Stable polymer polyols in base polyols with molecular weight greater than 4000 using high molecular weight dispersants
Assignee: Lyondell Chemical Technology LP
•
Filing: 1988-05-24
•
Granted: 1989-06-06
•
Expires: 2008-05-24
Abstract
Abstract Low viscosity polymer polyols having high styrene/acrylonitrile ratios and good stability may be achieved by the use of a base polyol having a molecular weight higher than 4000, for example, from 4000 to 6500 and a high molecular weight (HMW) dispersant. The dispersant polyol may range from 1 to 20 wt. %, but may be less than 5 wt. % of the total polyol component of the polymer polyol. The HMW dispersant should have a molecular weight higher than about 6000. Preferably, a semi-batch reactor is used, and a relatively high concentration of the HMW dispersant is initially charged to the reactor, relative to the portion of base polyol. Monomer ratios of styrene to acrylonitrile of 85/15 may be achieved with this method.
Inventors
- 👤 Robert G. Gastinger
- 👤 John E. Hayes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:51
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/63; C08G18/636; C08G18/632
Claims Analysis
Total Claims: 53
Claim 1
Independent Claim
86 words
A method for making stable, low viscosity polymer polyols comprising the steps of: adding a charge to a reactor, where the charge comprises a high molecular weight polyol dispersant; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight of greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 20% of the total of all polyols.
Claim 2
Independent Claim
86 words
A method for making stable, low viscosity polymer polyols comprising the steps of: adding a charge to a reactor, where the charge comprises a high molecular weight polyol dispersant; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight of greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 20% of the total of all polyols.
Claim 3
Dependent Claim
33 words
The method for making polymer polyols of claim 1 where the high molecular weight polyol dispersant has a molecular weight greater than about 6000 and a functionality ranging from about 2 to 4.
Claim 4
Dependent Claim
72 words
The method for making polymer polyols of claim 1 where the high molecular weight polyol dispersant in the reactor charge is a first portion, and a second high molecular weight dispersant portion is present in the feed stream, and both the first portion and second portion of the high molecular weight polyol dispersant together are in the range of about 1 to 20% of the total of all portions of both polyols.
Claim 5
Dependent Claim
33 words
The method for making polymer polyols of claim 1 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 50/50 to 95/5.
Claim 6
Dependent Claim
33 words
The method for making polymer polyols of claim 1 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 65/35 to 85/15.
Claim 7
Dependent Claim
39 words
The method for making polymer polyols of claim 1 where the concentration of the high molecular weight polyol dispersant in the charge to the reactor ranges from 10 to 100 wt. % of the total polyol in the charge.
Claim 8
Dependent Claim
38 words
The method for making polymer polyols of claim 1 where the reactor is selected from the group of reactors consisting of a batch reactor, a semi-batch reactor and a plurality of continuous stirred tank reactors (CSTRs) in series.
Claim 9
Dependent Claim
43 words
The method for making polymer polyols of claim 3 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 5% of the total of all portions of both polyols.
Claim 10
Dependent Claim
43 words
The method for making polymer polyols of claim 3 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 3% of the total of all portions of both polyols.
Claim 11
Dependent Claim
43 words
The method for making polymer polyols of claim 3 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 2% of the total of all portions of both polyols.
Claim 12
Dependent Claim
23 words
The method for making polymer polyols of claim 1 where the viscosity of the resulting polymer polyols is less than about 5000 cps.
Claim 13
Dependent Claim
36 words
The method for making polymer polyols of claim 1 where the high molecular weight polyol dispersant is made by adding an alkylene oxide component to a polyfunctional initiator in the presence of a zinc hexacyanocobaltate catalyst.
Claim 14
Dependent Claim
32 words
The method for making polymer polyols of claim 1 where the wt. % of the total of all polyols that is present in the feed ranges from 50 to 99 wt %.
Claim 15
Dependent Claim
26 words
The method for making polymer polyols of claim 1 where the reactor charge additionally comprises a base polyol having a molecular weight of greater than 4000.
Claim 16
Dependent Claim
33 words
The method for making polymer polyols of claim 14 where the high molecular weight polyol dispersant has a molecular weight greater than about 6000 and a functionality ranging from about 2 to 4.
