dependent Claim
43 words
A consolidated metal article as recited in claim 8, wherein said particles of aluminum-base alloy are compacted at a temperature of about 400 to 550° C. and each of the said dispersed intermetallic precipitates measure less than 500 nm. in any dimension thereof.
Claim 14
Dependent Claim
24 words
A consolidated metal article as recited in claim 7, wherein the volume fraction of said fine intermetallic precipitates ranges from about 10 to 50%.
Claim 15
Dependent Claim
23 words
A consolidated metal article as recited in claim 7, wherein said article is compacted by forging without substantial loss of its mechanical properties.
Claim 16
Dependent Claim
22 words
A consolidated metal article as recited in claim 7, wherein said article is compacted by extruding through a die into balk shapes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-11-06 | 1993-05-08 | 1993-11-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-11-06 | 1997-05-08 | 1997-11-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-11-06 | 2001-05-08 | 2001-11-07 | $7700.00 | Window Closed / Lapsed |