Method for the production of reinforced composites
Assignee: Lockheed Martin Corp
•
Filing: 1987-08-06
•
Granted: 1989-06-20
•
Expires: 2007-08-06
Abstract
Abstract A process for the production of reinforced refractory composite structures which may be of high density and shaped in desired three dimensional configurations. The shaped composite structures are produced by forming a suspension of particulate materials including a colloidal refractory power, colloidal sintering aid, and refractory reinforcement whiskers in a carrier liquid. The colloidal suspension is conformed to a desired configuration and brought into contact with a semipermeable membrane. A pressure is imposed on the suspension in the desired configuration to expel liquid from the suspension through the membrane to arrive at a green composite having a density of at least 40% of theoretical density. After drying, the green composite is then sintered under conditions to form an intergranular liquid phase in the composite providing further densification. A specific composite is a silicon carbide reinforced silicon nitride composite. The green composite may be sintered to provide a density of at least 93% of theoretical to produce a closed impermeable composite surface. The composite may then be subjected to hot isostatic pressing.
Inventors
- 👤 Douglas W. Freitag
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 18:10
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/593; C04B35/622; C04B35/64; C04B35/645; C04B35/6455; C04B35/71; C04B35/78; C04B35/80
Claims Analysis
Total Claims: 44
Claim 1
Independent Claim
136 words
In a method for producing a whisker reinforced refractory composite, the steps comprising: (a) forming a suspension in a carrier liquid of a mixture of particulate materials comprising a colloidal refractory matrix powder, a colloidal sintering aid and refractory reinforcing whiskers; (b) conforming said suspension to a desired configuration and into contact with a semi-permeable membrane; (c) retaining said suspension in said configuration while imposing a pressure on said suspension to expel liquid from said suspension through said membrane to arrive at a green composite shaped in said desired configuration and having a density equal to at least 40% of the theoretical density of said composite; (d) drying said green composite; and (e) thereafter sintering said shaped dried composite under an nonoxidative atmosphere at a temperature sufficient to form an intergranular liquid phase in said composite.
Claim 2
Dependent Claim
136 words
In a method for producing a whisker reinforced refractory composite, the steps comprising: (a) forming a suspension in a carrier liquid of a mixture of particulate materials comprising a colloidal refractory matrix powder, a colloidal sintering aid and refractory reinforcing whiskers; (b) conforming said suspension to a desired configuration and into contact with a semi-permeable membrane; (c) retaining said suspension in said configuration while imposing a pressure on said suspension to expel liquid from said suspension through said membrane to arrive at a green composite shaped in said desired configuration and having a density equal to at least 40% of the theoretical density of said composite; (d) drying said green composite; and (e) thereafter sintering said shaped dried composite under an nonoxidative atmosphere at a temperature sufficient to form an intergranular liquid phase in said composite.
Claim 3
Dependent Claim
24 words
The method of claim 1 wherein said colloidal suspension formed in step (a) has a particulate materials content of at least 20 volume %.
Claim 4
Dependent Claim
18 words
The method of claim 1 wherein said refractory whiskers are of a diameter no more than one micron.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said whiskers have a diameter no greater than the average diameter of said refractory powder.
Claim 6
Dependent Claim
28 words
The method of claim 1 wherein said suspension contains at least 20 volume % of said particulate materials and at least 50 volume % of said carrier liquid.
Claim 7
Dependent Claim
18 words
The method of claim 5 wherein said suspension contains at least 30 volume % of said particulate materials.
Claim 8
Dependent Claim
18 words
The method of claim 6 wherein said suspension contains at least 40 volume % of said particulate materials.
Claim 9
Dependent Claim
33 words
The method of claim 1 wherein said sintering aid in step (a) is present in an amount of at least 5 wt. % of the colloidal materials in said mixture of particulate materials.
Claim 10
Dependent Claim
70 words
The method of claim 1 further comprising incorporating a dispersing agent in said suspension of step (a) to aid in dispersing said particulate materials in said carrier liquid and further comprising the step of, after step (d) but before step (e) of claim 1, heating said dried composite to an elevated temperature sufficient to evolve said dispersing agent from said composite but less than the sintering temperature of step (e).
Claim 11
Dependent Claim
18 words
The method of claim 1 wherein step (c) is carried out by isostacticly imposing pressure on said suspension.
