Patent US4865706A successfully refreshed from Google Patents.
US4865706A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High performance microcapillary gel electrophoresis
Assignee: Northeastern University
•
Filing: 1986-10-21
•
Granted: 1989-09-12
•
Expires: 2006-10-21
Abstract
Abstract A microcapillary column for high performance electrophoresis includes a fused silica microcapillary, a gel of crosslinked polyacrylamide polymerized in the tube, and a thin layer of connecting material covalently bonded to the inner surface of the microcapillary wall and to the polymeric gel. The gel-containing microcapillary is prepared by first covalently bonding a suitable bifunctional reagent to the inner surface of the microcapillary wall, and then causing a mixture of monomer, crosslinking agent, and polymerization catalyst to react in the bore of the microcapillary to form a polymeric matrix which is covalently bonded to the microcapillary wall via the bifunctional reagent. In electrophoresis, the gel-containing microcapillary provides peak efficiencies in excess of 100,000 theoretical plates within separation times of less than thirty minutes, and permits trace level determinations of molecular weights.
Inventors
- 👤 Barry L. Karger
- 👤 Aharon Cohen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:09
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/416; G01N27/447; G01N27/44704; G01N27/44717; G01N27/44721; G01N27/44747; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49826; Y10T29/49885
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
129 words
A method for preparing a gel-containing microcapillary column for high performance high precision electrophoresis, comprising: flushing a silica-based microcapillary with ammonia gas; treating said microcapillary with a solution of bifunctional reagent, said reagent possessing a reactive silane functional group capable of reacting with silanol groups, and a vinyl functionality capable of polymerizing with monomers, to cause covalent bonding of said reagent to the inner surface of the wall of said microcapillary via said reactive silane; and treating said microcapillary with a solution containing at least one monomer, at least one crosslinking agent, and at least one free radical source, to cause polymerization, with formation of a crosslinked polymeric gel in the cavity of said microcapillary and covalent binding of said gel to said bifunctional reagent via said vinyl functionality.
Claim 2
Independent Claim
129 words
A method for preparing a gel-containing microcapillary column for high performance high precision electrophoresis, comprising: flushing a silica-based microcapillary with ammonia gas; treating said microcapillary with a solution of bifunctional reagent, said reagent possessing a reactive silane functional group capable of reacting with silanol groups, and a vinyl functionality capable of polymerizing with monomers, to cause covalent bonding of said reagent to the inner surface of the wall of said microcapillary via said reactive silane; and treating said microcapillary with a solution containing at least one monomer, at least one crosslinking agent, and at least one free radical source, to cause polymerization, with formation of a crosslinked polymeric gel in the cavity of said microcapillary and covalent binding of said gel to said bifunctional reagent via said vinyl functionality.
Claim 3
Dependent Claim
31 words
The method of claim 1 further comprising the step of heating said microcapillary for several hours at a temperature in excess of 100° C. prior to flushing it with ammonia gas.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said step of flushing with ammonia gas is conducted for at least two hours.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said step of flushing with ammonia gas is conducted at a temperature of approximately 30° C.
Claim 6
Dependent Claim
21 words
The method of claim 1 wherein said step of treating with bifunctional reagent solution is conducted for at least two hours.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein said step of treating with bifunctional reagent solution is conducted at a temperature of approximately 30° C.
Claim 8
Dependent Claim
23 words
The method of claim 1 further comprising the step of removing unreacted bifunctional reagent after the step of treating with bifunctional reagent solution.
Claim 9
Dependent Claim
18 words
The method of claim 7 wherein said removing step is conducted by flushing successively with methanol and water.
Claim 10
Dependent Claim
39 words
The method of claim 1 wherein in said step of treating with a solution of monomer, crosslinking agent, and free radical source, said solution is made up in the buffer to be employed in the electrophoresis, and is degassed.
Claim 11
Dependent Claim
38 words
The method of claim 1 further comprising the step of conducting said polymerization of said monomer, crosslinking agent, and free radical source in said microcapillary at the temperature to be employed for electrophoresis on the resulting gel-containing microcapillary.
Claim 12
Dependent Claim
25 words
The method of claim 10 wherein in said conducting step both ends of said microcapillary are submerged in said buffer solution during the polymerization reaction.
Claim 13
Dependent Claim
79 words
The method of claim 1 wherein in said step of treating with a solution of monomer, crosslinking agent, and free radical source, the concentrations of monomer and crosslinking agent are predetermined and the concentration of free radical source is determined experimentally by varying the concentration of such free radical source in trial solutions and monitoring the polymerization reaction until a concentration of such free radical source is found which causes nearly complete polymerization to occur in approximately 45-60 minutes.
Claim 14
Dependent Claim
30 words
The method of claim 1 further comprising the final step of sheathing an end of said microcapillary with TEFLON tubing and cutting it off cleanly and squarely with a microtome.
