Crack prevention of implanted prostheses
Assignee: Lifeshield Sciences LLC
•
Filing: 1988-06-15
•
Granted: 1989-07-25
•
Expires: 2008-06-15
Abstract
Abstract Implantable devices having a biocompatible polymeric surface which is elastomeric and susceptible to cracking under in vivo conditions are provided which have been subjected to treatment with a crack preventative composition that includes an elastomeric silicone such as poly(dimethyl siloxane). This treatment substantially prevents cracking of the implantable device after it is implanted.
Inventors
- 👤 Leonard Pinchuk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 05:45
CPC Classifications
A; A61; A61L; A61L27/00; A61L27/50; A61L27/28; A61L27/34; Y; Y10; Y10S; Y10S623/00; Y10S623/92
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
190 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said biocompatible polymeric surface is a polyurethane; applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR5## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including efecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 2
Independent Claim
190 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said biocompatible polymeric surface is a polyurethane; applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR5## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including efecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 3
Dependent Claim
58 words
The method according to claim 1, wherein said silicone rubber material of the crack preventative composition is a siloxane condensation reaction product of reactants including: (a) a silicone moiety of the formula: ##STR6## wherein n has an average value of greater than 100; and (b) an acetoxy silane crosslinker, ##STR7## whereby the reaction product is a poly(dimethyl siloxane).
Claim 4
Dependent Claim
24 words
The treatment method according to claim 1, wherein said crack preventative composition includes a solvent that does not detreimentally affect said biocompatible polymeric surface.
Claim 5
Dependent Claim
20 words
The treatment method according to claim 1, wherein said applying step includes imparting lubricating properties to the biocompatible polymeric surface.
Claim 6
Dependent Claim
127 words
The method according to claim 1, wherein said silicone rubber material of the crack preventative composition is a siloxane which, prior to curing, has the formula: ##STR8## wherein each R group is an organic moiety selected from the group consisting of one or more ester moieties, acetoxy moieties, acrylic moieties and alcohol moieties, wherein each R 3 and R 4 group is an organic group selected from the group consisting of aliphatic groups and substituted aliphatic groups having from 1 to about 12 carbon atoms, and aromatic groups and substituted aromatic groups having from 6 to about 20 carbon atoms, and wherein each R 1 group and R 2 group is an organic component selected from the group consisting of R, R 3 and R 4 .
Claim 7
Dependent Claim
18 words
The method according to claim 1, wherein said silicone material of the crack preventative composition is poly(dimethyl siloxane).
Claim 8
Independent Claim
200 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said shaped substrate includes one or more extruded fibers that are shaped by winding over a mandrel; applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR9## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including effecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 9
Independent Claim
200 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said shaped substrate includes one or more extruded fibers that are shaped by winding over a mandrel; applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR9## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including effecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 10
Independent Claim
195 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said shaped substrate includes one or more strands of said biocompatible polymer; applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR10## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including effecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 11
Independent Claim
195 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said shaped substrate includes one or more strands of said biocompatible polymer; applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR10## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including effecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 12
Dependent Claim
117 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR11## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said elastomeric biocompatible polymeric surface is a polyurethane.
Claim 13
Dependent Claim
117 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR11## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said elastomeric biocompatible polymeric surface is a polyurethane.
Claim 14
Dependent Claim
122 words
The implantable device according to claim 9, wherein said crack preventative is a siloxane which, prior to curing, has the formula: ##STR12## wherein each R group is an organic moiety selected from the group consisting of one or more ester moieties, acetoxy moieties, acrylic moieties and alcohol moieties, wherein each R 3 and R 4 group is an organic group selected from the group consisting of aliphatic groups and substituted aliphatic groups having from 1 to about 12 carbon atoms, and aromatic groups and substituted aromatic groups having from 6 to about 20 carbon atoms, and wherein each R 1 group and R 2 group is an organic component selected from the group consisting of R, R 3 and R 4 .
Claim 15
Dependent Claim
19 words
The implantable device according to claim 9, wherein said silicone material of the crack preventative composition is poly(dimethyl siloxane).
Claim 16
Dependent Claim
33 words
The implantable device according to claim 9, wherein said shaped substrate is a pacemaker lead insulator having a generally smooth surface of said elastomeric biocompatible polymeric material having said crack preventative bonded thereto.
Claim 17
Dependent Claim
122 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods, wherein said shaped substrate includes one or more strands of said biocompatible polymer; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR13## groups; and said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative.
