Method of producing heat treating furnace member
Assignee: Coorstek KK
•
Filing: 1987-09-08
•
Granted: 1989-06-06
•
Expires: 2007-09-08
Abstract
Abstract A method of producing a high density and high strength silicon carbide member for a heat treatment furnace to be used in the manufacture of a semiconductor device. In this method, SiC powder, carbon powder, deflocculating agent and water are mixed to form a slip. Then the slip is formed into a desired shape, cured under a nonoxidizing atmosphere, and removed of any impurity contained in the shaped body. Finally, the shaped body is immersed in a molten silicon to convert the carbon in the shaped body into silicon carbide.
Inventors
- 👤 Kenro Hayashi
- 👤 Takashi Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 22:51
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C04B35/573
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
129 words
A method for producing a member of a heat-treating furnace having high-strength and high-density, consisting essentially of: (a) forming a slip by preparing a mixture consisting essentially of SiC powder, 5-20% by weight of carbon powder based on the SiC powder, an effective amount of a deflocculating agent, and water; (b) forming the slip into a shaped body, said shaped body having SiC and carbon substantially uniformly dispersed therein; (c) curing the shaped body under a non-oxidizing gas atmosphere; (d) removing impurities from the shaped body by a wet or dry process; and (e) immersing the shaped body in molten silicon to form silicon carbide by the reaction between the impregnated silicon and the carbon contained in the raw material, to thereby form a three-dimensionally interconnected SiC structure therein.
Claim 2
Independent Claim
129 words
A method for producing a member of a heat-treating furnace having high-strength and high-density, consisting essentially of: (a) forming a slip by preparing a mixture consisting essentially of SiC powder, 5-20% by weight of carbon powder based on the SiC powder, an effective amount of a deflocculating agent, and water; (b) forming the slip into a shaped body, said shaped body having SiC and carbon substantially uniformly dispersed therein; (c) curing the shaped body under a non-oxidizing gas atmosphere; (d) removing impurities from the shaped body by a wet or dry process; and (e) immersing the shaped body in molten silicon to form silicon carbide by the reaction between the impregnated silicon and the carbon contained in the raw material, to thereby form a three-dimensionally interconnected SiC structure therein.
Claim 3
Dependent Claim
34 words
The method according to claim 1, wherein the SiC powder has a particle diameter of 40 to 1 μm, and the particle diameter of the carbon powder ranges between 5 μm and 1 μm.
Claim 4
Dependent Claim
31 words
The method according to claim 1, wherein the amount of the deflocculating agent ranges between 0.5 and 4% by weight based on the sum of the SiC powder and carbon powder.
Claim 5
Dependent Claim
18 words
The method according to claim 1, wherein the inert gas atmosphere is provided by a N 2 gas.
Claim 6
Dependent Claim
16 words
The method according to claim 1, wherein said deflocculating agent is sodium silicate or sodium aluminate.
Claim 7
Dependent Claim
19 words
The method according to claim 1, wherein said carbon powder is used in the amount of 10-15% by weight.
Claim 8
Dependent Claim
19 words
The method according to claim 1, wherein said curing temperature is in the range of 100° to 300° C.
Claim 9
Dependent Claim
55 words
The method according to claim 1, wherein said wet process for removing impurities comprises first sintering the shaped body in an inert atmopshere at a temperature of 1800° C. or more, and then immersing the shaped body in a mixed acid consisting of HF, HNO 3 and H 2 O, thereby dissolving out said impurities.
Claim 10
Dependent Claim
33 words
The method according to claim 1, wherein said dry process for removing impurities comprises heating the shaped body at a temperature of about 1600°-2000° C. in the presence of a halogen gas atmosphere.
Claim 11
Dependent Claim
17 words
The method according to claim 1, wherein said removed impurities comprise Ni, Fe, Cu, Na and Al.
Claim 12
Dependent Claim
20 words
The method according to claim 1, wherein said carbon powder is dispersed in a substantially uniform manner in said slip.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-05 | 1992-12-05 | 1993-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-05 | 1996-12-05 | 1997-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-05 | 2000-12-05 | 2001-06-06 | $7700.00 | Window Closed / Lapsed |