US4871694A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cellular ceramic material and method of production thereof
Assignee: Individual
•
Filing: 1987-09-17
•
Granted: 1989-10-03
•
Expires: 2007-09-17
Abstract
Abstract A material having superior that insulating qualities which may be formed in flat sheets or any other desired configuration. The material in its basic form is produced by mixing an alkali metal halide or nitrate into an alkali metal silicate solution to form a polymerized silicate gel. The gel may be heated to cause intumescence and the formation of a dry cellular ceramic, or may be used in gel form, e.g., as a fireproof barrier which will expand upon exposure to heat. Physical properties of the end product are altered by the inclusion of one or more additives prior to the polymerization reaction. These additives may be any of a number of materials that do not significantly react with the alkali metal silicate solution or otherwise inhibit the formation of the gel.
Inventors
- 👤 David J. Legare
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:16
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/006; C04B28/008; C04B35/00; C04B35/01; C04B35/16; C04B2111/00; C04B2111/20; C04B2111/28; Y; Y02; Y02P; Y02P40/00; Y02P40/10
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
91 words
A method of forming a silicate gel which exhibits intumescence upon application of heat said method comprising adding about 0.5 to 12 parts by weight of at least one alkali metal chloride, bromide, iodide or nitrate to 10 parts of an approximately 10 to 40% (by weight) aqueous solution of sodium or potassium silicate, wherein the soluble SiO 2 to alkali metal oxide ratio is between about 2:1 and 5:1 producing a gel by a polymerization reaction being characterized by the essential absence of precipitation of insoluble silicate from said solution.
Claim 2
Independent Claim
91 words
A method of forming a silicate gel which exhibits intumescence upon application of heat said method comprising adding about 0.5 to 12 parts by weight of at least one alkali metal chloride, bromide, iodide or nitrate to 10 parts of an approximately 10 to 40% (by weight) aqueous solution of sodium or potassium silicate, wherein the soluble SiO 2 to alkali metal oxide ratio is between about 2:1 and 5:1 producing a gel by a polymerization reaction being characterized by the essential absence of precipitation of insoluble silicate from said solution.
Claim 3
Dependent Claim
65 words
The method according to claim 1 and including the further step of mixing into said solution at least one insoluble silicate, carbonate or oxide which does not react with the soluble silicate or otherwise inhibit the gelling process, wherein the weight ratio of said insoluble material, including any colloidal SiO 2 initially present in said solution, to said solution is between about 0.05 and 1.
Claim 4
Dependent Claim
30 words
The method according to claim 1 wherein said alkali metal chloride, bromide or iodide or nitrate is at least one of sodium chloride, sodium nitrate, potassium chloride and potassium nitrate.
Claim 5
Dependent Claim
52 words
The method according to claim 1 and including the further step of incorporating into said gel at least one inert particulate material, organic or inorganic fiber in a quantity between about 0.5 parts by weight and the maximum amount of said particulate material or fiber which can be dispersed in the gel.
Claim 6
Independent Claim
32 words
The method of claims 1, 2 or 4 and including the further step of heating said gel at a temperature of at least about 1000° F. until intumescence thereof is substantially complete.
Claim 7
Dependent Claim
52 words
The method of claim 5 wherein said heating step is carried out by first heating said gel in a microwave oven to at least initiate intumescence of said gel, and then heating said gel with a thermal heat source at a temperature of at least 1000° F. until intumescence is essentially complete.
Claim 8
Independent Claim
22 words
The method according to claims 1, 2 or 4 and including the further step of pressing said gel into essentially flat sheets.
Claim 9
Dependent Claim
30 words
The method according to claim 7 and including the further step of heating said sheets at a temperature of at least about 1000° F. until intumescence thereof is substantially complete.
Claim 10
Dependent Claim
28 words
The method according to claim 1 and including the further step of molding said gel to a desired shape and incorporating therein at least one diverse reinforcing member.
Claim 11
Dependent Claim
47 words
The method according to claim 1 and including the further steps of heating said gel at about 1000° F. for a time sufficient to at least initiate intumescence and thereafter heating at least one surface of said gel to its melting temperature, thereby providing a glazed surface.
References Cited (Backward Citations)
US2806801A
Cited
GB1227482A
Cited
FR2053841A5
Cited
US4056937A
Cited
US4118325A
Cited
JPS53104626A
Cited
SU833664A1
Cited
US4378249A
Cited
US4466831A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-10-02 | 1993-04-03 | 1993-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-10-02 | 1997-04-03 | 1997-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-10-02 | 2001-04-03 | 2001-10-03 | $7700.00 | Window Closed / Lapsed |