Method for the manufacture of an anisotropic magnet material on the basis of Fe, B and a rare-earth metal
Assignee: Siemens AG
•
Filing: 1988-03-18
•
Granted: 1989-08-08
•
Expires: 2008-03-18
Abstract
Abstract An anisotropic magnetic material formed from iron, boron and a rare-earth metal is prepared by the rapid solidification of an alloy melt of the desired composition and subsequently treated to generate magnetic anisotropy. The materials attain comparatively higher coercivity field strengths. A preliminary alloy is first prepared with the material components and cobalt is added to the alloy in such an amount that the crystallization temperature of the corresponding amorphous material system is below the Curie temperature of the crystallizing SE 2 (Fe, Co) 14 B- phase. An intermediate product with amorphous structure is then developed from the melt of the preliminary alloy using a rapid solidification technique. Thereafter, a crystallization of the intermediate product is performed using a heat treatment at a temperature that is above the crystallization temperature but below the Curie Temperature in the presence of an external d-c magnetic field to generate the magnetic anisotropy. The particles involved can be aligned and mechanically fixed after the crystallization.
Inventors
- 👤 Joachim Wecker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 15:36
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055; H01F1/057; H01F1/0571; H01F1/0575; H01F1/0576
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
182 words
A method for manufacturing anisotropic magnetic material of a material system, comprising the steps of: preparing an alloy melt from at least three material compounds comprising iron (Fe), boron (B) and a rareearth metal (RE), said alloy melt containing a further material component consisting of cobalt (Co); forming an intermediate product having an amorphous structure by means of rapid solidification of said alloy melt, said cobalt of said amorphous material system being in such an amount that said corresponding amorphous material has a crystallization temperature below the Curie temperature of a crystallizing RE 2 (Fe, Co) 14 of said material system; developing said RE 2 (Fe, Co) 14 B phase of said material system in the presence of an external d-c magnetic field to form a magnetocrystalline anisotropy by means of heat treating said intermediate product at a heat treatment temperature above said crystallization temperature and below said Curie temperature, whereby said intermediate product is crystallized, said heat treating temperature being below a predetermined transition temperature at which the uniaxial preference direction of the magnetocrystalline anisotropy changes into a planar reference plane.
Claim 2
Independent Claim
182 words
A method for manufacturing anisotropic magnetic material of a material system, comprising the steps of: preparing an alloy melt from at least three material compounds comprising iron (Fe), boron (B) and a rareearth metal (RE), said alloy melt containing a further material component consisting of cobalt (Co); forming an intermediate product having an amorphous structure by means of rapid solidification of said alloy melt, said cobalt of said amorphous material system being in such an amount that said corresponding amorphous material has a crystallization temperature below the Curie temperature of a crystallizing RE 2 (Fe, Co) 14 of said material system; developing said RE 2 (Fe, Co) 14 B phase of said material system in the presence of an external d-c magnetic field to form a magnetocrystalline anisotropy by means of heat treating said intermediate product at a heat treatment temperature above said crystallization temperature and below said Curie temperature, whereby said intermediate product is crystallized, said heat treating temperature being below a predetermined transition temperature at which the uniaxial preference direction of the magnetocrystalline anisotropy changes into a planar reference plane.
Claim 3
Dependent Claim
23 words
A method as claimed in claim 1, wherein said rare-earth metal is selected from the group consisting of neodymium (Nd) and praseodymium (Pr).
Claim 4
Dependent Claim
19 words
A method as claimed in claim 1, wherein the ratio of Co to Fe is between 0.1 and 0.6.
Claim 5
Dependent Claim
19 words
A method as claimed in claim 3, wherein the ratio of Co to Fe is between 0.15 and 0.5.
Claim 6
Dependent Claim
22 words
A method as claimed in claim 1, wherein a further rare-earth metal partially substitutes for the rare-earth metal in said preliminary alloy.
Claim 7
Dependent Claim
14 words
A method as claimed in claim 5, wherein said further rare-earth metal is dysprosium.
Claim 8
Dependent Claim
21 words
A method as claimed in claim 1, wherein another metal at least partially substitutes for the Fe in said preliminary alloy.
Claim 9
Dependent Claim
14 words
A method as claimed in claim 7, wherein said another metal is aluminum (Al).
Claim 10
Dependent Claim
31 words
A method as claimed in claim 1, wherein said material system comprises RE x (Fe, Co) y B z , where 10 =x =30, 60 =y =85 and 3 =z =20.
Claim 11
Dependent Claim
26 words
A method as claimed in claim 9, wherein said material system has an overall composition of 11 =x =20; 65 =y =80 and 5 =z =20.
Claim 12
Dependent Claim
28 words
A method as claimed in claim 10, wherein said amorphous intermediate product has a form selected from the group consisting of tape, thin layers, or a metal powder.
Claim 13
Dependent Claim
19 words
A method as claimed in claim 11, further comprising the step of comminuting said intermediate product to form particles.
Claim 14
Dependent Claim
21 words
A method as claimed in claim 1, wherein said external magnetic field has a field strength between 0.5 and 100 kOe.
Claim 15
Dependent Claim
31 words
A method as claimed in claim 1, further comprising the steps of: aligning particles of the crystallized intermediate product after said crystallization; and mechanically fixing said particles to form a structure.
Claim 16
Dependent Claim
25 words
A method as claimed in claim 14, wherein said step of aligning said particles includes the step of applying an external d-c magnetic alignment field.
Claim 17
Dependent Claim
21 words
A method as claimed in claim 15, wherein said magnetic alignment field has a field strength of at least 1 kOe.
Claim 18
Dependent Claim
16 words
A method as claimed in claim 16, wherein said field strength is at least 5 kOe.
Claim 19
Dependent Claim
28 words
A method as claimed in claim 14, wherein the step of mechanically fixing said particles includes the step of mechanically fixing said particles with a hardenable synthetic material.
Claim 20
Dependent Claim
22 words
A method as claimed in claim 18, wherein said step of mechanically fixing said particles include the step of pressing said particles.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-08-07 | 1993-02-06 | 1993-08-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-08-07 | 1997-02-06 | 1997-08-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-08-07 | 2001-02-06 | 2001-08-08 | $7700.00 | Window Closed / Lapsed |