Claim 18
Dependent Claim
122 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods, wherein said shaped substrate includes one or more strands of said biocompatible polymer; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR13## groups; and said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative.
Claim 19
Dependent Claim
127 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods, wherein said shaped substrate includes one or more extruded fibers that are shaped by winding over a mandrel; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR14## groups; and said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative.
Claim 20
Dependent Claim
127 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods, wherein said shaped substrate includes one or more extruded fibers that are shaped by winding over a mandrel; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR14## groups; and said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative.
Claim 21
Dependent Claim
143 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR15## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said shaped substrate is a graft including wound strands of extruded fiber that overlie and intersect one another, and said extruded fiber is said elastomeric biocompatible polymeric surface having said crack preventative bonded thereto.
Claim 22
Dependent Claim
143 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR15## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said shaped substrate is a graft including wound strands of extruded fiber that overlie and intersect one another, and said extruded fiber is said elastomeric biocompatible polymeric surface having said crack preventative bonded thereto.
Claim 23
Dependent Claim
134 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR16## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said shaped substrate is a suture including an extruded fiber that is composed of said elastomeric biocompatible polymeric surface having said crack preventative bonded thereto.
Claim 24
Dependent Claim
134 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR16## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said shaped substrate is a suture including an extruded fiber that is composed of said elastomeric biocompatible polymeric surface having said crack preventative bonded thereto.
Claim 25
Dependent Claim
128 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR17## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said elastomeric biocompatible polymeric surface is a polyurethane, and said crack preventative bonded thereto is acetoxy terminated poly(dimethyl siloxane).
Claim 26
Dependent Claim
128 words
An implantable device for medical use under in vivo conditions, comprising: a shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to degradation cracking when subjected to implantation under in vivo conditions for substantial time periods; a crack preventative adsorbed to and grafted onto said substrate so that there is bonding between said elastomeric substrate and said crack preventative, said crack preventative being an elastomeric silicone material having a predetermined surface tension, said crack preventative being a siloxane including recurring ##STR17## groups; said biocompatible polymeric surface has a surface tension greater than the predetermined surface tension of the crack preventative; and said elastomeric biocompatible polymeric surface is a polyurethane, and said crack preventative bonded thereto is acetoxy terminated poly(dimethyl siloxane).
Claim 27
Independent Claim
203 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said elastomeric biocompatible polymeric surface is a polyurethane, and wherein said crack preventative bonded thereto is acetoxy terminated poly(dimethyl siloxane); applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR18## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including effecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
Claim 28
Independent Claim
203 words
A method for forming an implantable device for medical use, which device is treated to substantially prevent in vivo cracking thereof, the method comprising: providing a non-woven shaped substrate of an implantable medical device having a biocompatible polymeric surface that is elastomeric and susceptible to cracking when subjected to implantation under in vivo conditions for substantial time periods, said in vivo conditions including those that promote crack-forming degradation of said biocompatible polymeric surface, wherein said elastomeric biocompatible polymeric surface is a polyurethane, and wherein said crack preventative bonded thereto is acetoxy terminated poly(dimethyl siloxane); applying a crack preventative composition to said elastomeric biocompatible polymeric surface, said crack preventative composition including a silicone material being a siloxane including ##STR18## groups and, when polymerized, being elastomeric and having a predetermined surface tension, said applying step including effecting adsorption of the silicone material onto the biocompatible polymeric surface and bonding between said elastomeric silicone material and said elastomeric biocompatible polymeric surface so as to effect grafting of said polymerized elastomeric silicone material onto said elastomeric biocompatible polymeric surface; and said providing step includes selecting said elastomeric biocompatible polymeric surface to have a surface tension that is greater than the predetermined surface tension of said silicone material.
References Cited (Backward Citations)
US2609320A
Cited
US3187752A
Cited
US3434869A
Cited
US3527556A
Cited
US3629358A
Cited
US3729007A
Cited
US3683424A
Cited
US3708324A
Cited
SU562278A1
Cited
US4156067A
Cited
GB2140437A
Cited
US4475972A
Cited
US4608428A
Cited
US4687482A
Cited
US4595610A
Cited
JPH02183757A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-24 | 1993-01-23 | 1993-07-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-24 | 1997-01-23 | 1997-07-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-24 | 2001-01-23 | 2001-07-25 | $7700.00 | Window Closed / Lapsed |