Composite polymer-glass edge cladding for laser disks
Assignee: United States Department of Energy
•
Filing: 1987-11-02
•
Granted: 1989-07-18
•
Expires: 2007-11-02
Abstract
Abstract Large neodymium glass laser disks for disk amplifiers such as those used in the Nova laser require an edge cladding which absorbs at 1 micrometer. This cladding prevents edge reflections from causing parasitic oscillations which would otherwise deplete the gain. Nova now utilizes volume-absorbing monolithic-glass claddings which are fused at high temperature to the disks. These perform quite well but are expensive to produce. Absorbing glass strips are adhesively bonded to the edges of polygonal disks using a bonding agent whose index of refraction matches that of both the laser and absorbing glass. Optical finishing occurs after the strips are attached. Laser disks constructed with such claddings have shown identical gain performance to the previous Nova disks and have been tested for hundreds of shots without significant degradation.
Inventors
- 👤 Howard T. Powell
- 👤 Michael O. Riley
- 👤 Charles R. Wolfe
- 👤 Richard E. Lyon
- 👤 John H. Campbell
- 👤 Edward S. Jessop
- 👤 James E. Murray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:55
CPC Classifications
H; H01; H01S; H01S3/00; H01S3/05; H01S3/06; H01S3/0602; H01S3/0604; C; C03; C03C; C03C4/00; C03C4/0071; H01S2301/00; H01S2301/02; H01S3/0612; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24777; Y10T428/24793; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31518
Claims Analysis
Total Claims: 48
Claim 1
Independent Claim
148 words
A method for suppressing parasitic oscillations in a solid state laser component by producing an article having an integral solid state laser gain media which has bonded to its peripheral edge using a bonding agent a laser light absorbing material, the method comprising; (a) placing a thin layer of bonding agent selected from the group consisting of inorganic adhesives, cements, organic adhesives, organic polymers and polymerizable monomers, the bonding agent having a refractive index closely matching the solid state laser gain media and the laser light absorbing material, covering the entire outer surface of the peripheral edge of the solid state laser gain media, (b) using the bonding agent to bond a laser light absorbing material layer in close proximity and covering the entire outer surface of the peripheral edge of the solid state laser gain media, with the proviso that the bonding agent is not silicone rubber.
Claim 2
Independent Claim
148 words
A method for suppressing parasitic oscillations in a solid state laser component by producing an article having an integral solid state laser gain media which has bonded to its peripheral edge using a bonding agent a laser light absorbing material, the method comprising; (a) placing a thin layer of bonding agent selected from the group consisting of inorganic adhesives, cements, organic adhesives, organic polymers and polymerizable monomers, the bonding agent having a refractive index closely matching the solid state laser gain media and the laser light absorbing material, covering the entire outer surface of the peripheral edge of the solid state laser gain media, (b) using the bonding agent to bond a laser light absorbing material layer in close proximity and covering the entire outer surface of the peripheral edge of the solid state laser gain media, with the proviso that the bonding agent is not silicone rubber.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein the bonding agent or precursors to the bonding agent react to produce the bonding agent without the simultaneous production of volatile chemicals.
Claim 4
Dependent Claim
45 words
The method of claim 2 wherein the refractive index of the reacted bonding agent has a refractive index range of between about 1.3 and 1.7 at the laser wavelength in the visible or near IR regions of the spectrum between about 0.4 and 1.5 micrometers.
Claim 5
Dependent Claim
46 words
The method of claim 2 wherein the refractive index match required depends upon the size and gain coefficient of the laser material, for large components the refractive index match is between about + or -0.003 of the refractive index of the solid state laser gain media.
Claim 6
Dependent Claim
31 words
The method of claim 1 where the thermal coefficient of expansion of the solid state of laser gain media and the laser light absorbing material match between about + or -5%.
Claim 7
Dependent Claim
44 words
The method of claim 1 wherein the laser light absorbing material has the minimum required absorption coefficient at the laser light wavelength to minimize thermal stress on the junction formed by the solid state laser gain media, bonding agent and laser light absorbing material.
Claim 8
Dependent Claim
34 words
The method of claim 2 wherein the thickness of the bonding agent after curing between the solid state laser material and the laser light absorbing material is between about 1 micron and 2 millimeters.
