Method of etching aluminum alloys in semi-conductor wafers
Assignee: Nortel Networks Ltd
•
Filing: 1987-05-27
•
Granted: 1989-06-13
•
Expires: 2007-05-27
Abstract
Abstract A plasma etching technique for producing tapered side walls on the desired Aluminum conductor pattern is described. This involves forming a resist pattern on the Aluminum layer of a wafer and carrying out a first etching step using Cl2, BCl3 and CF4 at predetermined flow rates and low pressure until all the exposed Aluminum is removed. At the end of this step the Aluminum side walls are virtually vertical and facets are present on the resist. A second etching step is carried out under essentially the same conditions as before except that the Cl2 is reduced. During this etching step the facets on the resist are propagated laterally while the Aluminum side walls become tapered. According to modifications a rounded or jogged configuration can be obtained on the side walls but these too are considered generally tapered in nature as they progress from a wider base to a narrower peak.
Inventors
- 👤 Thomas Abraham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:45
CPC Classifications
C; C23; C23F; C23F4/00
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
151 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principle element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 at predetermined flow rates and operating at low pressure until all the exposed electrically conductive material is removed whereby virtually vertical side walls of the electrically conductive material are obtained, and subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same pressure and with the same flow rate of BCl 3 but with the flow rate of the Cl 2 reduced whereby tapering of the side walls is achieved, by lateral facet propagation of the resist using the chlorine species.
Claim 2
Independent Claim
151 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principle element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 at predetermined flow rates and operating at low pressure until all the exposed electrically conductive material is removed whereby virtually vertical side walls of the electrically conductive material are obtained, and subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same pressure and with the same flow rate of BCl 3 but with the flow rate of the Cl 2 reduced whereby tapering of the side walls is achieved, by lateral facet propagation of the resist using the chlorine species.
Claim 3
Dependent Claim
25 words
A method according to claim 1 in which, prior to the first etching step, the wafer is heated sufficiently to cause rounding of the resist.
Claim 4
Dependent Claim
26 words
A method according to claim 1 or claim 2 in which the Cl 2 is eliminated from the second etching step, thereby forming curved side walls.
Claim 5
Dependent Claim
19 words
A method according to claim 1 or claim 2 in which the electrically conductive material is essentially pure aluminum.
Claim 6
Independent Claim
176 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture but with higher flow rates of BCl 3 and Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of BCl 3 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 7
Independent Claim
176 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture but with higher flow rates of BCl 3 and Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of BCl 3 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 8
Dependent Claim
25 words
A method according to claim 5 in which, prior to the first etching step, the wafer is heated sufficiently to cause rounding of the resist.
Claim 9
Dependent Claim
18 words
A method according to claim 5 or 6 in which the electrically conductive material is essentially pure aluminum.
Claim 10
Independent Claim
150 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of SiCl 4 and Cl 2 at predetermined flow rates and operating at low pressure until all the exposed electrically conductive material is removed whereby virtually vertical side walls of the electrically conductive material are obtained, and subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and same pressure and with the same flow rate of SiCl 4 but with the flow rate of the Cl 2 reduced whereby tapering of the side walls is achieved, by lateral facet propagation of the resist using the chlorine species.
Claim 11
Independent Claim
150 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of SiCl 4 and Cl 2 at predetermined flow rates and operating at low pressure until all the exposed electrically conductive material is removed whereby virtually vertical side walls of the electrically conductive material are obtained, and subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and same pressure and with the same flow rate of SiCl 4 but with the flow rate of the Cl 2 reduced whereby tapering of the side walls is achieved, by lateral facet propagation of the resist using the chlorine species.
Claim 12
Dependent Claim
25 words
A method according to claim 8 in which, prior to the first etching step, the wafer is heated sufficiently to cause rounding of the resist.
Claim 13
Dependent Claim
26 words
A method according to claim 8 or claim 9 in which the Cl 2 is eliminated from the second etching step, thereby forming curved side walls.
Claim 14
Dependent Claim
19 words
A method according to claim 8 or claim 9 in which the electrically conductive material is essentially pure aluminum.
Claim 15
Independent Claim
176 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of SiCl 4 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture but with higher flow rates of SiCl 4 and Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of SiCl 4 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 16
Independent Claim
176 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of SiCl 4 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture but with higher flow rates of SiCl 4 and Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of SiCl 4 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 17
Dependent Claim
25 words
A method according to claim 12 in which, prior to the first etching step, the wafer is heated sufficiently to cause rounding of the resist.
Claim 18
Dependent Claim
18 words
A method according to claim 12 or 13 in which the electrically conductive material is essentially pure aluminum.
