Electrochromic device, new cathodic electrochromic material and method of making
Assignee: Ford Motor Co
•
Filing: 1987-12-24
•
Granted: 1989-06-27
•
Expires: 2007-12-24
Abstract
Abstract This invention teaches electrochromic bismuth oxide as a new electrochromic material. An electrochromic device is constructed from this material by forming a cathodic electrochromic device. A fast ion conductor is also provided which is capable of generating ions when an electric field is applied thereto. The fast ion conductor also permits ion movement therethrough while prohibiting electron movement therethrough. The fast ion conductor and the electrochromic bismuth oxide are arranged between an anode and a cathode to form an electrochromic device. Preferably, the bismuth oxide is in the form of a layer and that layer is positioned next to the cathode to form a cathodic electrochromic device which can generate a dark gray color.
Inventors
- 👤 Hulya Demirvont
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:16
CPC Classifications
G; G02; G02F; G02F1/00; G02F1/01; G02F1/15; G02F1/1514; G02F1/1523
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
47 words
A new cathodic electrochromic material comprising electrochromic bismuth oxide made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state.
Claim 2
Dependent Claim
47 words
A new cathodic electrochromic material comprising electrochromic bismuth oxide made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state.
Claim 3
Dependent Claim
99 words
An electrochromic device comprising: an anode, a cathode, a fast ion conductor capable of generating ions when an electrical field is applied thereto, said fast ion conductor permitting ion movement therethrough while prohibiting electron movement therethrough, and cathodic electrochromic material comprising electrochromic bismuth oxide made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state, said fast ion conductor and said electrochromic bismuth oxide being arranged between said anode and said cathode.
Claim 4
Dependent Claim
99 words
An electrochromic device comprising: an anode, a cathode, a fast ion conductor capable of generating ions when an electrical field is applied thereto, said fast ion conductor permitting ion movement therethrough while prohibiting electron movement therethrough, and cathodic electrochromic material comprising electrochromic bismuth oxide made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state, said fast ion conductor and said electrochromic bismuth oxide being arranged between said anode and said cathode.
Claim 5
Dependent Claim
20 words
The electrochromic device of claim 2 wherein: said fast ion conductor and said electrochromic bismuth oxide form a single layer.
Claim 6
Dependent Claim
18 words
The electrochromic device of claim 3 wherein: additional electrochromic materials are included between said anode and said cathode.
Claim 7
Dependent Claim
108 words
An electrochromic device comprising: an anode, a cathode, a fast ion conductor capable of generating ions when an electrical field is applied thereto, said fast ion conductor permitting ion movement therethrough while prohibiting electron movement therethrough, and a layer of cathodic electrochromic material comprising electrochromic bismuth oxide, said electrochromic bismuth oxide being made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) to a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state, said fast ion conductor and said electrochromic bismuth oxide layer being arranged between said anode and said cathode.
Claim 8
Dependent Claim
108 words
An electrochromic device comprising: an anode, a cathode, a fast ion conductor capable of generating ions when an electrical field is applied thereto, said fast ion conductor permitting ion movement therethrough while prohibiting electron movement therethrough, and a layer of cathodic electrochromic material comprising electrochromic bismuth oxide, said electrochromic bismuth oxide being made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) to a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state, said fast ion conductor and said electrochromic bismuth oxide layer being arranged between said anode and said cathode.
Claim 9
Dependent Claim
19 words
The electrochromic device of claim 5 wherein: additional electrochromic materials are included in said layer of electrochromic bismuth oxide.
Claim 10
Dependent Claim
48 words
The electrochromic device of claim 5 wherein: said electrochromic bismuth oxide layer is located adjacent said cathode, whereby said electrochromic device is a cathodic device, wherein coloration of said bismuth oxide layer is effected by reduction of said bismuth oxide layer when an electrical field is applied thereto.
Claim 11
Dependent Claim
37 words
A method of producing a dark grey color in an electrochromic device by applying a voltage of no greater than about -5 volts between said anode and said cathode of the electrochromic device defined in claim 7.
Claim 12
Independent Claim
125 words
A method of making a bismuth oxide cathodic electrochromic device which comprises: heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state and, applying the previously heated bismuth oxide to a cathode of said electrochromic device by thermally evaporating said previously heated bismuth oxide (Bi 2 O 3 ) in a vacuum of about 10 -4 torr and with said Bi 2 O 3 and said cathode being spaced from one another by a distance of about 10cm whereby electrochromic bismuth oxide is applied to said cathode at a rate of thickness build up of from 100 Å to 300 Å per minute.
Claim 13
Independent Claim
125 words
A method of making a bismuth oxide cathodic electrochromic device which comprises: heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state and, applying the previously heated bismuth oxide to a cathode of said electrochromic device by thermally evaporating said previously heated bismuth oxide (Bi 2 O 3 ) in a vacuum of about 10 -4 torr and with said Bi 2 O 3 and said cathode being spaced from one another by a distance of about 10cm whereby electrochromic bismuth oxide is applied to said cathode at a rate of thickness build up of from 100 Å to 300 Å per minute.
Claim 14
Dependent Claim
34 words
The method of making a bismuth oxide cathodic electrochromic device as defined in claim 9 wherein: said electrochromic bismuth oxide is applied at a rate of thickness build up of 200 Å per minute.
Claim 15
Dependent Claim
34 words
The method of making a bismuth oxide cathodic electrochromic device as defined in claim 9 wherein: said electrochromic bismuth oxide is applied to a thickness in a range from 3000 Å to 5000 Å.
Claim 16
Dependent Claim
29 words
The method of making a bismuth oxide cathodic electrochromic device as defined in claim 9 wherein: said electrochromic bismuth oxide is applied to a thickness of about 4000 Å.
Claim 17
Dependent Claim
81 words
An electrochromic device comprising: an anode, a cathode, a cathodic electrochromic layer interposed between said anode and said cathode, said cathodic electrochromic layer comprising bismuth oxide having a thickness in the range of from 3000 Å to 5000 Å, said electrochromic bismuth oxide made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state.
Claim 18
Dependent Claim
81 words
An electrochromic device comprising: an anode, a cathode, a cathodic electrochromic layer interposed between said anode and said cathode, said cathodic electrochromic layer comprising bismuth oxide having a thickness in the range of from 3000 Å to 5000 Å, said electrochromic bismuth oxide made by a method which comprises heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state.
Claim 19
Independent Claim
73 words
A method of making a bismuth oxide cathodic electrochromic device which comprises: heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state, and applying the previously heated bismuth oxide to one of the electrodes of said device by thermally evaporating said previously heated bismuth oxide in a vacuum onto said electrode.
Claim 20
Independent Claim
73 words
A method of making a bismuth oxide cathodic electrochromic device which comprises: heating bismuth oxide (Bi 2 O 3 ) at a temperature below the evaporation temperature of said bismuth oxide for a time sufficient to insure that it is in its base state, and applying the previously heated bismuth oxide to one of the electrodes of said device by thermally evaporating said previously heated bismuth oxide in a vacuum onto said electrode.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-26 | 1992-12-26 | 1993-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-26 | 1996-12-26 | 1997-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-26 | 2000-12-26 | 2001-06-27 | $7700.00 | Window Closed / Lapsed |