Claim 9
Dependent Claim
18 words
The method of claim 7 therein the thickness of the organic material is between 1 and 50 microns.
Claim 10
Dependent Claim
12 words
The method of claim 8 wherein the thickness is about 25 microns.
Claim 11
Dependent Claim
26 words
The method of claim 1 wherein the solid state laser gain media comprises inorganic glass, ceramics, crystals, phosphate, fluorophosphate, silica glass or laminates of these materials.
Claim 12
Dependent Claim
22 words
The method of claim 10 wherein the solid state laser gain media comprises inorganic glasses selected from silica, phosphate or fluorophosphate glasses.
Claim 13
Dependent Claim
21 words
The method of claim 1 wherein the laser light absorbing material comprises inorganic glasses, crystals, ceramics, or laminates of these materials.
Claim 14
Dependent Claim
21 words
The method of claim 12 wherein the laser light absorbing material comprises inorganic glasses selected from silica, phosphate or fluorophosphate glasses.
Claim 15
Dependent Claim
37 words
The method of claim 10 wherein the solid state laser gain media and the laser light absorbing material each comprise the same materials, having essentially a matching coefficient of thermal expansion and essentially a matching refractive index.
Claim 16
Dependent Claim
33 words
The method of claim 14 wherein the solid state laser gain material is phosphate glass doped with an active ion at a concentration up to about 10 21 ions per cm 3 .
Claim 17
Dependent Claim
27 words
The method of claim 13 wherein the laser light absorbing material is doped with active metal ions, at a concentration of up to 20 percent by weight.
Claim 18
Dependent Claim
28 words
The method of claim 1 wherein the method further includes: Step (c) prior treating the surfaces to be bonded with dilute acid to etch and clean the surface.
Claim 19
Dependent Claim
26 words
The method of claim 17 wherein the method further includes: Step (d) prior treating the surfaces to be bonded with a primer or a coupling agent.
Claim 20
Dependent Claim
11 words
The method of claim 15 wherein the active ion is neodymium.
Claim 21
Dependent Claim
14 words
The method of claim 13 wherein the laser light absorbing material comprises phosphate glass.
Claim 22
Dependent Claim
26 words
The method of claim 16 wherein the laser light absorbing material is doped with metal ions, up to a concentration of about 1 percent by weight.
Claim 23
Dependent Claim
11 words
The method of claim 21 wherein the metal ion is copper.
Claim 24
Dependent Claim
23 words
The method of claim 2 wherein the bonding agent comprises an adhesive selected from epoxy materials, epoxy precursors, urethane acrylics or rigid silicones.
Claim 25
Dependent Claim
16 words
The method of claim 23 wherein the epoxy precursors comprise an epoxide and an organic amine.
Claim 26
Dependent Claim
27 words
The method of claim 24 wherein the organic epoxide comprises an epoxide selected from the diglycidal ether of bis-phenol-A, the diglycidal ether of 1,4-butanediol or mixtures thereof.
Claim 27
Dependent Claim
28 words
The method of claim 25 wherein the diglycidal ether is crosslinked using an amine crosslinking agent selected from a polyether triamine in the presence of an amine accelerator.
Claim 28
Dependent Claim
47 words
The method of claim 1 wherein the face of the article is ground and polished after the peripheral edge bonding to obtain an uncontaminated optical surface with a minimum of thickness of bonding agent between the solid state laser gain media and the laser light absorbing material
Claim 29
Dependent Claim
201 words
The method of claim 27 wherein the article is produced in a two-step manner, itself comprising: (i) bonding discrete pieces of laser light absorbing material using a bonding agent to attach to alternating peripheral edges of the solid state laser gain media wherein open spaces remain on the peripheral edge of the solid state laser gain media, (ii) grinding and polishing the ends of the bonded laser light absorbing material and the intervening peripheral edges of the solid state gain media to produce a continuous, flat and uncontaminated surface, (iii) bonding additional pieces of laser light absorbing material in the remaining open spaces on alternating sides of the peripheral edge of the solid state laser gain media using a bonding agent thereby producing a completely continuous cladding of laser light absorbing material on the peripheral edge of the solid state laser gain media, and (iv) trimming the edge by grinding and polishing the ends of the bonded laser light absorbing material to be flush with the adjoining material, and (v) grinding and polishing the face surface created by the bonding of the solid state laser gain media, bonding agent and laser light absorbing material to produce an optically smooth face surface.