Claim 12
Dependent Claim
20 words
The method of claim 10 wherein said pressure in step (c) of claim 1 is no more than 7,000 psig.
Claim 13
Dependent Claim
20 words
The method of claim 11 wherein said sintering step is carried out at a pressure no more than 1000 psig.
Claim 14
Dependent Claim
36 words
The method of claim 1 wherein the concentration of said whiskers in mixture of particulate materials is no greater than the maximum concentration for the average aspect ratio of said whiskers as indicated by FIG. 1.
Claim 15
Dependent Claim
18 words
The method of claim 13 wherein said whiskers have an average aspect ratio of no more than 30.
Claim 16
Dependent Claim
32 words
The method of claim 1 wherein said refractory matrix powder is selected from the group consisting of aluminum oxide, aluminum nitride, silicon nitride, silicon dioxide, magnesium dioxide, zirconium dioxide and mixtures thereof.
Claim 17
Dependent Claim
30 words
The method of claim 15 wherein said refractory reinforcing whiskers are selected from the group, consisting of silicon carbide, silicon nitride, magnesium oxide, aluminum oxide, boron carbide and mixtures thereof.
Claim 18
Dependent Claim
142 words
In a method for producing a silicon carbide reinforced silicon nitride ceramic composite structure, the steps comprising: (a) forming a suspension in a carrier liquid of a mixture of particulate materials comprising a colloidal silicon nitride powder, a colloidal sintering aid material and silicon carbide reinforcing whiskers; (b) conforming said suspension to a desired configuration and into contact with a semi-permeable membrane; (c) retaining said suspension in said configuration while imposing a pressure on said suspension to expel liquid from said suspension through said membrane to arrive at a green composite shaped in said desired configuration and having a density equal to at least 40% of the theoretical density of said composite; (d) drying said green composite; and (e) thereafter sintering said shaped dried composite under a nitrogen atmosphere at a temperature sufficient to form an intergranular liquid phase in said composite.
Claim 19
Dependent Claim
142 words
In a method for producing a silicon carbide reinforced silicon nitride ceramic composite structure, the steps comprising: (a) forming a suspension in a carrier liquid of a mixture of particulate materials comprising a colloidal silicon nitride powder, a colloidal sintering aid material and silicon carbide reinforcing whiskers; (b) conforming said suspension to a desired configuration and into contact with a semi-permeable membrane; (c) retaining said suspension in said configuration while imposing a pressure on said suspension to expel liquid from said suspension through said membrane to arrive at a green composite shaped in said desired configuration and having a density equal to at least 40% of the theoretical density of said composite; (d) drying said green composite; and (e) thereafter sintering said shaped dried composite under a nitrogen atmosphere at a temperature sufficient to form an intergranular liquid phase in said composite.
Claim 20
Dependent Claim
30 words
The method of claim 17 wherein step (c) is carried out to expel liquid from said suspension to arrive at a density equal to at least 45% of theoretical density.
Claim 21
Dependent Claim
30 words
The method of claim 17 wherein step (c) is carried out to expel liquid from said suspension to arrive at a density equal to at least 50% of theoretical density.
Claim 22
Dependent Claim
19 words
The method of claim 17 wherein step (e) is carried out at a pressure no greater than 1000 psig.
Claim 23
Dependent Claim
23 words
The method of claim 20 wherein the pressure imposed on said suspension in step (c) to expel liquid is less than 10,000 psig.
Claim 24
Dependent Claim
23 words
The method of claim 17 wherein step (e) is carried out under nitrogen atmosphere at a pressure with the range of 1-200 psig.
Claim 25
Dependent Claim
16 words
The method of claim 22 wherein said nitrogen atmosphere is within the range of 100-200 psig.
Claim 26
Dependent Claim
23 words
The method of claim 17 wherein said suspension formed in step (a) has a particulate materials content of at least 20 volume %.
Claim 27
Dependent Claim
18 words
The method of claim 24 wherein said suspension contains at least 30 volume % of said particulate materials.
Claim 28
Dependent Claim
18 words
The method of claim 24 wherein said suspension contains at least 40 volume % of said particulate materials.
Claim 29
Dependent Claim
20 words
The method of claim 17 wherein said silicon carbide whiskers are of a diameter of no more than one micron.
