Synthetic filament-reinforced polymer material sheet and process for producing the same
Assignee: Teijin Ltd
•
Filing: 1987-09-10
•
Granted: 1989-10-17
•
Expires: 2007-09-10
Abstract
Abstract A synthetic filament-reinforced polymer material sheet having a very small thickness of 0.25 mm or less and a large specific tensile strength of 3.4×10 6 cm or more is composed of a reinforcing sheet in which a number of straightened individual synthetic polymer filaments are arranged in parallel to each other and are spaced from each other at an average interval not larger than the average thickness of the filaments, and which has a width W anmd a thickness T satisfying the relationship W/T≧40 and a coefficient of variation of thickness of 30% or less, and a polymer material impregnated in the spaces between the individual filaments.
Inventors
- 👤 Yoshiyuki Sasaki
- 👤 Tetsuo Okamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:47
CPC Classifications
B; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/10; B29C70/16; B29C70/20; B29C70/28; B29C70/54; B29C70/56; D; D02; D02G; D02G1/00; D02G1/10; D04; D04H; D04H3/00; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/249942; Y10T428/249947
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
112 words
A synthetic filament-reinforced polymer material sheet having a thickness of 0.25 mm or less and a specific tensile strength of 3.4×10 6 cm or more, and comprising: a reinforcing sheet comprising a number of individual synthetic polymer filaments straightened and arranged substantially in parallel to each other and spaced from each other at an average interval equal to or smaller than the average thickness of the individual filaments, and having a width W and a thickness T thereof satisfying the relationship: W/T≧40 and a coefficient of variation in the thickness thereof of 30% or less; and a polymer material impregnated in the reinforcing sheet to fill the spaces among the individual filaments.
Claim 2
Dependent Claim
112 words
A synthetic filament-reinforced polymer material sheet having a thickness of 0.25 mm or less and a specific tensile strength of 3.4×10 6 cm or more, and comprising: a reinforcing sheet comprising a number of individual synthetic polymer filaments straightened and arranged substantially in parallel to each other and spaced from each other at an average interval equal to or smaller than the average thickness of the individual filaments, and having a width W and a thickness T thereof satisfying the relationship: W/T≧40 and a coefficient of variation in the thickness thereof of 30% or less; and a polymer material impregnated in the reinforcing sheet to fill the spaces among the individual filaments.
Claim 3
Dependent Claim
31 words
The sheet as claimed in claim 1, wherein the individual filaments comprise a synthetic polymer selected from wholly aromatic polyamides, modified polymers of the above-mentioned polyamides, wholly aromatic polyesters, and polyethylenes.
Claim 4
Dependent Claim
20 words
The sheet as claimed in claim 2, wherein the individual filaments comprise a poly-p-phenylene terephthalamide or a modified polymer thereof.
Claim 5
Dependent Claim
32 words
The sheet as claimed in claim 1, 2, or 3, wherein the individual filaments have a degree of orientation of 90% or more and a degree of crystallization of 65% or more.
Claim 6
Dependent Claim
73 words
The sheet as claimed in claim 1, wherein the polymer material comprises at least one member selected from epoxy resins, phenolic compound-formaldehyde resins, unsaturated polyester resins, diallylphthalate resins, bis-maleimide resins, triazine resins, silicone resins, polybutylene terephthalate resins, saturated polyester resins, polyacetal resins, polycarbonate resins, aliphatic polyamide (nylon) resins, modified polyphenyleneoxide resins, polysulfon resins, polyethersulfon resins, polyphenylenesulfide resins, polyallylate resins, polyamideimide resins, polyetherimide resins, polyetherketone resins, polyimide resins, polyoxybenzoate resins, and fluorine-containing polymer resins.
Claim 7
Dependent Claim
25 words
The sheet as claimed in claim 1, wherein the reinforcing sheet and the polymer material are in a weight ratio of from 70:30 to 20:80.
Claim 8
Dependent Claim
18 words
The sheet as claimed in claim 1, wherein the individual filaments have a denier of 0.8 to 6.
References Cited (Backward Citations)
US3180003A
Cited
US3255875A
Cited
US3505155A
Cited
US3391050A
Cited
DE1629830A1
Cited
US3472730A
Cited
US4216856A
Cited
EP0167303A1
Cited
US4612241A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-16 | 1993-04-17 | 1993-10-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-16 | 1997-04-17 | 1997-10-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-16 | 2001-04-17 | 2001-10-17 | $7700.00 | Window Closed / Lapsed |