Doped titanate glass-ceramic for grain boundary barrier layer capacitors
Assignee: International Business Machines Corp
•
Filing: 1989-01-17
•
Granted: 1989-09-26
•
Expires: 2009-01-17
Abstract
Abstract A high dielectric constant glass-ceramic material comprising small conducting grains based on BaTiO 3 and/or SrTiO 3 on the order of about 0.5-10.0 μm surrounded by a thin microcrystalline insulating barrier layer at the grain boundary about 0.01-0.10 μm thick wherein the conductivity of the grains is enhanced by addition of about 0.1-4.0 mol % of a dopant selected from among Group V elements, Ge and Si substantially incorporated in the bulk lattice of the grains upon Ti sites. A novel process for forming the glass-ceramic material is also disclosed.
Inventors
- 👤 Dudley A. Chance
- 👤 Yung-Haw Hu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 02:05
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/47; C04B35/468; C04B35/4682; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1272; H01G4/1281; H01G4/129; Y; Y10; Y10T; Y10T29/00; Y10T29/43; Y10T29/435
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
78 words
A high dielectric constant glass-ceramic material comprising small conducting grains based on BaTiO 3 and/or SrTiO 3 on the order of about 0.5-10.0 μm surrounded by a thin microcrystalline insulating barrier layer at the grain boundary about 0.01-0.10 μm thick wherein the conductivity of the grains is enhanced by addition of about 0.1-4.0 mol% of a dopant selected from among Group V elements, Ge and Si substantially incorporated in the bulk lattice of the grains upon Ti sites.
Claim 2
Dependent Claim
78 words
A high dielectric constant glass-ceramic material comprising small conducting grains based on BaTiO 3 and/or SrTiO 3 on the order of about 0.5-10.0 μm surrounded by a thin microcrystalline insulating barrier layer at the grain boundary about 0.01-0.10 μm thick wherein the conductivity of the grains is enhanced by addition of about 0.1-4.0 mol% of a dopant selected from among Group V elements, Ge and Si substantially incorporated in the bulk lattice of the grains upon Ti sites.
Claim 3
Dependent Claim
21 words
The glass-ceramic material of claim 1, wherein said microcrystalline insulating barrier layer is uniformly distributed and titanate crystals are essentially absent.
Claim 4
Dependent Claim
14 words
The glass-ceramic material of claim 1, wherein said dopant is Nb, Ta or V.
Claim 5
Dependent Claim
11 words
The glass-ceramic material of claim 3, wherein said dopant is Nb.
Claim 6
Dependent Claim
18 words
The glass-ceramic material of claim 1, wherein said microcrystalline insulating barrier layer is β-eucryptite or barium aluminum silicate.
Claim 7
Dependent Claim
14 words
The glass-ceramic material of claim 1, wherein said conducting grains comprise barium titanate crystals.
Claim 8
Dependent Claim
41 words
The glass-ceramic material of claim 1, wherein said conducting grains comprise barium titanate crystals of about 1μm, said barrier layer comprises β-eucryptite of about 0.10 μm thickness and said dopant is Nb added in an amount of about 0.4 mol %.
Claim 9
Dependent Claim
56 words
In a module for supporting electronic circuit chips in a circuit including a planar ceramic substrate and a capacitive element contained within said substrate comprising thin conductive sheets and a thin layer of dielectric material therebetween, the improvement which comprises, said thin layers of dielectric material comprising the high dielectric constant glass-ceramic material of claim 1.
Claim 10
Dependent Claim
29 words
The module for supporting electronic circuit chips of claim 8, wherein said high dielectric constant glass-ceramic material of claim 1 is co-sintered with the thin layers of dielectric material.
Claim 11
Dependent Claim
13 words
The module of claim 8, wherein said capacitive element is on said module.
Claim 12
Dependent Claim
13 words
The module of claim 8, wherein said capacitive element is within said module.
Claim 13
Dependent Claim
23 words
A stack of capacitive elements composed of thin conductive sheets laminated with thin layers of the high dielectric glass-ceramic material of claim 1.
Claim 14
Dependent Claim
15 words
A high capacitance low frequency discrete capacitor formed of the glass-ceramic material of claim 1.
Claim 15
Dependent Claim
13 words
A high frequency module capacitor formed of the glass-ceramic material of claim 1.
