US4845058A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for improving strength of SiC ceramics
Assignee: Albemarle Corp
•
Filing: 1988-03-04
•
Granted: 1989-07-04
•
Expires: 2008-03-04
Abstract
Abstract The strength of SiC ceramic parts derived from certain preceramic compositions is improved by (A) cooling the parts in an inert atmosphere to a temperature at least as low as about 800° C. after preparing them by molding and pyrolyzing the preceramic compositions, (B) then heating them in air to about 1200°-1300° C., and (C) keeping them in air at that temperature for at least about one hour before allowing them to cool. The preceramic compositions from which the ceramics are derived are mixtures of SiC powders and polysilazanes having an alkali metal content of 0-100 ppm and prepared by reacting an organodihalosilane with ammonia, treating the ammonolysis product with a basic catalyst which is capable of deprotonating an NH group that is adjacent to an SiH group, and quenching the resultant product with an electrophilic quenching reagent.
Inventors
- 👤 John J. Rogers
- 👤 John Semen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 03:01
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/571
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
159 words
A process for preparing a ceramic which comprises (A) molding a preceramic composition comprising about 50-85% by weight of SiC powder and about 15-50% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder having an alkali metal content of 0-100 ppm and being a polysilazane prepared by reacting an organodihalosilane with ammonia, treating the ammonolysis product with a basic catalyst which is capable of deprotonating an NH group that is adjacent to an SiH group, and quenching the resultant product with an electrophilic quenching reagent, (B) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1200°-1450° C., (C) cooling the resultant ceramic part in an inert atmosphere to a temperature at least as low as about 800° C., (D) heating it in air to about 1200°-1300° C., and (E) keeping it in air at about 1200°-1300° C. for at least about one hour before allowing it to cool.
Claim 2
Dependent Claim
159 words
A process for preparing a ceramic which comprises (A) molding a preceramic composition comprising about 50-85% by weight of SiC powder and about 15-50% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder having an alkali metal content of 0-100 ppm and being a polysilazane prepared by reacting an organodihalosilane with ammonia, treating the ammonolysis product with a basic catalyst which is capable of deprotonating an NH group that is adjacent to an SiH group, and quenching the resultant product with an electrophilic quenching reagent, (B) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1200°-1450° C., (C) cooling the resultant ceramic part in an inert atmosphere to a temperature at least as low as about 800° C., (D) heating it in air to about 1200°-1300° C., and (E) keeping it in air at about 1200°-1300° C. for at least about one hour before allowing it to cool.
Claim 3
Dependent Claim
17 words
The process of claim 1 wherein the preceramic binder has an alkali metal content of 0-5 ppm.
Claim 4
Dependent Claim
32 words
The process of claim 1 wherein the preceramic binder is a polysilazane prepared by reacting methyldichlorosilane with ammonia, treating the ammonolysis product with potassium hydride, and quenching the resultant product with dimethylchlorosilane.
Claim 5
Dependent Claim
24 words
The process of claim 1 wherein the preceramic composition comprises about 70-80% by weight of SiC powder and about 20-30% by weight of binder.
Claim 6
Dependent Claim
19 words
The process of claim 1 wherein the preceramic composition has a particle size not larger than about 105 micrometers.
Claim 7
Dependent Claim
48 words
The process of claim 1 wherein the molded composition is pyrolyzed to a temperature of about 1300° C. and the resultant ceramic part, after being cooled, is heated in air to about 1300° C. and kept in air at about 1300° C. for at least about one hour.
Claim 8
Dependent Claim
150 words
A process for preparing a ceramic which comprises (A) molding a preceramic composition having a particle size not larger than about 105 micrometers and comprising about 70-80% by weight of SiC powder and about 20-30% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder having an alkali metal content of 0-5 ppm and being a polysilazane prepared by reacting methyldichlorosilane with ammonia, treating the ammonolysis product with potassium hydride, and quenching the resultant product with dimethylchlorosilane, (B) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1300° C., (C) cooling the resultant ceramic part in an inert atmosphere to a temperature at least as low as about 800° C., (D) heating it in air to about 1300° C., and (E) keeping it in air at about 1300° C. for at least about one hour before allowing it to cool.
Claim 9
Dependent Claim
150 words
A process for preparing a ceramic which comprises (A) molding a preceramic composition having a particle size not larger than about 105 micrometers and comprising about 70-80% by weight of SiC powder and about 20-30% by weight of a preceramic polysilazane binder at a temperature of about 60°-225° C., said binder having an alkali metal content of 0-5 ppm and being a polysilazane prepared by reacting methyldichlorosilane with ammonia, treating the ammonolysis product with potassium hydride, and quenching the resultant product with dimethylchlorosilane, (B) pyrolyzing the molded composition in an inert atmosphere to a temperature of about 1300° C., (C) cooling the resultant ceramic part in an inert atmosphere to a temperature at least as low as about 800° C., (D) heating it in air to about 1300° C., and (E) keeping it in air at about 1300° C. for at least about one hour before allowing it to cool.
References Cited (Backward Citations)
US4117507A
Cited
DE2833904A1
Cited
US4560526A
Cited
WO1985000363A1
Cited
US4482669A
Cited
US4645807A
Cited
US4650837A
Cited
US4659850A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-07-03 | 1993-01-02 | 1993-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-07-03 | 1997-01-02 | 1997-07-04 | $3760.00 | Window Closed / Lapsed |