Claim 17
Dependent Claim
72 words
The method for making polymer polyols of claim 14 where the high molecular weight polyol dispersant in the reactor charge is a first portion, and a second high molecular weight dispersant portion is present in the feed stream, and both the first portion and second portion of the high molecular weight polyol dispersant together are in the range of about 1 to 20% of the total of all portions of both polyols.
Claim 18
Dependent Claim
33 words
The method for making polymer polyols of claim 14 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 50/50 to 95/5.
Claim 19
Dependent Claim
33 words
The method for making polymer polyols of claim 14 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 65/35 to 85/15.
Claim 20
Dependent Claim
39 words
The method for making polymer polyols of claim 14 where the concentration of the high molecular weight polyol dispersant in the charge to the reactor ranges from 10 to 50 wt. % of the total polyol in the charge.
Claim 21
Dependent Claim
38 words
The method for making polymer polyols of claim 14 where the reactor is selected from the group of reactors consisting of a batch reactor, a semi-batch reactor and a plurality of continuous stirred tank reactors (CSTRs) in series.
Claim 22
Dependent Claim
43 words
The method for making polymer polyols of claim 16 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 5% of the total of all portions of both polyols.
Claim 23
Dependent Claim
43 words
The method for making polymer polyols of claim 16 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 3% of the total of all portions of both polyols.
Claim 24
Dependent Claim
43 words
The method for making polymer polyols of claim 16 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 2% of the total of all portions of both polyols.
Claim 25
Dependent Claim
23 words
The method for making polymer polyols of claim 14 where the viscosity of the resulting polymer polyols is less than about 5000 cps.
Claim 26
Dependent Claim
36 words
The method for making polymer polyols of claim 14 where the high molecular weight polyol dispersant is made by adding an alkylene oxide component to a polyfunctional initiator in the presence of a zinc hexacyanocobaltate catalyst.
Claim 27
Dependent Claim
32 words
The method for making polymer polyols of claim 14 where the wt. % of the total of all polyols that is present in the feed ranges from 50 to 99 wt %.
Claim 28
Dependent Claim
29 words
The method for making polymer polyols of claim 14 where the base polyol in the reactor charge and the base polyol in the reactor feed are the same polyol.
Claim 29
Independent Claim
93 words
A method for making stable, low viscosity polymer polyols comprising the steps of: adding a charge to a reactor, where the charge comprises a high molecular weight polyol dispersant having a molecular weight greater than about 6000; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 5% of the total of all polyols.
Claim 30
Independent Claim
93 words
A method for making stable, low viscosity polymer polyols comprising the steps of: adding a charge to a reactor, where the charge comprises a high molecular weight polyol dispersant having a molecular weight greater than about 6000; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 5% of the total of all polyols.
Claim 31
Dependent Claim
22 words
The method for making polymer polyols of claim 28 where the high molecular weight dispersant polyol has an absence of induced unsaturation.
Claim 32
Dependent Claim
33 words
The method for making polymer polyols of claim 28 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 65/35 to 85/15.
Claim 33
Dependent Claim
39 words
The method for making polymer polyols of claim 28 where the concentration of the high molecular weight polyol dispersant in the charge to the reactor ranges from 10 to 100 wt. % of the total polyol in the charge.
Claim 34
Dependent Claim
38 words
The method for making polymer polyols of claim 28 where the reactor is selected from the group of reactors consisting of a batch reactor, a semi-batch reactor and a plurality of continuous stirred tank reactors (CSTRs) in series.
Claim 35
Dependent Claim
74 words
The method for making polymer polyols of claim 28 where the high molecular weight polyol dispersant in the reactor charge is a first portion, and a second portion of high molecular weight polyol dispersant is present in the feed stream, and the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 3% of the total of all portions of both polyols.
Claim 36
Dependent Claim
43 words
The method for making polymer polyols of claim 33 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 2% of the total of all portions of both polyols.
Claim 37
Dependent Claim
25 words
The method for making polymer polyols of claim 28 where the reactor charge further comprises a base polyol having a molecular weight greater than 4000.
Claim 38
Dependent Claim
29 words
The method for making polymer polyols of claim 33 where the base polyol in the reactor charge and the base polyol in the feed stream are the same polyol.
