US4845133A — Flexible polyurea or polyurea-polyurethane foams …

Claim 1

Independent Claim 120 words

An open-celled flexible polyurea or polyurea-polyurethane foam having a density of 6 pounds per cubic foot or less, which is the reaction product of a reaction mixture comprising (A) a relatively high equivalent weight compound or mixture thereof having an average of about 1.5 to about 4 active hydrogen-containing groups per molecule, of which active hydrogen-containing groups, at least about 30 percent are primary aromatic, Lewis acid-blocked primary aliphatic, secondary aliphatic or aromatic amine groups or a mixture of such groups, (B) a blowing agent, in amount sufficient to provide a cellular structure to the foam, (C) less than about 5 parts by weight of a cross-linker or chain extender per 100 parts of component (A), and (D) a polyisocyanate.

Claim 2

Dependent Claim 120 words

An open-celled flexible polyurea or polyurea-polyurethane foam having a density of 6 pounds per cubic foot or less, which is the reaction product of a reaction mixture comprising (A) a relatively high equivalent weight compound or mixture thereof having an average of about 1.5 to about 4 active hydrogen-containing groups per molecule, of which active hydrogen-containing groups, at least about 30 percent are primary aromatic, Lewis acid-blocked primary aliphatic, secondary aliphatic or aromatic amine groups or a mixture of such groups, (B) a blowing agent, in amount sufficient to provide a cellular structure to the foam, (C) less than about 5 parts by weight of a cross-linker or chain extender per 100 parts of component (A), and (D) a polyisocyanate.

Claim 3

Dependent Claim 17 words

The foam of claim 1 wherein the reaction mixture further comprises an effective amount of a catalyst.

Claim 4

Dependent Claim 25 words

The foam of claim 2 wherein the polyisocyanate is present in an amount sufficient to provide an isocyanate index of about 90 to about 125.

Claim 5

Dependent Claim 30 words

The foam of claim 3 wherein the blowing agent comprises water, which is present in an amount of at least 3.5 parts by weight per 100 parts of Component (A).

Claim 6

Dependent Claim 18 words

The foam of claim 4 wherein Component (A) has an equivalent weight from about 500 to about 2500.

Claim 7

Dependent Claim 10 words

The foam of claim 5 which is a molded foam.

Claim 8

Dependent Claim 15 words

The foam of claim 6 which is prepared in the substantial absence of a surfactant.

Claim 9

Dependent Claim 17 words

The foam of claim 5 wherein the polyisocyanate comprises an isomeric mixture of 2,4- and 2,6-toluene diisocyanate.

Claim 10

Dependent Claim 32 words

The foam of claim 5 wherein the polyisocyanate comprises an isomeric mixture of 2,4'- and 4,4'-diphenylmethanediisocyanate or derivative thereof and component (A) has an average functionality of about 1.9 to about 2.05.

Claim 11

Dependent Claim 17 words

The foam of claim 6 wherein the reaction mixture contains about 5 to about 10 parts water.

Claim 12

Dependent Claim 13 words

The foam of claim 1 wherein Component (A) comprises an aromatic amine-terminated polyether.

Claim 13

Dependent Claim 13 words

The foam of claim 6 wherein Component (A) comprises an aromatic amine-terminated polyether.

Claim 14

Dependent Claim 35 words

The foam of claim 11 wherein the aromatic amine-terminated polyether comprises a reaction product of a polyether polyol and a halogenated nitrobenzene compound in which the nitro groups are subsequently reduced to primary amine groups.

Claim 15

Dependent Claim 35 words

The foam of claim 12 wherein the aromatic amine-terminated polyether comprises a reaction product of a polyether polyol and a halogenated nitrobenzene compound in which the nitro groups are subsequently reduced to primary amine groups.

Claim 16

Dependent Claim 14 words

The foam of claim 1 wherein Component (A) comprises a secondary aliphatic amine-terminated polyether.

Claim 17

Dependent Claim 14 words

The foam of claim 6 wherein Component (A) comprises a secondary aliphatic amine-terminated polyether.

Claim 18

Dependent Claim 26 words

The foam of claim 15 wherein the secondary aliphatic amine-terminated polyether comprises a Michael addition product of a primary amine-terminated polyether and an ethylenically unsaturated compound.

