Method for making electrically conductive textile materials
Assignee: Milliken and Co
•
Filing: 1988-06-27
•
Granted: 1989-10-31
•
Expires: 2008-06-27
Abstract
Abstract Fabrics are made electrically conductive by contacting the fiber under agitation conditions with an aqueous solution of a pyrrole compound, an oxidizing agent and a doping agent or counter ion and then depositing onto the surface of individual fibers of the fabric a prepolymer of the pyrrole compound so as to uniformly and coherently cover the fibers with a conductive film of the polymerized pyrrole compound and wherein, furthermore, the oxidizing agent is a ferric salt and the aqueous solution further contains a weak complexing agent for ferric ions to effectively control the reaction rate such that the prepolymer is uniformly and coherently adsorbed onto the surface of the textile material, thereby providing improved films of electrically conductive polymerized compound on the textile material.
Inventors
- 👤 Hans H. Kuhn
- 👤 William C. Kimbrell, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:45
CPC Classifications
D; D06; D06M; D06M13/00; D06M13/10; D06M13/184; D06M13/188; D06M13/244; D06M13/248; D06M13/256; D06M13/322; D06M13/35; D06M13/352; H; H01; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/124; H01B1/127; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T442/00; Y10T442/20; Y10T442/2418; Y10T442/2459
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
204 words
A method for imparting electrical conductivity to a textile material, which comprises: (a) contacting the textile material with an aqueous solution of an oxidatively polymerizable pyrrole compound and an oxidizing agent capable of oxidizing said compound to a polymer, said contacting being carried out in the presence of a counter ion or doping agent which imparts electrical conductivity to said polymer when fully formed, said contacting being under conditions at which the pyrrole compound and the oxidizing agent react with each other to form a prepolymer in said aqueous solution; (b) depositing onto the surface of the textile material the prepolymer of the polymerizable compound; and (c) allowing the prepolymer to polymerize while deposited on the textile material so as to uniformly and coherently cover the textile material with a conductive film of polymerized compound; the improvement wherein in step (a) a ferric salt is used as the oxidizing agent and a weak complexing agent for ferric ions is included in the aqueous solution, in an amount sufficient to effectively control the polymerization rate of steps (b) and (c) such that the prepolymer is uniformly and coherently adsorbed onto the surface of the textile material while effectively avoiding undesired formation of polymer in solution.
Claim 2
Independent Claim
204 words
A method for imparting electrical conductivity to a textile material, which comprises: (a) contacting the textile material with an aqueous solution of an oxidatively polymerizable pyrrole compound and an oxidizing agent capable of oxidizing said compound to a polymer, said contacting being carried out in the presence of a counter ion or doping agent which imparts electrical conductivity to said polymer when fully formed, said contacting being under conditions at which the pyrrole compound and the oxidizing agent react with each other to form a prepolymer in said aqueous solution; (b) depositing onto the surface of the textile material the prepolymer of the polymerizable compound; and (c) allowing the prepolymer to polymerize while deposited on the textile material so as to uniformly and coherently cover the textile material with a conductive film of polymerized compound; the improvement wherein in step (a) a ferric salt is used as the oxidizing agent and a weak complexing agent for ferric ions is included in the aqueous solution, in an amount sufficient to effectively control the polymerization rate of steps (b) and (c) such that the prepolymer is uniformly and coherently adsorbed onto the surface of the textile material while effectively avoiding undesired formation of polymer in solution.
Claim 3
Dependent Claim
30 words
The method of claim 1 wherein said pyrrole compound is selected from the group consisting of pyrrole, a 3- and 3,4-alkyl or aryl substituted pyrrole, N-alkyl pyrrole and N-aryl pyrrole.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said weak complexing agent is selected from aromatic, hydroxycarboxylic acids, and aromatic, hydroxysulfonic acids.
Claim 5
Dependent Claim
13 words
The method of claim 3 wherein said weak complexing agent is sulfosalicylic acid.
Claim 6
Dependent Claim
26 words
The method of claim 1 wherein said pyrrole compound is present in said solution in an amount of from about 0.01 to 5 grams per liter.
Claim 7
Dependent Claim
18 words
The method of claim 1 wherein said textile material comprises a knitted, woven or non-woven fibrous textile fabric.
Claim 8
Dependent Claim
31 words
The method of claim 6 where the fibers of said fabric are uniformly and coherently covered with said conductive film to a thickness of from about 0.05 to about 2 microns.
Claim 9
Dependent Claim
15 words
The method of claim 6 wherein said textile fabric is constructed of continuous filament yarns.
Claim 10
Dependent Claim
23 words
The method of claim 8 wherein said textile fabric comprises synthetic fibers selected from the group consisting of polyester, nylon and acrylic fibers.
Claim 11
Dependent Claim
22 words
The method of claim 8 wherein said textile fabric comprises high modulus fibers selected from aromatic polyester, aromatic polyamide and polybenzimidazole fibers.
Claim 12
Dependent Claim
20 words
The method of claim 8 wherein said textile material comprises high modulus inorganic fibers selected from glass and ceramic fibers.
Claim 13
Dependent Claim
22 words
The method of claim 7 wherein said treated textile fabric has a resistivity from about 50 to about 500,000 ohms per square.
Claim 14
Dependent Claim
18 words
The method of claim 7 wherein said textile material is or is comprised of basic dyeable polyester fibers.
Claim 15
Dependent Claim
16 words
The method of claim 1 wherein said textile material comprises a wound yarn, filament or fiber.
Claim 16
Dependent Claim
19 words
The method of claim 1 wherein said pyrrole compound is pyrrole, N-methylpyrrole or a mixture of pyrrole and N-methylpyrrole.
Claim 17
Dependent Claim
30 words
The method of claim 1 wherein said counter ion is an anionic counter ion selected from the group consisting of chloride, sulfate, alkyl or aryl-sulfonic acid, and aryl disulfonic acids.
Claim 18
Dependent Claim
32 words
An electrically conductive textile material which is the product of the process of claim 1, having a resistivity in the range of from about 50 to about 10 6 ohms per square.
Claim 19
Dependent Claim
21 words
The electrically conductive material of claim 17 which is a fabric comprised of fibers, filaments or yarns of polyester or polyamide.
Claim 20
Dependent Claim
26 words
The electrically conductive material of claim 17 wherein the pyrrole compound is pyrrole and the polypyrrole film has a thickness of less than about 2 microns.
References Cited (Backward Citations)
US3909195A
Cited
US4521450A
Cited
US4568483A
Cited
US4468291A
Cited
GB2133022A
Cited
US4569734A
Cited
US4547270A
Cited
US4578433A
Cited
US4697000A
Cited
US4710401A
Cited
US4617228A
Cited
US4696835A
Cited
US4697001A
Cited
US4604427A
Cited
US4642331A
Cited
US4710400A
Cited
US4617353A
Cited
GB2181367A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-30 | 1993-05-01 | 1993-10-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-30 | 1997-05-01 | 1997-10-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-30 | 2001-05-01 | 2001-10-31 | $7700.00 | Window Closed / Lapsed |