Growth of semi-insulating indium phosphide by liquid phase epitaxy
Assignee: Nortel Networks Ltd
•
Filing: 1988-06-02
•
Granted: 1989-07-18
•
Expires: 2008-06-02
Abstract
Abstract In a method for Liquid Phase Epitaxy (LPE) of semi-insulating InP, a solution of P, Ti and a p-type dopant in molten In is cooled in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on the surface. The concentration of p-type dopant in the solution is such as to provide a concentration of p-type dopant in the grown epitaxial layer greater than the aggregate concentration of any residual contaminants in the grown epitaxial layer, and the concentration of Ti in the solution is such as to provide a concentration of Ti in the grown epitaxial layer greater than the concentration of p-type dopant in the grown epitaxial layer. The required melt concentrations are determined empirically. The method can be performed at temperature below 650 degrees Celsius and is particularly suited to the LPE growth of semi-insulating InP to isolate InP-InGaAsP buried heterostructure lasers.
Inventors
- 👤 D. Gordon Knight
- 👤 William Benyon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 21:25
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/29; H10P14/2901; H10P14/2907; H10P14/2909; H10P14/26; H10P14/263; H10P14/265; H10P14/27; H10P14/271; H10P14/32; H10P14/3202; H10P14/3214; H10P14/3218; H10P14/34; H10P14/3402; H10P14/3414; H10P14/3418; H10P14/3438; H10P14/3441; H10P14/3444; H10P14/3446; Y; Y10; Y10S; Y10S148/00; Y10S148/023; Y10S148/066; Y10S148/095; Y10S148/101
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
116 words
A method for Liquid Phase Epitaxy (LPE) of semi-insulating InP, comprising cooling a solution of P, Ti and a p-type dopant in molten In in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on said surface, the concentration of p-type dopant in said solution being such as to provide a concentration of p-type dopant in the grown epitaxial layer greater than the aggregate concentration of any residual contaminants in the grown epitaxial layer, and the concentration of Ti in said solution being such as to provide a concentration of Ti in the grown epitaxial layer greater than the concentration of p-type dopant in the grown epitaxial layer.
Claim 2
Independent Claim
116 words
A method for Liquid Phase Epitaxy (LPE) of semi-insulating InP, comprising cooling a solution of P, Ti and a p-type dopant in molten In in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on said surface, the concentration of p-type dopant in said solution being such as to provide a concentration of p-type dopant in the grown epitaxial layer greater than the aggregate concentration of any residual contaminants in the grown epitaxial layer, and the concentration of Ti in said solution being such as to provide a concentration of Ti in the grown epitaxial layer greater than the concentration of p-type dopant in the grown epitaxial layer.
Claim 3
Dependent Claim
24 words
A method as defined in claim 1, wherein the p-type dopant is selected from the group consisting of Zn, Cd, Hg, Be and Mg.
Claim 4
Independent Claim
111 words
A method for Liquid Phase Epitaxy (LPE) of semi-insulating InP, comprising cooling a solution of P, Ti and Zn in molten In in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on said surface, the concentration of Zn in said solution being such as to provide a concentration of Zn in the grown epitaxial layer greater than the aggregate concentration of any residual contaminants in the grown epitaxial layer, and the concentration of Ti in said solution being such as to provide a concentration of Ti in the grown epitaxial layer greater than the concentration of Zn in the grown epitaxial layer.
Claim 5
Independent Claim
111 words
A method for Liquid Phase Epitaxy (LPE) of semi-insulating InP, comprising cooling a solution of P, Ti and Zn in molten In in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on said surface, the concentration of Zn in said solution being such as to provide a concentration of Zn in the grown epitaxial layer greater than the aggregate concentration of any residual contaminants in the grown epitaxial layer, and the concentration of Ti in said solution being such as to provide a concentration of Ti in the grown epitaxial layer greater than the concentration of Zn in the grown epitaxial layer.
Claim 6
Dependent Claim
24 words
A method as defined in claim 3, comprising providing the solution by melting In, Zn doped InP and deoxidized Ti in a non-oxidizing ambient.
Claim 7
Dependent Claim
21 words
A method as defined in claim 4, further comprising melting undoped InP with the In, Zn doped InP and deoxidized Ti.
Claim 8
Dependent Claim
38 words
A method as defined in claim 4, further comprising baking the molten In in a non-oxidizing ambient to drive impurities from the molten In and resolidifying the In before melting it with the Zn-doped InP and deoxidized Ti.
Claim 9
Dependent Claim
20 words
A method as defined in claim 4, comprising etching the In to remove surface contaminants immediately before melting the In.
Claim 10
Dependent Claim
23 words
A method as defined in claim 4, comprising etching the Zn-doped InP to remove surface contaminants immediately before melting it with the In.
