Process of forming silicon carbide bodies
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1976-12-30
•
Granted: 1978-11-28
•
Expires: 1996-12-30
Abstract
Abstract A castable slip of a bimodal distribution of silicon carbide particles is prepared, the slip preferably containing a water miscible curable resin. A shaped body is cast in a plaster of paris mold which also preferably contains a small amount of a water soluble polymer. The casting and mold are then heat treated to increase the strength of the green casting. In a preferred embodiment of the invention the resin in the slip is cured by the heat treating step. The mold is then removed by decomposing the mold material, preferably by dipping the mold in acid to attack the mold material (e.g. the water soluble polymer or the plaster of paris itself). The cured resin in the casting is sufficiently resistant to attack by the acid to survive the mold removal. In an alternative embodiment the silicon carbide body is heated to a sufficiently high temperature (e.g. 650°-750° C) to slightly oxidize the SiC and to strengthen the green casting. Along with this heating the water soluble polymer in the mold is burned out and the mold is thereby weakened to permit its ready removal. Thereafter, the cast silicon carbide product is fired to carbonize any resin in the SiC and recrystallize the silicon carbide. The product is then preferably siliconized to react all of the carbon remaining from the resin and any additional carbon that may be added after recrystallization of the silicon carbide.
Inventors
- 👤 Gerald Q. Weaver
- 👤 John C. Logan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:34
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; B; B28; B28B; B28B1/00; B28B1/26; B28B7/00; B28B7/34; B28B7/342; C04B35/573; C04B35/622; C04B35/626; C04B35/62605; C04B35/62625; C04B35/6263; C04B35/6269; C04B35/63; C04B35/632; C04B35/636; C04B35/6365; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/34; C04B2235/3427; C04B2235/38; C04B2235/3817; C04B2235/3826; C04B2235/42; C04B2235/428; C04B2235/48; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/5436; C04B2235/5463; C04B2235/5472; C04B2235/60; C04B2235/602; C04B2235/6027; C04B2235/6028; C04B2235/616; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/66; C04B2235/661; C04B2235/662; C04B2235/70; C04B2235/80
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
162 words
A process for casting a complex silicon carbide shape which requires destruction of the mold to permit removal of the complex cast shape, said process including the steps of forming a castable aqueous slip from particles of finely powdered silicon carbide, said slip containing approximately 1 to 10% of a water miscible resin that will set or cure at a temperature below 200° C. to a structure that is relatively inert to an acid, casting said slip into a plaster mold which is attacked by said acid, heat treating the mold and cast slip to cure said resin and increase the green strength of the casting, decomposing the plaster mold by treating with said acid to facilitate removal of the mold from the strengthened casting, the curing step imparting substantial strength to the green casting so that the cured green casting is stronger than the acid treated mold, removing the decomposed mold to free the green casting and further firing the casting.
Claim 2
Dependent Claim
162 words
A process for casting a complex silicon carbide shape which requires destruction of the mold to permit removal of the complex cast shape, said process including the steps of forming a castable aqueous slip from particles of finely powdered silicon carbide, said slip containing approximately 1 to 10% of a water miscible resin that will set or cure at a temperature below 200° C. to a structure that is relatively inert to an acid, casting said slip into a plaster mold which is attacked by said acid, heat treating the mold and cast slip to cure said resin and increase the green strength of the casting, decomposing the plaster mold by treating with said acid to facilitate removal of the mold from the strengthened casting, the curing step imparting substantial strength to the green casting so that the cured green casting is stronger than the acid treated mold, removing the decomposed mold to free the green casting and further firing the casting.
Claim 3
Dependent Claim
224 words
The process of forming a silicon carbide body having thin delicate sections which comprises forming a castable slip of a bimodal mixture of silicon carbide fine particles, a portion of said particles having an average size on the order of 3 microns and another portion of said particles having an average size of less than about 200 mesh, preparing an aqueous plaster mold mix by incorporating in the plaster mold mix 0.1 to 4% (by weight) of an organic polymer, said polymer being in an aqueous solution and having the property of forming very fine bubbles in the plaster mix and also of maintaining the plaster particles suspended in the aqueous mix in dilutions where the particles would normally settle, preparing a mold having a smooth porous surface from said plaster mix, casting said slip into the porous plaster mold, solidifying the slip in the mold, heating the mold and the casting to a temperature in excess of 600° C in an oxidizing atmosphere for a sufficiently long time to partially oxidize the silicon carbide and thereby substantially increase the green strength of the casting by forming a glassy bond for the silicon carbide, the heating step also serving to oxidize the polymer in the mold to decompose the mold sufficiently so that it can be readily brushed from the green silicon carbide casting.