Claim 19
Independent Claim
157 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 and CF 4 at predetermined flow rates and operating at low pressure until all the exposed electrically conductive material is removed whereby virtually vertical side walls of the electrically conductive material are obtained, and subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same pressure and with the same flow rates of BCl 3 and CF 4 but with the flow rate of the Cl 2 reduced whereby tapering of the side walls is achieved, by lateral facet propagation of the resist using the Chlorine species.
Claim 20
Independent Claim
157 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 and CF 4 at predetermined flow rates and operating at low pressure until all the exposed electrically conductive material is removed whereby virtually vertical side walls of the electrically conductive material are obtained, and subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same pressure and with the same flow rates of BCl 3 and CF 4 but with the flow rate of the Cl 2 reduced whereby tapering of the side walls is achieved, by lateral facet propagation of the resist using the Chlorine species.
Claim 21
Dependent Claim
25 words
A method according to claim 15 in which, prior to the first etching step, the wafer is heated sufficiently to cause rounding of the resist.
Claim 22
Dependent Claim
26 words
A method according to claim 15 or claim 16 in which the Cl 2 is eliminated from the second etching step, thereby forming curved side walls.
Claim 23
Dependent Claim
19 words
A method according to claim 15 or claim 16 in which the electrically conductive material is essentially pure aluminum.
Claim 24
Dependent Claim
20 words
A method according to claim 1, 8 or 15 in which the low pressure is no greater than 20 mtorr.
Claim 25
Independent Claim
190 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 and CF 4 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same flow rate of CF 4 but with higher flow rates of BCl 3 and Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rates of BCl 3 and CF 4 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 26
Independent Claim
190 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 and CF 4 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same flow rate of CF 4 but with higher flow rates of BCl 3 and Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rates of BCl 3 and CF 4 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 27
Dependent Claim
25 words
A method according to claim 20 in which, prior to the first etching step, the wafer is heated sufficiently to cause rounding of the resist.
Claim 28
Dependent Claim
18 words
A method according to claim 20 or 21 in which the electrically conductive material is essentially pure aluminum.
Claim 29
Dependent Claim
25 words
A method according to claim 5, 12 or 20 in which the low pressure in the first etching step is no greater than 20 mtorr.
Claim 30
Independent Claim
182 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same flow rate of BCl 3 but with a higher flow rate of Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of BCl 3 as in the first etching step but a lower flat rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 31
Independent Claim
182 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same flow rate of BCl 3 but with a higher flow rate of Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of BCl 3 as in the first etching step but a lower flat rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 32
Independent Claim
183 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of SiCl 4 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and with the same flow rate of SiCl 4 but with a higher flow rate of Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of SiCl 4 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 33
Independent Claim
183 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of SiCl 4 and Cl 2 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and with the same flow rate of SiCl 4 but with a higher flow rate of Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, and subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rate of SiCl 4 as in the first etching step but a lower flow rate of Cl 2 , whereby jogged side walls of the electrically conductive material are obtained.
Claim 34
Independent Claim
190 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 , Cl 2 and CF 4 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same flow rates of BCl 3 and CF 4 but with a higher flow rate of Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, the subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rates of BCl 3 and CF 4 as in the first etching step but a lower flow rate of Cl 2 whereby jogging side walls of the electrically conductive material are obtained.
Claim 35
Independent Claim
190 words
A method of etching a layer of electrically conductive material, having aluminum as the principal element, formed on a semiconductor wafer, comprising forming a resist pattern on a layer of electrically conductive material having aluminum as the principal element, subjecting the wafer to a first plasma etching step using a gas mixture consisting essentially of BCl 3 , Cl 2 and CF 4 at predetermined flow rates and operating at low pressure until the exposed electrically conductive material begins to be removed, subjecting the wafer to a second plasma etching step using essentially the same components in the gas mixture and the same flow rates of BCl 3 and CF 4 but with a higher flow rate of Cl 2 and higher pressure until all of the exposed electrically conductive material is removed, the subjecting the wafer to a third plasma etching step using essentially the same components of the gas mixture and pressure and the same flow rates of BCl 3 and CF 4 as in the first etching step but a lower flow rate of Cl 2 whereby jogging side walls of the electrically conductive material are obtained.
References Cited (Backward Citations)
US4182646A
Cited
US4341593A
Cited
US4412885A
Cited
US4505782A
Cited
US4479850A
Cited
US4529475A
Cited
US4468284A
Cited
US4597826A
Cited
US4618398A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-12 | 1992-12-12 | 1993-06-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-12 | 1996-12-12 | 1997-06-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-12 | 2000-12-12 | 2001-06-13 | $7700.00 | Window Closed / Lapsed |