Laser beam welding
Assignee: Newcastle University
•
Filing: 1987-02-17
•
Granted: 1989-09-12
•
Expires: 2007-02-17
Abstract
Abstract A 3-25 mm metal plate 22, 27, usually ferrous, is welded by a heavy-duty laser (5-25 kw) which melts through the plate and into a support member 24, 31 below to give a unitary weld. A gas supply to the laser beam focus is provided such that on the one hand the plasma is retained at least partially near the weld pool to give good energy transfer and on the other the plasma does not all escape.
Inventors
- 👤 David R. Martyr
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:22
CPC Classifications
B; B23; B23K; B23K26/00; B23K26/20; B23K26/21; B23K26/12; B23K26/123; B23K26/14; B23K26/1462; B23K26/1464; B23K26/147; B23K26/18; B23K26/24; B23K26/244
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
205 words
A method for welding ferrous metal plate of at least 1 mm thickness to an underlying ferrous attachment member, there being gaps between the plate and the underlying member at some places but not others, comprising the steps of: focussing a laser beam upon the plate at the other side of the plate from the said attachment member so as to melt both the metal of the plate and that of the attachment member underlying the plate; feeding to the focussed beam an elongate body of filler material whereby said material is also melted; directing a supply of gas to at least partially confine the plasma formed; moving the beam along the plate, over the position of the attachment member at a rate such that molten material solidifies as a weld line in the path of travel behind the beam; and causing during such travel molten material to flow from the molten weld into any gaps from time to time encountered to either side of the weld line and between said plate and said attachment member, said step of causing material to flow into any gaps comprising feeding the filler material at such a rate as to provide molten material sufficient to fill the gaps.
Claim 2
Independent Claim
205 words
A method for welding ferrous metal plate of at least 1 mm thickness to an underlying ferrous attachment member, there being gaps between the plate and the underlying member at some places but not others, comprising the steps of: focussing a laser beam upon the plate at the other side of the plate from the said attachment member so as to melt both the metal of the plate and that of the attachment member underlying the plate; feeding to the focussed beam an elongate body of filler material whereby said material is also melted; directing a supply of gas to at least partially confine the plasma formed; moving the beam along the plate, over the position of the attachment member at a rate such that molten material solidifies as a weld line in the path of travel behind the beam; and causing during such travel molten material to flow from the molten weld into any gaps from time to time encountered to either side of the weld line and between said plate and said attachment member, said step of causing material to flow into any gaps comprising feeding the filler material at such a rate as to provide molten material sufficient to fill the gaps.
Claim 3
Dependent Claim
48 words
A method as claimed in claim 1 in which the underlying attachment member is a plate arranged at right angles to the upper metal plate so as to define the stem of a T-shaped configuration, and the weld passes into the end face of the underlying attachment member.
Claim 4
Dependent Claim
59 words
A method as claimed in claim 1 in which the underlying attachment member is a plate arranged at right angles to the upper metal plate so as to define the stem of a T-shaped configuration, and three welds are used, one passing centrally into the end face and the others, located to either side of the central weld passing.
Claim 5
Dependent Claim
27 words
A method as claimed in claim 1 in which the plate is welded in at least one pass to a lip formed on the underlying attachment member.
Claim 6
Dependent Claim
19 words
A method as claimed in claim 1 in which two overlapping plates are welded in at least one pass.
Claim 7
Dependent Claim
21 words
A method as claimed in claim 1 in which the laser beam has an intensity of from 5 to 25 kW.
Claim 8
Dependent Claim
21 words
A method as in claim 1 in which the ferrous metal plate has a thickness of between 5 to 25 mm.
References Cited (Backward Citations)
US4377735A
Cited
US4424435A
Cited
US4546230A
Cited
US4507540A
Cited
US4634832A
Cited
US4603089A
Cited
US4642446A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-11 | 1993-03-13 | 1993-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-11 | 1997-03-13 | 1997-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-11 | 2001-03-13 | 2001-09-12 | $7700.00 | Window Closed / Lapsed |