Claim 4
Dependent Claim
224 words
The process of forming a silicon carbide body having thin delicate sections which comprises forming a castable slip of a bimodal mixture of silicon carbide fine particles, a portion of said particles having an average size on the order of 3 microns and another portion of said particles having an average size of less than about 200 mesh, preparing an aqueous plaster mold mix by incorporating in the plaster mold mix 0.1 to 4% (by weight) of an organic polymer, said polymer being in an aqueous solution and having the property of forming very fine bubbles in the plaster mix and also of maintaining the plaster particles suspended in the aqueous mix in dilutions where the particles would normally settle, preparing a mold having a smooth porous surface from said plaster mix, casting said slip into the porous plaster mold, solidifying the slip in the mold, heating the mold and the casting to a temperature in excess of 600° C in an oxidizing atmosphere for a sufficiently long time to partially oxidize the silicon carbide and thereby substantially increase the green strength of the casting by forming a glassy bond for the silicon carbide, the heating step also serving to oxidize the polymer in the mold to decompose the mold sufficiently so that it can be readily brushed from the green silicon carbide casting.
Claim 5
Dependent Claim
167 words
A process for casting a complex refractory shape which requires destruction of the mold to permit removal of the complex cast shape, said process including the steps of forming a castable aqueous slip from particles of finely powdered refractory material said slip containing approximately 1 to 10% of a water miscible resin that will set or cure at a temperature below 200° C. to a structure that is relatively inert to an acid, casting said slip into a plaster mold which is attacked by said acid, heat treating the mold and cast slip to cure said resin and increase the green strength of the casting, decomposing the plaster mold by treating with said acid to facilitate removal of the mold from the strengthened casting, the curing step imparting substantial strength to the green casting so that the cured green casting is stronger than the acid treated mold, removing the decomposed mold to free the green casting and further heat treating the casting by firing the green casting.
Claim 6
Dependent Claim
167 words
A process for casting a complex refractory shape which requires destruction of the mold to permit removal of the complex cast shape, said process including the steps of forming a castable aqueous slip from particles of finely powdered refractory material said slip containing approximately 1 to 10% of a water miscible resin that will set or cure at a temperature below 200° C. to a structure that is relatively inert to an acid, casting said slip into a plaster mold which is attacked by said acid, heat treating the mold and cast slip to cure said resin and increase the green strength of the casting, decomposing the plaster mold by treating with said acid to facilitate removal of the mold from the strengthened casting, the curing step imparting substantial strength to the green casting so that the cured green casting is stronger than the acid treated mold, removing the decomposed mold to free the green casting and further heat treating the casting by firing the green casting.
Claim 7
Dependent Claim
243 words
A process for casting a complex refractory shape which requires destruction of the mold to permit removal of the complex cast shape, said process including the steps of forming a castable aqueous slip from particles of a mixture of powdered refractory material, a portion of said particles being silicon carbide having an average size on the order of 3 microns and another portion of said particles having an average size of less than about 200 mesh, preparing an aqueous plaster mold mix by incorporating in the plaster mold mix 0.1 to 4% (by weight) of an organic polymer, said polymer being in an aqueous solution and having the property of forming very fine bubbles in the plaster mix and also of maintaining the plaster particles suspended in the aqueous mix in dilutions where the particles would normally settle, preparing a mold having a smooth porous surface from said plaster mix, casting said slip into the porous plaster mold, solidifying the slip in the mold, heating the mold and the casting to a temperature in excess of 600° C in an oxidizing atmosphere for a sufficiently long time to partially oxidize the fine silicon carbide and thereby substantially increase the green strength of the casting by forming a glassy bond for the silicon carbide, the heating step also serving to oxidize the polymer in the mold to decompose the mold sufficiently so that it can be readily brushed from the green silicon carbide casting.
Claim 8
Dependent Claim
243 words
A process for casting a complex refractory shape which requires destruction of the mold to permit removal of the complex cast shape, said process including the steps of forming a castable aqueous slip from particles of a mixture of powdered refractory material, a portion of said particles being silicon carbide having an average size on the order of 3 microns and another portion of said particles having an average size of less than about 200 mesh, preparing an aqueous plaster mold mix by incorporating in the plaster mold mix 0.1 to 4% (by weight) of an organic polymer, said polymer being in an aqueous solution and having the property of forming very fine bubbles in the plaster mix and also of maintaining the plaster particles suspended in the aqueous mix in dilutions where the particles would normally settle, preparing a mold having a smooth porous surface from said plaster mix, casting said slip into the porous plaster mold, solidifying the slip in the mold, heating the mold and the casting to a temperature in excess of 600° C in an oxidizing atmosphere for a sufficiently long time to partially oxidize the fine silicon carbide and thereby substantially increase the green strength of the casting by forming a glassy bond for the silicon carbide, the heating step also serving to oxidize the polymer in the mold to decompose the mold sufficiently so that it can be readily brushed from the green silicon carbide casting.
References Cited (Backward Citations)
US2303303A
Cited
US2527390A
Cited
US2964823A
Cited
US3383444A
Cited
US3673293A
Cited
US3549473A
Cited
DE2234924A1
Cited
US4017433A
Cited
US4041117A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-11-27 | 1982-05-29 | 1982-11-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-11-27 | 1986-05-29 | 1986-11-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-11-27 | 1990-05-29 | 1990-11-28 | $7700.00 | Window Closed / Lapsed |