US4847122A — Cavitation-resistant polymer and coating

Claim 1

Independent Claim 103 words

A cavitation resistant composition comprising from about 24 to 48 wt. % of a liquid epoxy resin, from about 24 to 48 wt. % of a blocked isocyanate prepolymer, from about 4.2 to 12 wt. % of a rheological additive, from about 10 to 14 wt. % of a curing agent for the epoxy resin and the isocyanate, from about 1 to 4 wt. % of a plasticizer, and from about 0.1 to 0.6 wt. % of a surface modifying agent containing silane groups, wherein at least about 65 wt. % of the rheological additive is comprised of an amorphous silica flatting agent.

Claim 2

Dependent Claim 103 words

A cavitation resistant composition comprising from about 24 to 48 wt. % of a liquid epoxy resin, from about 24 to 48 wt. % of a blocked isocyanate prepolymer, from about 4.2 to 12 wt. % of a rheological additive, from about 10 to 14 wt. % of a curing agent for the epoxy resin and the isocyanate, from about 1 to 4 wt. % of a plasticizer, and from about 0.1 to 0.6 wt. % of a surface modifying agent containing silane groups, wherein at least about 65 wt. % of the rheological additive is comprised of an amorphous silica flatting agent.

Claim 3

Dependent Claim 23 words

The composition of claim 1 containing from about 3 to about 12 wt. % amorphous silica flatting agent, based on the composition weight.

Claim 4

Dependent Claim 23 words

The composition of claim 1 containing from about 3 to about 8 wt. % amorphous silica flatting agent, based on the composition weight.

Claim 5

Dependent Claim 72 words

The composition of claim 1 comprising about 36.4 wt. % of the epoxy resin, about 36.4 wt. % of the blocked isocyanate prepolymer, about 6.5 wt. % of the amorphous silica flatting agent and 3.5 wt. % of a rheological additive other than amorphous silica flatting agent, about 12.84 wt. % of the curing agent, about 2.8 wt. % of the plasticizer, and about 0.36 wt. % of the surface modifying agent.

Claim 6

Dependent Claim 19 words

The composition of claim 1 containing a member selected from the group consisting of pigments, fillers, and mixtures thereof.

Claim 7

Dependent Claim 22 words

The composition of claim 5 containing up to about 2 wt. % pigment and up to about 2 wt. % magnesium silicate.

Claim 8

Dependent Claim 18 words

The composition of claim 1 wherein the amorphous silica flatting agent contains 97.5 wt. % SiO 2 (anhydrous).

Claim 9

Dependent Claim 37 words

The composition of claim 7 wherein the amorphous silica flatting agent has an average particle size of about 0.02 microns, a surface area of about 150 square inches/gram, and a bulk density of about 7-10 pounds/cubic foot.

Claim 10

Dependent Claim 109 words

A cavitation resistant coating comprising the reaction product of from about 24 to 48 wt. % of a liquid epoxy resin, from about 24 to 48 wt. % of a blocked isocyanate prepolymer, and from about 10 to 14 wt. % of a curing agent for the epoxy resin and the isocyanate; and from about 4.2 to 12 wt. % of a rheological additive at least 65 wt. % of which is an amorphous silica flatting agent, from about 1 to 4 wt. % of a plasticizer, from about 0.1 to 0.6 wt. % of a surface modifying agent containing silane groups, and auxiliary agents to aid in handling.

Claim 11

Dependent Claim 109 words

A cavitation resistant coating comprising the reaction product of from about 24 to 48 wt. % of a liquid epoxy resin, from about 24 to 48 wt. % of a blocked isocyanate prepolymer, and from about 10 to 14 wt. % of a curing agent for the epoxy resin and the isocyanate; and from about 4.2 to 12 wt. % of a rheological additive at least 65 wt. % of which is an amorphous silica flatting agent, from about 1 to 4 wt. % of a plasticizer, from about 0.1 to 0.6 wt. % of a surface modifying agent containing silane groups, and auxiliary agents to aid in handling.

Claim 12

Dependent Claim 76 words

The coating of claim 9 wherein the epoxy resin is a diglycidyl ether of bisphenol A, the blocked isocyanate is an alkyl phenol blocked toluene diisocyanate, the curing agent is an alkyleneamine having the formula NH 2 CH 2 CH 2 CH 2 O(CH 2 CH 2 O) 2 CH 2 CH 2 CH 2 NH 2 , the plasticizer is dibutyl phthalate, the surface modifying agent is gamma-aminopropyltriethoxysilane, and the auxiliary agent is magnesium silicate.

Claim 13

Dependent Claim 18 words

The coating of claim 9 wherein the amorphous silica flatting agent contains 97.5 wt. % SiO 2 (anhydrous).

Claim 14

Dependent Claim 36 words

The coating of claim 11 wherein the silica flatting agent has an average particle size of about 0.02 microns, a surface area of about 150 square inches/gram, and a bulk density of about 7-10 pounds/cubic foot.

Claim 15

Dependent Claim 109 words

A cavitation resistant polymer comprising the reaction product of from about 24 to 48 wt. % of a liquid epoxy resin, from about 24 to 48 wt. % of a blocked isocyanate prepolymer, and from about 10 to 14 wt. % of a curing agent for the epoxy resin and the isocyanate; and from about 4.2 to 12 wt. % of a rheological additive at least 65 wt. % of which is an amorphous silica flatting agent, from about 1 to 4 wt. % of a plasticizer, from about 0.1 to 0.6 wt. % of a surface modifying agent containing silane groups, and auxiliary agents to aid in handling.