Claim 16
Independent Claim
224 words
A method for producing a high dielectric constant glass-ceramic material comprising: (a) admixing about 40-65 total wt % BaO and/or SrO, about 20-35 wt % TiO 2 , about 0.1-4.0 wt % of a dopant selected from among Group V elements, Ge and Si, about 10-15 wt % SiO 2 , about 6-12 wt % Al 2 O 3 , about 0-2 wt % MgO, and about 0-3 wt % Li 2 O, by a powder mixing process to obtain a homogeneous powder mixture; (b) melting the powder mixture in a crucible or like vessel at a temperature of about 1500° to 1600° C. for about 1 to 4 hours to form a melt; (c) quenching the melt by pouring it on a quench plate or into water to form glass cullets; (d) crushing the glass cullets to obtain a powder mixture sufficiently fine to pass through a 325 mesh screen; (e) admixing the powder mixture for about 10 to 30 hours to obtain a dry glass powder mixture of average particle size of about 2 to 7 μm; (f) pressing the dry glass powder in a die at a pressure of about 5,000-15,000 lbs. to obtain a green compact; (g) firing the green compact to sintering temperatures sufficient to accomplish sintering or coalescence of glass particles and conversion to a glass-ceramic by crystallization.
Claim 17
Independent Claim
224 words
A method for producing a high dielectric constant glass-ceramic material comprising: (a) admixing about 40-65 total wt % BaO and/or SrO, about 20-35 wt % TiO 2 , about 0.1-4.0 wt % of a dopant selected from among Group V elements, Ge and Si, about 10-15 wt % SiO 2 , about 6-12 wt % Al 2 O 3 , about 0-2 wt % MgO, and about 0-3 wt % Li 2 O, by a powder mixing process to obtain a homogeneous powder mixture; (b) melting the powder mixture in a crucible or like vessel at a temperature of about 1500° to 1600° C. for about 1 to 4 hours to form a melt; (c) quenching the melt by pouring it on a quench plate or into water to form glass cullets; (d) crushing the glass cullets to obtain a powder mixture sufficiently fine to pass through a 325 mesh screen; (e) admixing the powder mixture for about 10 to 30 hours to obtain a dry glass powder mixture of average particle size of about 2 to 7 μm; (f) pressing the dry glass powder in a die at a pressure of about 5,000-15,000 lbs. to obtain a green compact; (g) firing the green compact to sintering temperatures sufficient to accomplish sintering or coalescence of glass particles and conversion to a glass-ceramic by crystallization.
Claim 18
Dependent Claim
60 words
The method of claim 15, wherein said admixing step (a) uses 40-65 wt % BaO, 20-35 wt % TiO 2 , 0.1-4.0 wt % Nb 2 O 5 as the dopant, 10-15 wt % SiO 2 , 6-12 wt % Al 2 O 3 , up to 2 wt % MgO, and up to 3 wt % Li 2 O.
Claim 19
Dependent Claim
24 words
The method of claim 15, wherein said Li 2 O is replaced with an equivalent amount of Na 2 O or K 2 O.
Claim 20
Dependent Claim
21 words
The method of claim 15, wherein said admixing steps (a) and (e) are performed by a ball mill powder mixing process.
Claim 21
Dependent Claim
30 words
The method of claim 15, wherein said crucible is a platinum or platinum alloy crucible, said quench plate is an aluminum plate, and said die is a stainless steel die.
Claim 22
Dependent Claim
19 words
The method of claim 15, wherein said pressing step (f) is a multilayer substrate fabrication process forming green sheets.
Claim 23
Dependent Claim
63 words
The method of claim 20, wherein said multilayer substrate fabrication process comprises grinding said dry glass powder mixture with a suitable organic binder and solvent to form a castable slurry wherein the average particle size is about 2 to 7 μm, casting said slurry into green sheets, and laminating said green sheets together in a laminating press to form a monolithic green substrate.
Claim 24
Dependent Claim
41 words
The method of claim 15 wherein said firing step (g) comprises an oxidation heating step, a first crystallization heating step in a reducing atmosphere, a second crystallization heating step in a reducing atmosphere, and a cooling step in an oxidizing atmosphere.
Claim 25
Dependent Claim
133 words
The method according to claim 22, wherein said oxidation heating step comprises heating the green compact at a rate of about 3°-5° C./min. in an oxidizing atmosphere to a temperature sufficient to burn off carbonaceous material, and holding at said temperature for about 1-2 hours; said first crystallization heating step comprises heating said green compact at a rate of about 3°-5° C./min. to the first crystallization temperature of the glass, and holding at that temperature for about 3-5 hours; said second crystallization heating step comprises heating the green compact at a rate of about 3°-5° C./min. to the second crystallization temperature of the glass, and holding at that temperature for about 1-2 hours; and said cooling step comprises cooling the resulting glass-ceramic material to room temperature at a rate of about 4°-6° C./min.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-25 | 1993-03-27 | 1993-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-25 | 1997-03-27 | 1997-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-25 | 2001-03-27 | 2001-09-26 | $7700.00 | Window Closed / Lapsed |