US4873283A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Molded or formed poly(arylene thioether-ketone) articles
Assignee: Kureha Corp
•
Filing: 1988-05-12
•
Granted: 1989-10-10
•
Expires: 2008-05-12
Abstract
Abstract Disclosed herein is a molded or formed poly(arylene thioether-ketone) article made of a thermoplastic material which comprises 100 parts by weight of a melt-stable poly(arylene thioether-ketone) (PTK) and if desired, up to 100 parts by weight of at least one of thermoplastic resins and/or up to 300 parts by weight of at least one of fibrous fillers and/or least one of inorganic fillers. The PTK has predominant recurring units of the formula ##STR1## wherein the --CO-- and --S-- are in the para position to each other, and has a melting point, Tm of 310°-380° C., a residual melt cyrstallization enthalpy, ΔHmc (420° C./10 min) of at least 10 J/g, a melt crystallization temperature, Tmc (420° C./10 min) of at least 210° C., and a reduced viscosity of 0.2-2 dl/g as determined by viscosity measurement at 25° C. and a polymer concentration of 0.5 g/dl in 98 percent by weight sulfuric acid. This invention provides extruded articles, injection-molded articles, unstretched films and the like, all of which have practical physical properties, by using a novel high-density and high crystallinity PTK having melt stability sufficient to apply conventional melt processing techniques.
Inventors
- 👤 Yoshikatsu Satake
- 👤 Yo Iizuka
- 👤 Toshitaka Kouyama
- 👤 Takayuki Katto
- 👤 Zenya Shiiki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:10
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; B; B29; B29C; B29C55/00; B29C55/005; C08G; C08G75/00; C08G75/02; C08G75/0204; C08G75/0227; C08G75/0236; C08G75/024; C08G75/025; C08G75/0254; C08L; C08L81/00; C08L81/02; B29K; B29K2081/00; C08J2381/00; C08J2381/02; C08L101/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
215 words
A molded or formed poly(arylene thioether-ketone) article made of a thermoplastic material which comprises: (A) 100 parts by weight of a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR8## wherein the --CO-- and--S-- are in the para position to each other, and having the following physical properties (a)-(c): (a) melting point, Tm being 310°-380° C.; (b) residual melt crystallization enthalpy, ΔHmc 420° C./10 min) being at least 10 J/g, and melt crystallization temperature, Tmc (420° C./10 min) being at least 210° C., wherein Δ Hmc (420° C./10 min) and Tmc (420° C./10 min) are determined by a differential scanning colorimeter at a cooling rate of 10° C./min, after the poly(arylene thioether-ketone) is held at 50° C. for 5 minutes in an inert gas atmosphere, heated to 420° C. at a rate of 75° C./min and then held for I0 minutes at 420° C.; and (c) reduced viscosity being 0.2-2 dl/g as determined by viscosity measurement at 25° C. and a polymer concentration of 0.5g/dl in 98 percent by weight sulfuric acid; and optionally, (B) at least one component selected from (i) up to 100 arts weight of at least one thermoplastic resin and (ii) up to 300 parts by weight of at least one filler selected from fibrous fillers nd inorganic fillers.
Claim 2
Dependent Claim
215 words
A molded or formed poly(arylene thioether-ketone) article made of a thermoplastic material which comprises: (A) 100 parts by weight of a melt-stable poly(arylene thioether-ketone) having predominant recurring units of the formula ##STR8## wherein the --CO-- and--S-- are in the para position to each other, and having the following physical properties (a)-(c): (a) melting point, Tm being 310°-380° C.; (b) residual melt crystallization enthalpy, ΔHmc 420° C./10 min) being at least 10 J/g, and melt crystallization temperature, Tmc (420° C./10 min) being at least 210° C., wherein Δ Hmc (420° C./10 min) and Tmc (420° C./10 min) are determined by a differential scanning colorimeter at a cooling rate of 10° C./min, after the poly(arylene thioether-ketone) is held at 50° C. for 5 minutes in an inert gas atmosphere, heated to 420° C. at a rate of 75° C./min and then held for I0 minutes at 420° C.; and (c) reduced viscosity being 0.2-2 dl/g as determined by viscosity measurement at 25° C. and a polymer concentration of 0.5g/dl in 98 percent by weight sulfuric acid; and optionally, (B) at least one component selected from (i) up to 100 arts weight of at least one thermoplastic resin and (ii) up to 300 parts by weight of at least one filler selected from fibrous fillers nd inorganic fillers.