Claim 16

Dependent Claim 109 words

A cavitation resistant polymer comprising the reaction product of from about 24 to 48 wt. % of a liquid epoxy resin, from about 24 to 48 wt. % of a blocked isocyanate prepolymer, and from about 10 to 14 wt. % of a curing agent for the epoxy resin and the isocyanate; and from about 4.2 to 12 wt. % of a rheological additive at least 65 wt. % of which is an amorphous silica flatting agent, from about 1 to 4 wt. % of a plasticizer, from about 0.1 to 0.6 wt. % of a surface modifying agent containing silane groups, and auxiliary agents to aid in handling.

Claim 17

Dependent Claim 76 words

The polymer of claim 13 wherein the epoxy resin is a diglycidyl ether of bisphenol A, the blocked isocyanate is an alkyl phenol blocked toluene diisocyanate, the curing agent is an alkyleneamine having the formula NH 2 CH 2 CH 2 CH 2 O(CH 2 CH 2 O) 2 CH 2 CH 2 CH 2 NH 2 , the plasticizer is dibutyl phthalate, the surface modifying agent is gamma-aminopropyltriethoxysilane, and the auxiliary agent is magnesium silicate.

Claim 18

Dependent Claim 19 words

The polymer of claim 13 wherein the amorphous silica flatting rheological additive contains 97.5 wt. % SiO 2 (anhydrous).

Claim 19

Dependent Claim 37 words

The polymer of claim 15 wherein the amorphous silica flatting agent has an average particle size of about 0.02 microns, a surface area of about 150 square inches/gram, and a bulk density of about 7-10 pounds/cubic foot.

Claim 20

Independent Claim 179 words

A method for producing a cavitation resistant coating which comprises: (a) preparing a first portion by mixing from about 30 to 60 wt. % of a liquid epoxy resin, from about 30 to 60 wt. % of a blocked isocyanate prepolymer, and from about 4 to 10 wt. % of an amorphous silica flatting agent to produce a first portion of said coating; (b) preparing a second portion by mixing from about 50 to 70 wt. % of a curing agent for the epoxy resin and the isocyanate, from about 5 to 20 wt. % of a plasticizer, from about 0.5 to 3 wt. % of a surface modifying agent containing silane groups, and from about 5 to 20 wt. % of a rheological additive to produce a second portion of said coating; (c) mixing four parts by weight of the first portion of said coating with one part by weight of the second portion of said coating to produce a coating composition; (d) applying the composition to a surface; and (e) curing the composition to produce the coating.

Claim 21

Independent Claim 179 words

A method for producing a cavitation resistant coating which comprises: (a) preparing a first portion by mixing from about 30 to 60 wt. % of a liquid epoxy resin, from about 30 to 60 wt. % of a blocked isocyanate prepolymer, and from about 4 to 10 wt. % of an amorphous silica flatting agent to produce a first portion of said coating; (b) preparing a second portion by mixing from about 50 to 70 wt. % of a curing agent for the epoxy resin and the isocyanate, from about 5 to 20 wt. % of a plasticizer, from about 0.5 to 3 wt. % of a surface modifying agent containing silane groups, and from about 5 to 20 wt. % of a rheological additive to produce a second portion of said coating; (c) mixing four parts by weight of the first portion of said coating with one part by weight of the second portion of said coating to produce a coating composition; (d) applying the composition to a surface; and (e) curing the composition to produce the coating.

Claim 22

Dependent Claim 75 words

The method of claim 17 wherein the first portion comprises about 45.50 wt. % of the epoxy resin, about 45.50 wt. % of the blocked isocyanate prepolymer, and about 8.60 wt. % of the amorphous silica flatting agent; the second portion comprises about 64.20 wt. % of the curing agent, about 14.00 wt. % of the plasticizer, about 1.80 wt. % of the surface modifying agent, and about 15.50 wt. % of a rheological additive.

Claim 23

Dependent Claim 23 words

The method of claim 17 wherein the portions contain a member selected from the group consisting of pigments, mineral fillers, and mixtures thereof.

Claim 24

Dependent Claim 13 words

The method of claim 17 wherein the composition is cured at ambient temperature.

Claim 25

Dependent Claim 99 words

The method of claim 17 wherein the epoxy resin is a diglycidyl ether of bisphenol A, the blocked isocyanate is an alkyl phenol blocked toluene diisocyanate, the curing agent is an alkylene amine having the formula NH 2 CH 2 CH 2 CH 2 O(CH 2 CH 2 O) 2 CH 2 CH 2 CH 2 NH 2 , the amorphous silica flatting agent contains about 97.5 wt. % SiO 2 (anhydrous) and has an average particle size of about 0.02, the plasticizer is dibutyl phthalate, the surface modifying agent is gamma-aminopropyltriethoxysilane, and the second portion contains magnesium silicate.

Claim 26

Dependent Claim 19 words

The method of claim 17 wherein the surface to which the composition is applied is coated with a primer.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1992-07-10	1993-01-09	1993-07-11	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1996-07-10	1997-01-09	1997-07-11	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2000-07-10	2001-01-09	2001-07-11	$7700.00	Window Closed / Lapsed

Cavitation-resistant polymer and coating

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)