Claim 19

Dependent Claim 26 words

The foam of claim 16 wherein the secondary aliphatic amine-terminated polyether comprises a Michael addition product of a primary amine-terminated polyether and an ethylenically unsaturated compound.

Claim 20

Dependent Claim 25 words

The foam of claim 17 wherein the secondary aliphatic amine-terminated polyether is prepared in a reductive amination of a polyether polyol with a primary amine.

Claim 21

Dependent Claim 25 words

The foam of claim 18 wherein the secondary aliphatic amine-terminated polyether is prepared in a reductive amination of a polyether polyol with a primary amine.

Claim 22

Dependent Claim 11 words

The foam of claim 20 wherein the primary amine is isopropylamine.

Claim 23

Dependent Claim 11 words

The foam of claim 21 wherein the primary amine is isopropylamine.

Claim 24

Dependent Claim 133 words

A process for preparing an open-celled polyurethane foam, comprising reacting a reaction mixture in a one-step process under conditions such that a flexible polyurea or polyurea-polyurethane foam is obtained, wherein the reaction mixture comprises (A) a relatively high equivalent weight compound or mixture thereof having an average of about 1.5 to about 4 active hydrogen-containing groups per molecule, of which active hydrogen-containing groups, at least about 30 percent are primary aromatic, Lewis acid-blocked primary aliphatic, secondary aromatic or aliphatic amine groups or a mixture of such groups, (B) a blowing agent, in amount sufficient to provide the foam with a density of less than 6 pounds per cubic foot, (C) less than about 5 parts by weight of a cross-linker or chain extender per 100 parts of component (A), and (D) a polyisocyanate.

Claim 25

Dependent Claim 133 words

A process for preparing an open-celled polyurethane foam, comprising reacting a reaction mixture in a one-step process under conditions such that a flexible polyurea or polyurea-polyurethane foam is obtained, wherein the reaction mixture comprises (A) a relatively high equivalent weight compound or mixture thereof having an average of about 1.5 to about 4 active hydrogen-containing groups per molecule, of which active hydrogen-containing groups, at least about 30 percent are primary aromatic, Lewis acid-blocked primary aliphatic, secondary aromatic or aliphatic amine groups or a mixture of such groups, (B) a blowing agent, in amount sufficient to provide the foam with a density of less than 6 pounds per cubic foot, (C) less than about 5 parts by weight of a cross-linker or chain extender per 100 parts of component (A), and (D) a polyisocyanate.

Claim 26

Dependent Claim 48 words

The process of claim 23 wherein component (A) has an average equivalent weight from about 500 to about 2500, component (C) comprises an isomeric mixture of toluene diisocyanate, MDI or a derivative of MDI, and the reaction mixture further comprises effective amounts of a catalyst and a surfactant.

Claim 27

Dependent Claim 11 words

The process of claim 24 wherein the blowing agent comprises water.

Claim 28

Dependent Claim 13 words

The process of claim 25 wherein component (A) comprises an aromatic amine-terminated polyether.

Claim 29

Dependent Claim 14 words

The process of claim 25 wherein component (A) comprises a secondary aliphatic amine-terminated polyether.

Claim 30

Dependent Claim 130 words

An improvement in a process for preparing an open-celled flexible polymer foam by reacting components comprising a relatively high equivalent weight compound having a plurality of active hydrogen-containing groups, less than 5 parts by weight of a cross-linker or chain extender per 100 parts of the relatively high equivalent weight compound and a polyisocyanate in the presence of a sufficient amount of a blowing agent to provide the foam with a density of 6 pounds per cubic foot or less, the improvement comprising using as the relatively high equivalent weight compound a relatively high equivalent weight compound having from about 1.5 to about 4 active hydrogen-containing groups per molecule, of which groups at least about 30 percent are primary aromatic, Lewis-acid-blocked primary aliphatic or secondary aliphatic or aromatic amine groups.