Claim 39
Independent Claim
167 words
A method for making stable, low viscosity polymer polyols comprising the steps of: adding a charge to a reactor, where the charge comprises a first portion of a high molecular weight polyol dispersant having a molecular weight greater than about 6000 and being free from induced unsaturation, and a first portion of a base polyol having a molecular weight greater than 4000, where the concentration of the high molecular weight polyol dispersant in the charge to the reactor ranges from 10 to 50 wt. % of the total polyol in the charge; providing a feed stream to the reactor, where the feed stream comprises a second portion of the high molecular weight polyol dispersant, a second portion of the base polyol, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 5% of the total of all portions of both polyols.
Claim 40
Independent Claim
167 words
A method for making stable, low viscosity polymer polyols comprising the steps of: adding a charge to a reactor, where the charge comprises a first portion of a high molecular weight polyol dispersant having a molecular weight greater than about 6000 and being free from induced unsaturation, and a first portion of a base polyol having a molecular weight greater than 4000, where the concentration of the high molecular weight polyol dispersant in the charge to the reactor ranges from 10 to 50 wt. % of the total polyol in the charge; providing a feed stream to the reactor, where the feed stream comprises a second portion of the high molecular weight polyol dispersant, a second portion of the base polyol, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 5% of the total of all portions of both polyols.
Claim 41
Dependent Claim
33 words
The method for making polymer polyols of claim 37 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 65/35 to 85/15.
Claim 42
Dependent Claim
38 words
The method for making polymer polyols of claim 37 where the reactor is selected from the group of reactors consisting of a batch reactor, a semi-batch reactor and a plurality of continuous stirred tank reactors (CSTRs) in series.
Claim 43
Dependent Claim
43 words
The method for making polymer polyols of claim 37 where the total of the first and second portions of the high molecular weight polyol dispersant is in the range of about 1 to 2% of the total of all portions of both polyols.
Claim 44
Dependent Claim
86 words
Stable, low viscosity polymer polyols made by the process comprising the steps of: adding a charge to a batch reactor, where the charge comprises a high molecular weight polyol dispersant; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 20% of the total of all polyols.
Claim 45
Dependent Claim
86 words
Stable, low viscosity polymer polyols made by the process comprising the steps of: adding a charge to a batch reactor, where the charge comprises a high molecular weight polyol dispersant; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 20% of the total of all polyols.
Claim 46
Dependent Claim
19 words
The stable, low viscosity polymer polyols of claim 41 where the base polyol has an absence of induced unsaturation.
Claim 47
Dependent Claim
33 words
The stable, low viscosity polymer polyols of claim 41 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 50/50 to 95/5.
Claim 48
Dependent Claim
33 words
The stable, low viscosity polymer polyols of claim 41 where the monomer portion is a mixture of styrene and acrylonitrile in a ratio of styrene to acrylonitrile of from about 65/35 to 85/15.
Claim 49
Dependent Claim
23 words
The stable, low viscosity polymer polyols of claim 41 where the viscosity of the resulting polymer polyols is less than about 5000 cps.
Claim 50
Dependent Claim
25 words
The stable, low viscosity polymer polyols of claim 41 where the reactor charge also comprises a base polyol having a molecular weight greater than 4000.
Claim 51
Dependent Claim
29 words
The stable, low viscosity polymer polyols of claim 46 where the base polyol in the reactor charge and the base polyol in the feed stream are the same polyol.
Claim 52
Dependent Claim
109 words
A polyurethane product made by a process comprising reacting a polymer polyol with an organic polyisocyanate in the presence of a polyurethane catalyst, where the polymer polyol is made by the process comprising the steps of: adding a charge to a batch reactor, where the charge comprises a high molecular weight polyol dispersant; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 20% of the total of all polyols.
Claim 53
Dependent Claim
109 words
A polyurethane product made by a process comprising reacting a polymer polyol with an organic polyisocyanate in the presence of a polyurethane catalyst, where the polymer polyol is made by the process comprising the steps of: adding a charge to a batch reactor, where the charge comprises a high molecular weight polyol dispersant; providing a feed stream to the reactor, where the feed stream comprises a base polyol having a molecular weight greater than 4000, a monomer portion and an initiator suitable for polymerizing the monomer portion, where the high molecular weight polyol dispersant is in the range of about 1 to 20% of the total of all polyols.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-05 | 1992-12-05 | 1993-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-05 | 1996-12-05 | 1997-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-05 | 2000-12-05 | 2001-06-06 | $7700.00 | Window Closed / Lapsed |