Chaff comprising metal coated fibers
Assignee: COMPOSITE MATERIAL LLC
•
Filing: 1984-07-13
•
Granted: 1989-08-01
•
Expires: 2004-07-13
Abstract
Abstract High strength composite fibers are disclosed comprising a core, e.g., of carbon or the like, and a thin and uniform, firmly adherent electrically conductive layer of an electrodepositable metal, e.g., of nickel or the like. The composite fiber can be produced by electrodeposition from an electrolyte onto the core but the procedure must use external voltages high enough both (i) dissociate the metal at the core and (ii) to mucleate the metal through the boundary layer into direct contact with the core. Such composite fibers are chopped to shortened lengths to provide chaff, which is effective as a radar countermeasure.
Inventors
- 👤 Louis G. Morin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:21
CPC Classifications
F; F41; F41J; F41J2/00; D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/127; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
60 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff comprising continuous composite fibers, each comprising a semi-metallic core and at least one thin and uniform, firmly adherent, electrically conductive layer of at least one metal on said core, said composite fibers having been chopped into one or more lengths.
Claim 2
Independent Claim
60 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff comprising continuous composite fibers, each comprising a semi-metallic core and at least one thin and uniform, firmly adherent, electrically conductive layer of at least one metal on said core, said composite fibers having been chopped into one or more lengths.
Claim 3
Dependent Claim
28 words
A method of reflecting radar according to claim 1, wherein said composite fibers have been chopped into wavelengths relative to the wavelength of one or more radar frequencies.
Claim 4
Independent Claim
64 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff comprising continuous composite fibers, each comprising an electrically conductive semi-metallic substantially undegraded core and at least one thin and uniform, firmly adherent, electrically conductive layer of at least one metal one said core, said composite fibers having been chopped into one or more lengths.
Claim 5
Independent Claim
64 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff comprising continuous composite fibers, each comprising an electrically conductive semi-metallic substantially undegraded core and at least one thin and uniform, firmly adherent, electrically conductive layer of at least one metal one said core, said composite fibers having been chopped into one or more lengths.
Claim 6
Dependent Claim
28 words
A method of reflecting radar according to claim 3, wherein said composite fibers have been chopped into wavelengths relative to the wavelength of one or more radar frequencies.
Claim 7
Independent Claim
127 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff prepared by a process comprising: (a) providing a plurality of semi-metallic core fibers, (b) continuously immersing at least a portion of the length of said biers in bath capable of electrolytically depositing at least one metal, (c) applying an external voltage between the fibers and the bath in excess of 10 volts, (d) maintaining said voltage and resulting current for a time sufficient to produce a thin and uniform, firmly adherent, electrically conductive layer of electrolytically deposited metal on said core, (e) maintaining said fibers cool enough outside said bath to prevent degradation of said fibers, and (f) chopping the resultant metal coated fibers into shortened stands.
Claim 8
Independent Claim
127 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff prepared by a process comprising: (a) providing a plurality of semi-metallic core fibers, (b) continuously immersing at least a portion of the length of said biers in bath capable of electrolytically depositing at least one metal, (c) applying an external voltage between the fibers and the bath in excess of 10 volts, (d) maintaining said voltage and resulting current for a time sufficient to produce a thin and uniform, firmly adherent, electrically conductive layer of electrolytically deposited metal on said core, (e) maintaining said fibers cool enough outside said bath to prevent degradation of said fibers, and (f) chopping the resultant metal coated fibers into shortened stands.
Claim 9
Independent Claim
168 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff prepared by a process comprising: (a) providing a plurality of semi-metallic core fibers, (b) continuously immersing at least a portion of the length of said fibers in bath capable of electrolytically depositing at least one metal, (c) applying an external voltage between the fibers and the bath in excess of 10 volts. (d) maintaining said voltage and resulting current for a time sufficient to produce a thin and uniform, firmly adherent, electrically conductive layer of electrolytically deposited metal on said core, (e) maintaining said fibers cool enough outside said bath to prevent degradation of said fibers, and (f) chopping the resultant metal coated fibers into shortened stands, and wherein said process includes recycling the bath into contact with the fibers immediately prior to immersion therein so as to provide increased current carrying capacity to the fibers and replenishment of the electrolyte on the surface of the fibers therein.
Claim 10
Independent Claim
168 words
A method of reflecting radar comprising dispersing in effective proximity to a radar source an effective amount of a chaff prepared by a process comprising: (a) providing a plurality of semi-metallic core fibers, (b) continuously immersing at least a portion of the length of said fibers in bath capable of electrolytically depositing at least one metal, (c) applying an external voltage between the fibers and the bath in excess of 10 volts. (d) maintaining said voltage and resulting current for a time sufficient to produce a thin and uniform, firmly adherent, electrically conductive layer of electrolytically deposited metal on said core, (e) maintaining said fibers cool enough outside said bath to prevent degradation of said fibers, and (f) chopping the resultant metal coated fibers into shortened stands, and wherein said process includes recycling the bath into contact with the fibers immediately prior to immersion therein so as to provide increased current carrying capacity to the fibers and replenishment of the electrolyte on the surface of the fibers therein.
Claim 11
Dependent Claim
19 words
A method as defined in claim 1 wherein said core fibers comprise carbon fibers and said metal comprises nickel.
Claim 12
Dependent Claim
19 words
A method as defined in claim 3 wherein said core fibers comprise carbon fibers and said metal comprises nickel.
Claim 13
Dependent Claim
19 words
A method as defined in claim 5 wherein said core fibers comprise carbon fibers and said metal comprises nickel.
Claim 14
Dependent Claim
19 words
A method as defined in claim 6 wherein said core fibers comprise carbon fibers and said metal comprises nickel.
References Cited (Backward Citations)
US3622283A
Cited
GB1325794A
Cited
US3896010A
Cited
US4014757A
Cited
US4132828A
Cited
GB2112214A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-31 | 1993-01-30 | 1993-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-31 | 1997-01-30 | 1997-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-31 | 2001-01-30 | 2001-08-01 | $7700.00 | Window Closed / Lapsed |