Process for attaching a porous layer to a substrate and using the process to the making of a prosthesis
Assignee: Commissariat à l'Énergie Atomique et Aux Énergies Alternatives
•
Filing: 1988-01-27
•
Granted: 1989-07-11
•
Expires: 2008-01-27
Abstract
Abstract A process for attaching a porous layer to a substrate adapted to form the core of a hip prosthesis, the substrate is placed in a cavity in a mould. Spherules are introduced into the space between the substrate and the walls of the cavity. The mould is placed in a furnace, which is heated to a temperature at which the material of which the substrate is made is superplastic. Then a pressure of the order of 10 to 30 MPa is applied to the mould, enabling the spherules to be encrusted on the substrate at a relatively low temperature.
Inventors
- 👤 Jacques Devillard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 10:23
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/002; A; A61; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/306; A61F2/3094; A61F2002/30001; A61F2002/30108; A61F2002/30199; A61F2002/30242; A61F2002/30968; A61F2230/00; A61F2230/0063; A61F2230/0071; A61F2310/00; A61F2310/00005; A61F2310/00011; A61F2310/00023; A61F2310/00029; A61F2310/00035; A61F2310/00059; A61F2310/00131; A61F2310/00389; A61F2310/00395; A61F2310/00407; A61F2310/00413
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
73 words
A process for attaching a porous layer to a substrate, the substrate being made of a first material and the porous layer of a second material, characterized in that said process comprises the following stages: (a) putting the substrate in conditions in which the first material is superplastic, and (b) sintering the porous layer on to the substrate so that the layer becomes at least partially encrusted on the surface of the substrate.
Claim 2
Dependent Claim
73 words
A process for attaching a porous layer to a substrate, the substrate being made of a first material and the porous layer of a second material, characterized in that said process comprises the following stages: (a) putting the substrate in conditions in which the first material is superplastic, and (b) sintering the porous layer on to the substrate so that the layer becomes at least partially encrusted on the surface of the substrate.
Claim 3
Dependent Claim
25 words
A process according to claim 1, characterized in that the first material belongs to the group formed by titanium, cobalt, chromium, tantalum and their alloys.
Claim 4
Dependent Claim
25 words
A process according to claim 1, characterized in that the second material belongs to the group formed by titanium, cobalt, chromium, tantalum and their alloys.
Claim 5
Dependent Claim
16 words
A process according to claim 1, characterized in that the porous layer is formed by spherules.
Claim 6
Dependent Claim
20 words
A process according to claim 4, characterized in that the diameter of the spherules is between 100 and 1000 microns.
Claim 7
Dependent Claim
18 words
A process according to claim 5, characterized further that the diameter is preferably between 500 and 600 microns.
Claim 8
Dependent Claim
30 words
A process according to claim 1, characterized in that the first material being titanium, stage (b) is performed at a temperature of between 700 and 950° C., preferably 825° C.
Claim 9
Dependent Claim
26 words
A process according to claim 1, characterized in that the stage (b) is performed at a pressure of between 10 and 30 MPa, preferably 20 MPa.
Claim 10
Dependent Claim
32 words
A process according to claim 1, characterized in that it comprises an extra stage (c), performed before stage (b) and consisting in creating an antidiffusion barrier on the surface of the substrate.
Claim 11
Dependent Claim
25 words
A process according to claim 9, characterized in that the stage (c) is performed by creating an oxide layer on the surface of the substrate.
Claim 12
Dependent Claim
48 words
A process according to claim 1, characterized in that it comprises an extra stage (d), performed before the stage (b) and consisting of sintering the porous layer outside the substrate at an elevated temperature, resulting in the second material diffusion bonding at all points of contact amongst itself.
Claim 13
Dependent Claim
31 words
A process according to claim 11, characterized in that the second material being titanium, the stage (d) is performed at a temperature of between 1000 and 1450° C., preferably 1250° C.
Claim 14
Dependent Claim
47 words
A process according to claim 1, wherein the properties of the second material and first material are selected so they will promote diffusion bonding at all points of contact amongst the second material with itself and the partial embedding of said second material into said first material.
Claim 15
Dependent Claim
57 words
A process according to claim 1, characterized in that the porous layer is formed by a stack of or a multiplicity of layers of the second material, said second material being diffusion bonded together at all points of contact amongst itself, and said porous layer forming a ring which encompasses a preselected surface area of the substrate.
Claim 16
Dependent Claim
79 words
A process for attaching a porous layer to a substrate, the substrate being made of a first material and the porous layer of a second material, characterized in that said process comprises the following stages: (a) putting the substrate in conditions in which the first material is superplastic, and (b) sintering the porous layer onto the substrate so that the layer becomes at least partially encrusted on the surface of the substrate, said porous layer being formed by spherules.
Claim 17
Dependent Claim
79 words
A process for attaching a porous layer to a substrate, the substrate being made of a first material and the porous layer of a second material, characterized in that said process comprises the following stages: (a) putting the substrate in conditions in which the first material is superplastic, and (b) sintering the porous layer onto the substrate so that the layer becomes at least partially encrusted on the surface of the substrate, said porous layer being formed by spherules.
References Cited (Backward Citations)
US4040159A
Cited
US4570271A
Cited
US4483478A
Cited
US4393987A
Cited
US4608052A
Cited
US4660755A
Cited
US4636219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-10 | 1993-01-09 | 1993-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-10 | 1997-01-09 | 1997-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-07-10 | 2001-01-09 | 2001-07-11 | $7700.00 | Window Closed / Lapsed |