Claim 3
Dependent Claim
31 words
The article as claimed in claim 1, wherein the poly(arylene thioether-ketone) has a density of at least 1.34 g/cm 3 at 25° C. when annealed at 280° C. for 30 minutes.
Claim 4
Dependent Claim
15 words
The article as claimed in claim 1, wherein the poly(arylene thioether-ketone) is an uncured polymer.
Claim 5
Dependent Claim
28 words
The article as claimed in claim 1, wherein the poly(arylene thioether-ketone) is a polymer with at least some structure selected from crosslinked structure and branched structure introduced therein.
Claim 6
Dependent Claim
23 words
The article as claimed in claim 1, wherein the thermoplastic material is substantially free of said at least one of the thermoplastic resins.
Claim 7
Dependent Claim
28 words
The article as claimed in claim 1, wherein said at least one of the thermoplastic resins is a poly(arylene thioether) having predominant recurring units of the formula ##STR9##
Claim 8
Dependent Claim
28 words
The article as claimed in claim 1, wherein the thermoplastic material contains 0.1-300 parts by weight of at least one filler selected from fibrous fillers and inorganic fillers.
Claim 9
Dependent Claim
24 words
The article as claimed in claim 7, wherein said at least one of the fibrous fillers is selected from glass fibers and carbon fibers.
Claim 10
Dependent Claim
14 words
The article as claimed in claim 1, wherein the article is an extruded article.
Claim 11
Dependent Claim
84 words
The article as claimed in claim 9, wherein the extruded article has the following physical properties (a)-(e): (a) density of poly(arylene thioether-ketone) portion being at least 1.34 g/cm 3 at 25° C.; (b) heat distortion temperature being at least 135° C. under 18.6 kg/cm 2 load; (c) tensile strength being at least 5 kg/mm 2 at 23° C.; (d) tensile modulus being at least 100 kg/mm 2 at 23° C.; and (e) Izod impact strength (unnotched) being at least 5 kg·cm/cm at 23° C.
Claim 12
Dependent Claim
14 words
The article as claimed in claim 1, wherein the article is an injection-molded article.
Claim 13
Dependent Claim
84 words
The article as claimed in claim 11, wherein the injection-molded article has the following physical properties (a)-(e): (a) density of poly(arylene thioether-ketone) portions being at least 1.34 g/cm 3 at 25° C.; (b) heat distortion temperature being at least 135° C. under 18.6 kg/cm 2 load; (c) flexural strength being at least 5 kg/mm 2 at 23° C.; (d) flexural modulus being at least 100 kg/mm 2 at 23° C.; and (e) Izod impact strength (unnotched) being at least 5 kg·cm/cm at 23° C.
Claim 14
Dependent Claim
14 words
The article as claimed in claim 1, wherein the article is an unstretched film.
Claim 15
Dependent Claim
78 words
The article as claimed in claim 13, wherein the unstretched film has been obtained by melt-forming, into a film-like configuration, a thermoplastic material composed of 100 parts by weight of the melt-stable poly(arylene thioether-ketone) and optionally, the at least one component selected from (i) up to 100 parts by weight of the at least one thermoplastic resin and (ii) up to 200 parts by weight of the at least one filler selected from fibrous fillers and inorganic fillers.
Claim 16
Dependent Claim
87 words
The article as claimed in claim 13, wherein the unstretched film has the following physical properties (a)-(d): (a) density of poly(arylene thioether-ketone) portions being at least I.34 g/cm 3 at 25° C.; (b) tensile strength being at least 5 kg/mm 2 at 23° C. or at least I kg/mm 2 at 250° C.; (c) tensile modulus being at least 100 kg/mm 2 at 23° C. or at least 5 kg/mm 2 at 250° C.; and (d) temperature of 10-second solder heat resistance being at least 280 C.
Claim 17
Dependent Claim
31 words
The article as claimed in claim 14, wherein the unstretched film contains, as at least one of the thermoplastic resins, a poly(arylene thioether) having predominant recurring units of the formula ##STR10##
References Cited (Backward Citations)
JPS4713347U
Cited
JPS6058435A
Cited
JPS60104126A
Cited
DE3405523A1
Cited
US4590104A
Cited
US4698415A
Cited
JPS61221229A
Cited
US4745167A
Cited
US4690972A
Cited
US4716212A
Cited
EP0270955A2
Cited
EP0274754A2
Cited
EP0280325A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-09 | 1993-04-10 | 1993-10-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-09 | 1997-04-10 | 1997-10-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-09 | 2001-04-10 | 2001-10-10 | $7700.00 | Window Closed / Lapsed |