Claim 15
Independent Claim
223 words
A method for preparing a gel-containing microcapillary column for high performance high precision electrophoresis, comprising: heating a silica-based microcapillary for several hours at a temperature in excess of 100° C.; flushing said microcapillary with dry ammonia gas; treating said microcapillary with a solution of bifunctional reagent, said reagent possessing a reactive silane functional group capable of reacting with silanol groups, and a vinyl group capable of polymerizing with monomers; maintaining said solution of bifunctional reagent in said microcapillary for a predetermined time, said treating and maintaining steps causing covalent bonding of said reagent to the inner surface of the wall of said microcapillary via said reactive silane; removing unreacted bifunctional reagent; filling said microcapillary with a degassed polymerization reagent mixture containing at least one monomer, at least one crosslinking agent, and at least one free radical source at predetermined concentrations, said degassed polymerization reagent mixture being prepared in the buffer to be employed for the electrophoresis; allowing said polymerization reagent mixture to polymerize in said microcapillary while controlling the reaction temperature to that temperature which is to be employed for electrophoresis on the resulting gel-containing microcapillary, to cause formation of a crosslinked polymeric gel in the cavity of said microcapillary and covalent bonding of said gel to said bifunctional reagent; and cutting off at least one end of said microcapillary cleanly and squarely.
Claim 16
Independent Claim
223 words
A method for preparing a gel-containing microcapillary column for high performance high precision electrophoresis, comprising: heating a silica-based microcapillary for several hours at a temperature in excess of 100° C.; flushing said microcapillary with dry ammonia gas; treating said microcapillary with a solution of bifunctional reagent, said reagent possessing a reactive silane functional group capable of reacting with silanol groups, and a vinyl group capable of polymerizing with monomers; maintaining said solution of bifunctional reagent in said microcapillary for a predetermined time, said treating and maintaining steps causing covalent bonding of said reagent to the inner surface of the wall of said microcapillary via said reactive silane; removing unreacted bifunctional reagent; filling said microcapillary with a degassed polymerization reagent mixture containing at least one monomer, at least one crosslinking agent, and at least one free radical source at predetermined concentrations, said degassed polymerization reagent mixture being prepared in the buffer to be employed for the electrophoresis; allowing said polymerization reagent mixture to polymerize in said microcapillary while controlling the reaction temperature to that temperature which is to be employed for electrophoresis on the resulting gel-containing microcapillary, to cause formation of a crosslinked polymeric gel in the cavity of said microcapillary and covalent bonding of said gel to said bifunctional reagent; and cutting off at least one end of said microcapillary cleanly and squarely.
Claim 17
Dependent Claim
20 words
The method of claim 14 wherein said heating step is conducted at a temperature between 110° C. and 200° C.
Claim 18
Dependent Claim
20 words
The method of claim 14 wherein said step of flushing with ammonia gas is conducted for at least two hours.
Claim 19
Dependent Claim
22 words
The method of claim 14 wherein said step of flushing with ammonia gas is conducted at a temperature of approximately 30° C.
Claim 20
Dependent Claim
23 words
The method of claim 14 wherein said bifunctional reagent is selected from the group consisting of 3-Methacryloxypropyltrimethyoxysilane, 3-Methacryloxypropyldimethylethoxysilane, vinyltriacetoxysilane, vinyltri(β-methoxyethoxy)silane, vinyltrichlorosilane, and methylvinyldichlorosilane.
Claim 21
Dependent Claim
13 words
The method of claim 18 wherein said bifunctional reagent is 3-Methacryloxypropyltrimethyoxysilane or 3-Methacryloxypropyldimethylethoxysilane.
Claim 22
Dependent Claim
31 words
The method of claim 14 wherein said step of treating with a solution of bifunctional reagent is conducted by passing at least 100 microcapillary volumes of said solution through said microcapillary.
Claim 23
Dependent Claim
18 words
The method of claim 14 wherein said treating step is conducted at a temperature of approximately 30° C.
Claim 24
Dependent Claim
21 words
The method of claim 14 wherein said solution of bifunctional reagent contains between 4% and 50% by volume of said reagent.
Claim 25
Dependent Claim
18 words
The method of claim 14 wherein in said maintaining step the predetermined time is at least two hours.
Claim 26
Dependent Claim
21 words
The method of claim 14 wherein said removing step is conducted by flushing said microcapillary with a solvent, then with water.
Claim 27
Dependent Claim
10 words
The method of claim 40 wherein said solvent is methanol.
Claim 28
Dependent Claim
67 words
The method of claim 14 wherein in said polymerization reagent mixture the concentrations of monomer and crosslinking agent are predetermined and the concentration of free radical source is determined experimentally by varying the concentrations of such free radical source in trial solutions and monitoring the polymerization reaction until a concentration of free radical source is found which causes nearly complete polymerization to occur in approximately 45-60 minutes.
Claim 29
Dependent Claim
29 words
The method of claim 14 wherein said allowing step both ends of said microcapillary are submerged in the buffer to be employed for the electrphoresis during the polymerization reaction.
Claim 30
Dependent Claim
28 words
The method of claim 14 wherein said cutting step is conducted by sheathing and end of said microcapillary with TEFLON tubing, and cutting it off with a microtome.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-11 | 1993-03-13 | 1993-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-11 | 1997-03-13 | 1997-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-11 | 2001-03-13 | 2001-09-12 | $7700.00 | Window Closed / Lapsed |