Claim 30
Dependent Claim
27 words
The method of claim 17 wherein said whiskers have a diameter no greater than the average diameter of said silicon nitride powder and said sintering aid material.
Claim 31
Dependent Claim
18 words
The method of claim 17 wherein step (c) is carried out by isostaticly imposing pressure on said suspension.
Claim 32
Dependent Claim
20 words
The method of claim 29 wherein said pressure in step (c) of claim 14 is no more than 7,000 psig.
Claim 33
Dependent Claim
21 words
The method of claim 30 wherein said sintering step is carried out at a pressure of no more than 1000 psig.
Claim 34
Dependent Claim
39 words
The method of claim 31 wherein the concentration of said silicon carbide whiskers in the mixture of particulate materials is no greater than the maximum concentration for the average aspect ratio of said whiskers as indicated by FIG. 1.
Claim 35
Dependent Claim
18 words
The method of claim 32 wherein said whiskers have an average aspect ratio of no more than 30.
Claim 36
Dependent Claim
25 words
The method of claim 17 wherein said composite has a density at the conclusion of said sintering step of at least 90% of theoretical density.
Claim 37
Dependent Claim
25 words
The method of claim 17 wherein said composite has a density at the conclusion of said sintering step of at least 93% of theoretical density.
Claim 38
Dependent Claim
34 words
The method of claim 35 further comprising the step of subjecting the sintered composite to hot isostatic pressing at a pressure substantially greater than the pressure at which said sintering step is carried out.
Claim 39
Dependent Claim
37 words
The method of claim 36 wherein said sintering step is carried out at a pressure no greater than 1000 psig and said hot isostatic pressing step is carried out at a pressure of at least 10,000 psig.
Claim 40
Dependent Claim
121 words
In method for producing a silicon carbide reinforced silicon nitride ceramic composite structure, the steps comprising: (a) forming a suspension in a carrier liquid of particulate materials comprising colloidal silicon nitride powder, colloidal sintering aid material, and silicon carbide reinforcing whiskers; (b) conforming said suspension to a desired configuration and expelling liquid from said configuration under an applied pressure less than 5000 psig to arrive at a green composite shaped in said configuration; and (c) thereafter sintering said dried composite under a nitrogen atmosphere less than 200 psig at a temperature sufficient to form an intergranular liquid phase in said composite and in the presence of an ambient buffer material containing silicon nitride, a particulate sintering aid material and boron nitride.
Claim 41
Dependent Claim
121 words
In method for producing a silicon carbide reinforced silicon nitride ceramic composite structure, the steps comprising: (a) forming a suspension in a carrier liquid of particulate materials comprising colloidal silicon nitride powder, colloidal sintering aid material, and silicon carbide reinforcing whiskers; (b) conforming said suspension to a desired configuration and expelling liquid from said configuration under an applied pressure less than 5000 psig to arrive at a green composite shaped in said configuration; and (c) thereafter sintering said dried composite under a nitrogen atmosphere less than 200 psig at a temperature sufficient to form an intergranular liquid phase in said composite and in the presence of an ambient buffer material containing silicon nitride, a particulate sintering aid material and boron nitride.
Claim 42
Dependent Claim
48 words
The method of claim 38 wherein said sintering aid material in said suspension is less than the amount of said silicon nitride ceramic powder in said suspension and wherein the sintering aid material in the buffer is less than the amount of the silicon nitride in said buffer.
Claim 43
Dependent Claim
41 words
The method of claim 38 wherein said liquid is expelled from said mixture by imposing a pressure upon said mixture in said desired configuration to remove filtrate through a filter structure having a pore size sufficient to retain said particulate materials.
Claim 44
Dependent Claim
20 words
The method of claim 40 wherein said liquid is expelled from said suspension by isostatically imposing pressure on said suspension.
References Cited (Backward Citations)
US2311588A
Cited
US3833389A
Cited
US4560668A
Cited
JPS5954680A
Cited
US4507224A
Cited
US4543345A
Cited
US4693857A
Cited
GB2165230A
Cited
US4737326A
Cited
US4652413A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-19 | 1992-12-19 | 1993-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-19 | 1996-12-19 | 1997-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-19 | 2000-12-19 | 2001-06-20 | $7700.00 | Window Closed / Lapsed |