Claim 31

Dependent Claim 130 words

An improvement in a process for preparing an open-celled flexible polymer foam by reacting components comprising a relatively high equivalent weight compound having a plurality of active hydrogen-containing groups, less than 5 parts by weight of a cross-linker or chain extender per 100 parts of the relatively high equivalent weight compound and a polyisocyanate in the presence of a sufficient amount of a blowing agent to provide the foam with a density of 6 pounds per cubic foot or less, the improvement comprising using as the relatively high equivalent weight compound a relatively high equivalent weight compound having from about 1.5 to about 4 active hydrogen-containing groups per molecule, of which groups at least about 30 percent are primary aromatic, Lewis-acid-blocked primary aliphatic or secondary aliphatic or aromatic amine groups.

Claim 32

Dependent Claim 11 words

The process of claim 28 wherein the blowing agent comprises water.

Claim 33

Dependent Claim 14 words

The process of claim 29 wherein component (A) comprises a secondary aliphatic amine-terminated polyether.

Claim 34

Dependent Claim 13 words

The process of claim 29 wherein component (A) comprises an aromatic amine-terminated polyether.

Claim 35

Dependent Claim 131 words

An open-celled polyurea or polyurea-polyurethane foam having a density of 6 pounds per cubic foot or less prepared by reacting a reaction mixture comprising (A) a polyether having an equivalent weight from about 500 to about 2500, an average functionality from about 1.8 to about 3, and having about 50 to about 100 percent of its active hydrogen-containing groups in the form of aromatic amine groups; (B) about 3.5 to about 8 parts of water per 100 parts by weight of component (A); (C) an effective amount of a tertiary amine catalyst; (D) about 0.1 to about 4 parts, per 100 parts by weight of component (A) of an alkanolamine cross-linker; and (E) a sufficient amount of an aromatic polyisocyanate to provide an isocyanate index from about 95 to about 120.

Claim 36

Dependent Claim 131 words

An open-celled polyurea or polyurea-polyurethane foam having a density of 6 pounds per cubic foot or less prepared by reacting a reaction mixture comprising (A) a polyether having an equivalent weight from about 500 to about 2500, an average functionality from about 1.8 to about 3, and having about 50 to about 100 percent of its active hydrogen-containing groups in the form of aromatic amine groups; (B) about 3.5 to about 8 parts of water per 100 parts by weight of component (A); (C) an effective amount of a tertiary amine catalyst; (D) about 0.1 to about 4 parts, per 100 parts by weight of component (A) of an alkanolamine cross-linker; and (E) a sufficient amount of an aromatic polyisocyanate to provide an isocyanate index from about 95 to about 120.

Claim 37

Dependent Claim 132 words

An open-celled polyurea or polyurea-polyurethane foam having a density of 6 pounds per cubic foot or less prepared by reacting a reaction mixture comprising (A) a polyether having an equivalent weight from about 500 to about 2500, an average functionality from about 1.8 to about 3, and having about 50 to about 100 percent of its active hydrogen-containing groups in the form of secondary aliphatic amine groups; (B) about 3.5 to about 8 parts of water per 100 parts by weight of component (A); (C) an effective amount of a tertiary amine catalyst; (D) about 0.1 to about 4 parts, per 100 parts by weight of component (A) of an alkanolamine cross-linker; and (E) a sufficient amount of an aromatic polyisocyanate to provide an isocyanate index from about 95 to about 120.

Claim 38

Dependent Claim 132 words

An open-celled polyurea or polyurea-polyurethane foam having a density of 6 pounds per cubic foot or less prepared by reacting a reaction mixture comprising (A) a polyether having an equivalent weight from about 500 to about 2500, an average functionality from about 1.8 to about 3, and having about 50 to about 100 percent of its active hydrogen-containing groups in the form of secondary aliphatic amine groups; (B) about 3.5 to about 8 parts of water per 100 parts by weight of component (A); (C) an effective amount of a tertiary amine catalyst; (D) about 0.1 to about 4 parts, per 100 parts by weight of component (A) of an alkanolamine cross-linker; and (E) a sufficient amount of an aromatic polyisocyanate to provide an isocyanate index from about 95 to about 120.

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1992-07-03	1993-01-02	1993-07-04	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1996-07-03	1997-01-02	1997-07-04	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	2000-07-03	2001-01-02	2001-07-04	$7700.00	Window Closed / Lapsed

Flexible polyurea or polyurea-polyurethane foams prepared from high equivalent weight amine-terminated compounds

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)