Claim 30
Dependent Claim
33 words
The article having an integral solid state laser gain media which has bonded to its peripheral edge, using a bonding agent, a light absorbing material produced according to the method of claim 1.
Claim 31
Dependent Claim
33 words
The article having an integral solid state laser gain media which has bonded to its peripheral edge, using a bonding agent, a light absorbing material produced according to the method of claim 14.
Claim 32
Dependent Claim
33 words
The article having an integral solid state laser gain media which has bonded to its peripheral edge, using a bonding agent, a light absorbing material produced according to the method of claim 28.
Claim 33
Dependent Claim
41 words
The article of claim 29 wherein the peripheral edge of the solid state laser gain media is cut wherein the peripheral edge has an angle of between about 0.1 and 5 degrees from the perpendicular with respect to the face surface.
Claim 34
Dependent Claim
40 words
The article according to claim 29 wherein the bonding by the bonding agent between the solid state laser gain media and the laser light absorption material is stable in operation without voids or delaminations for more than 2000 operating cycles.
Claim 35
Independent Claim
95 words
A method for suppressing parasitic oscillations in solid state laser gain media, the method comprising: (a) dissolving a dye, or dispersing a pigment, or adding a particulate material which absorbs light at a wavelength matching that of the light generated by the laser material in an organic material selected from the group consisting or organic polymers and polymerizable monomers, the proviso that the organic material is not an organic soft silicone rubber, and (b) bonding the organic material mixed with the dye or pigment on the peripheral edges of the solid state laser gain medium.
Claim 36
Independent Claim
95 words
A method for suppressing parasitic oscillations in solid state laser gain media, the method comprising: (a) dissolving a dye, or dispersing a pigment, or adding a particulate material which absorbs light at a wavelength matching that of the light generated by the laser material in an organic material selected from the group consisting or organic polymers and polymerizable monomers, the proviso that the organic material is not an organic soft silicone rubber, and (b) bonding the organic material mixed with the dye or pigment on the peripheral edges of the solid state laser gain medium.
Claim 37
Dependent Claim
24 words
The method of claim 34 in which the aggregate dissolved dyes or dispersed pigments are in concentration up to about 10 percent by weight.
Claim 38
Dependent Claim
17 words
The method of claim 34 wherein the concentration is between about 0.01 and 0.02 percent by weight.
Claim 39
Dependent Claim
33 words
The method of claim 34 wherein the dyes or pigments are selected from: organometallic complexes, 10 micron to 1 millimeter sized glass beads, micron sized pigments, or micron sized broad band wavelength absorbers.
Claim 40
Dependent Claim
52 words
The method of claim 37 in which the dyes or pigments are typically chosen from the group consisting of: (i) bis(4-dimethylaminodithiobenzyl)-nickel, (ii) an antimony containing organic compound of the formula: N 4 C 30 H 42 .SbF 6 , and (iii) sub-micron sized carbon black particles or a similar broadband wavelength absorber.
Claim 41
Dependent Claim
21 words
The method of claim 34 wherein the organic polymer is selected from rigid silicone compounds, epoxies, polyamides, acrylics, polyphosphazenes or urethane-acrylates.
Claim 42
Dependent Claim
73 words
The method of claim 34 wherein: the solid state laser gain media is phosphate glass; the dye or pigment is selected from bis (4-dimethylaminodithiobenzyl) - nickel, an antimony containing organic compound, 10 micron to 1 millimeter sized glass beads containing an absorber, or submicronsized carbon particles, and the organic material is selected from an organic polymer selected from rigid silicone compounds, epoxies, free radical polymerized polyesters, acrylics, polyurethanes, polyphosphazenes, polyurethane-acrylics, poly(styrene) or poly(vinylbutyryl).
Claim 43
Dependent Claim
9 words
The article produced by the method of claim 34.
Claim 44
Dependent Claim
9 words
The article produced by the method of claim 40.
