Patent US4863796A successfully refreshed from Google Patents.
US4863796A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Paper coated with synthetic alkali metal alumino-silicates
Assignee: JM Huber Corp
•
Filing: 1989-01-19
•
Granted: 1989-09-05
•
Expires: 2009-01-19
Abstract
Abstract A family of synthetic alkali metal aluminosilicates (SAMS) are produced by the hydrothermal reaction between kaolin clay and alkali metal silicates. The integrated composition of the SAMS products is a unique entity having an overall composition of xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2.zH.sub.2 O where x is the number of moles of alkali metal oxide and is an integer from 0.01 to 2.0, M is an alkali metal, y is the number of moles of SiO 2 in the unique SAMS compsoition, and z is the number of moles of bound water and is an integer ranging from 1.0 to 5.0. The composition essentially comprises altered kaolin clay platelets with an integral rim or protuberance of essentially amorphous alkali metal silicate-kaolin reaction product. The unique SAMS compositions are structured materials in which the structure can be controlled, and are therefore useful as functional fillers, as TiO 2 extenders, as silica extenders or as reinforcing agents for paper, paint, rubber, plastics and specialty products.
Inventors
- 👤 Satish K. Wason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 09:30
CPC Classifications
C; C09; C09C; C09C1/00; C09C1/40; C09C1/405; D; D21; D21H; D21H19/00; D21H19/36; D21H19/38; D21H19/40; C01; C01P; C01P2002/00; C01P2002/02; C01P2002/70; C01P2002/72; C01P2002/74; C01P2002/80; C01P2002/82; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/04; C01P2004/20; C01P2004/50; C01P2004/51; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/80; C01P2004/82; C01P2006/00; C01P2006/12; C01P2006/14; C01P2006/19; C01P2006/21; C01P2006/60; C01P2006/80; C01P2006/82; C01P2006/90; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24893; Y10T428/24901; Y10T428/24909; Y10T428/24926; Y10T428/24934; Y10T428/25; Y10T428/256; Y10T428/258; Y10T428/259; Y10T428/31504; Y10T428/31971; Y10T428/31993
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
121 words
A paper containing a paper coating comprising an alkali metal alumino-silicate having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O wherein x is the number of moles of alkali metal oxide and is an integer of 0.01 to 2.0, M is an alkali metal, y is the number of moles of SiO 2 associated with the compositions and is an integer of 2.0 to 20.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0, wherein primary particles of said alkali metal alumino-silicate comprise a core of clay platelets having an integral adjacent area of essentially amorphous alkali metal silicate base-kaolin clay reaction product.
Claim 2
Dependent Claim
121 words
A paper containing a paper coating comprising an alkali metal alumino-silicate having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O wherein x is the number of moles of alkali metal oxide and is an integer of 0.01 to 2.0, M is an alkali metal, y is the number of moles of SiO 2 associated with the compositions and is an integer of 2.0 to 20.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0, wherein primary particles of said alkali metal alumino-silicate comprise a core of clay platelets having an integral adjacent area of essentially amorphous alkali metal silicate base-kaolin clay reaction product.
Claim 3
Dependent Claim
26 words
A paper composition according to claim 1 wherein the alkali metal aluminosilicate has the morphology of the integral rimmed particles as depicted in TEM FIGS. 18-23.
Claim 4
Dependent Claim
166 words
A paper containing a coating which comprises an alkali metal alumino-silicate comprising a core of kaolin clay platelets which have been altered at their edges by reaction so as to be integral with one or more adjacent areas of essentially amorphous alkali metal silicate-base kaolin clay reaction product having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where M is sodium or potassium, x is the number of moles of sodium oxide or potassium oxide and is an integer of 0.01 to 2.0, y is the number of moles of SiO 2 in the composition and is an integer greater than 2.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0; wherein the primary particles of said alkali metal alumino-silicate have attenuated kaolin peaks as compared to kaolin in x-ray diffraction patterns from the kaolin remnants in the compositions, and have the IR scan shown in FIGS. 3-6.
Claim 5
Dependent Claim
166 words
A paper containing a coating which comprises an alkali metal alumino-silicate comprising a core of kaolin clay platelets which have been altered at their edges by reaction so as to be integral with one or more adjacent areas of essentially amorphous alkali metal silicate-base kaolin clay reaction product having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where M is sodium or potassium, x is the number of moles of sodium oxide or potassium oxide and is an integer of 0.01 to 2.0, y is the number of moles of SiO 2 in the composition and is an integer greater than 2.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0; wherein the primary particles of said alkali metal alumino-silicate have attenuated kaolin peaks as compared to kaolin in x-ray diffraction patterns from the kaolin remnants in the compositions, and have the IR scan shown in FIGS. 3-6.
Claim 6
Dependent Claim
24 words
A paper according to claim 3 wherein the alkali metal silicate is sodium silicate, and the silicate product has a rimmed structure comprising silica.
Claim 7
Dependent Claim
26 words
A paper according to claim 3 wherein the alkali metal silicate is potassium silicate and the silicate product has a rimmed structure comprising silica and potassium.
Claim 8
Dependent Claim
26 words
A paper according to claim 3 wherein the alkali metal silicate is lithium silicate and the silicate product comprises a platelet area with amorphous protuberances thereon.
Claim 9
Dependent Claim
20 words
A paper according to claim 3 wherein the silicate composition also contains at least a trace of a zeolite composition.
Claim 10
Dependent Claim
37 words
A paper according to claim 3 wherein the silicate composition has an oil absorption value having a range between about 40 to 220 ml/100 g, and a surface area of about 2 to 300 m 2 /g.
Claim 11
Dependent Claim
34 words
A paper according to claim 3 wherein the silicate compositions have an oil absorption range of between 80 to 160 ml/100 g and a surface area range between 10 to 30 m 2 /g.
References Cited (Backward Citations)
US4775560A
Cited
US4758461A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-09-04 | 1993-03-06 | 1993-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-09-04 | 1997-03-06 | 1997-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-09-04 | 2001-03-06 | 2001-09-05 | $7700.00 | Window Closed / Lapsed |