Claim 11
Dependent Claim
23 words
A method as defined in claim 5, comprising etching the undoped InP immediately before melting it with the Zn-doped InP, Ti and In.
Claim 12
Dependent Claim
115 words
A method as defined in claim 3, comprising providing the solution by: melting In, deoxidized Ti and undoped InP in a graphite vessel in a non-oxidizing ambient to form a first melt; baking the first melt in a non-oxidizing ambient to drive Ti into walls of the graphite vessel; removing the first melt from the graphite vessel; melting In in the graphite vessel in a nonoxidizing ambient to form a second melt, baking the second melt in a non-oxidizing ambient to draw Ti from the walls of the graphite vessel into the second melt and resolidifying the second melt; and melting undoped InP and Zn-doped InP with the resolidified second melt in a non-oxidizing ambient.
Claim 13
Dependent Claim
55 words
A method as defined in claim 10, comprising baking the first melt at 660 degrees Celsius for 5 hours to drive Ti into the walls of the graphite vessel and baking the second melt at 700 degrees Celsius for 20 hours to draw Ti from the walls of the qraphite vessel into the resulting melt.
Claim 14
Dependent Claim
34 words
A method as defined in claim 11, comprising providing 7.2×10 -4 moles of deoxidized Ti and 6.54×10 -3 moles of P in the first melt for each mole of In in the first melt.
Claim 15
Dependent Claim
49 words
A method as defined in claim 10, comprising forming the first melt by: melting In in a non-oxidizing ambient; baking the molten In in a non-oxidizing ambient to drive impurities from the molten In; resolidifying the molten In; and melting the resolidified In with deoxidized Ti and undoped InP.
Claim 16
Dependent Claim
22 words
A method as defined in claim 13, comprising etching the In to remove surface contaminants immediately before melting and baking the In.
Claim 17
Dependent Claim
23 words
A method as defined in claim 10, comprising etching the undoped InP and Zn-doped InP to remove surface contaminants immediately before melting them.
Claim 18
Independent Claim
80 words
A method for Liquid Phase Epitaxy (LPE) of semiinsulating InP, comprising cooling a solution of P, Ti and Zn in molten In in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on said surface, the concentration of Zn in said solution being at least 4×10 -7 moles per mole of In, and the concentration of Ti in said solution being at least 200 times the concentration of Zn in said solution.
Claim 19
Independent Claim
80 words
A method for Liquid Phase Epitaxy (LPE) of semiinsulating InP, comprising cooling a solution of P, Ti and Zn in molten In in a non-oxidizing ambient at a surface of a substrate to grow an epitaxial layer of doped InP on said surface, the concentration of Zn in said solution being at least 4×10 -7 moles per mole of In, and the concentration of Ti in said solution being at least 200 times the concentration of Zn in said solution.
Claim 20
Dependent Claim
87 words
A method as defined in claim 16, wherein the concentration of Zn in said solution is 6×10 -7 moles of Zn per mole of In, the concentration of Ti in said solution is 1.2×10 -4 moles of Ti per mole of In, and the concentration of P in said solution is 6.54×10 -3 moles of P per mole of In. 1.2×10 -4 moles of Ti per mole of In, and the concentration of P in said solution is 6.54×10 -3 moles of P per mole of In.
Claim 21
Independent Claim
77 words
A method of making a buried heterostructure semiconductor laser, comprising: growing an InP-InGaAsP heterostructure on an InP substrate; removing regions of the heterostructure to define a mesa; growing a layer of semi-insulating InP adjacent the mesa by a LPE method comprising cooling a solution of p-type dopant in molten In in a non-oxidizing ambient, to electrically isolated the mesa; forming electrical contacts to the mesa and to the substrate; and forming reflective end facets on the mesa.
Claim 22
Independent Claim
77 words
A method of making a buried heterostructure semiconductor laser, comprising: growing an InP-InGaAsP heterostructure on an InP substrate; removing regions of the heterostructure to define a mesa; growing a layer of semi-insulating InP adjacent the mesa by a LPE method comprising cooling a solution of p-type dopant in molten In in a non-oxidizing ambient, to electrically isolated the mesa; forming electrical contacts to the mesa and to the substrate; and forming reflective end facets on the mesa.
Claim 23
Dependent Claim
27 words
A method as defined in claim 17, comprising growing a layer of Ti-Zn codoped semi-insulating InP adjacent the mesa by LPE at temperatures below 650 degrees Celsius.
References Cited (Backward Citations)
FR2598862A1
Cited
US4774554A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-17 | 1993-01-16 | 1993-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-17 | 1997-01-16 | 1997-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-17 | 2001-01-16 | 2001-07-18 | $7700.00 | Window Closed / Lapsed |