Claim 45
Dependent Claim
36 words
The article produced by the method of claim 34 wherein the peripheral edge of the solid state laser gain media is between about 0.1 and 5 degrees from the perpendicular with respect to the face surfaces.
Claim 46
Dependent Claim
57 words
The method of claim 43 wherein: the solid state laser gain material is phosphate glass doped with neodymium, the organic material is an epoxy-based adhesive, and the dye or pigment is selected from bis (4-dimethylaminodithionyl)-nickel (Kodak Q-Switch), an antimony containing organic compound (Cyasorb IR-99); 10 micron to 1 millimeter sized glass beads, or submicron sized carbon particles.
Claim 47
Independent Claim
345 words
A method for suppressing parasitic oscillations in a solid state laser component by producing an article having an integral solid state laser gain media which has bonded to its peripheral edge using a bonding agent a laser light absorbing material, the method comprising; (a) placing a thin layer of a bonding agent comprising an epoxy based adhesive having a refractive index essentially matching the solid state laser gain media which is comprised of a Pt-incursion free phosphate glass doped with neodymium and also the laser light absorbing material which is comprised of a Pt-incursion free phosphate glass doped with copper covering the entire outer surface of the peripheral edge of the solid sate laser gain media, (b) using the bonding agent to bond a laser light absorbing material layer in close proximity and covering the entire outer surface of the peripheral edge of the solid state laser gain media wherein the article is produced in a two-step manner, itself comprising: (i) bonding discrete pieces of the laser light absorbing material using an epoxy adhesive to attach to alternating peripheral edges of the solid state laser gain media wherein open spaces remain on the peripheral edge of the solid state laser gain media, (ii) grinding and polishing the ends of the bonded laser light absorbing material and the intervening peripheral edges of the solid state gain media to produce a continuous, flat, and uncontaminated surface, (iii) bonding additional pieces of laser light absorbing material in the remaining open spaces on alternating sides of peripheral edge of the solid state laser gain media using a bonding agent thereby producing a completely continuous cladding of laser light absorbing material on the peripheral edge of the solid state laser gain media, and (iv) trimming the edge by grinding and polishing the ends of the bonded laser light absorbing material to be flush with the adjoining material, and (v) grinding and polishing the face surface created by the bonding of the solid state laser gain media, bonding agent and laser light absorbing material to produce an optically smooth face surface.
Claim 48
Independent Claim
345 words
A method for suppressing parasitic oscillations in a solid state laser component by producing an article having an integral solid state laser gain media which has bonded to its peripheral edge using a bonding agent a laser light absorbing material, the method comprising; (a) placing a thin layer of a bonding agent comprising an epoxy based adhesive having a refractive index essentially matching the solid state laser gain media which is comprised of a Pt-incursion free phosphate glass doped with neodymium and also the laser light absorbing material which is comprised of a Pt-incursion free phosphate glass doped with copper covering the entire outer surface of the peripheral edge of the solid sate laser gain media, (b) using the bonding agent to bond a laser light absorbing material layer in close proximity and covering the entire outer surface of the peripheral edge of the solid state laser gain media wherein the article is produced in a two-step manner, itself comprising: (i) bonding discrete pieces of the laser light absorbing material using an epoxy adhesive to attach to alternating peripheral edges of the solid state laser gain media wherein open spaces remain on the peripheral edge of the solid state laser gain media, (ii) grinding and polishing the ends of the bonded laser light absorbing material and the intervening peripheral edges of the solid state gain media to produce a continuous, flat, and uncontaminated surface, (iii) bonding additional pieces of laser light absorbing material in the remaining open spaces on alternating sides of peripheral edge of the solid state laser gain media using a bonding agent thereby producing a completely continuous cladding of laser light absorbing material on the peripheral edge of the solid state laser gain media, and (iv) trimming the edge by grinding and polishing the ends of the bonded laser light absorbing material to be flush with the adjoining material, and (v) grinding and polishing the face surface created by the bonding of the solid state laser gain media, bonding agent and laser light absorbing material to produce an optically smooth face surface.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-17 | 1993-01-16 | 1993-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-17 | 1997-01-16 | 1997-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-17 | 2001-01-16 | 2001-07-18 | $7700.00 | Window Closed / Lapsed |