Method and apparatus for sputtering a superconductor onto a substrate
Assignee: Individual
•
Filing: 1988-03-07
•
Granted: 1989-05-30
•
Expires: 2008-03-07
Abstract
Abstract A method for sputter deposition of films or coatings over large areas or at widely different substrate locations relative to the target where the coating is of exactly the same component composition as the target from where the material is being sputtered. This is accomplished by sputtering in a noble gas or other vapor plasma through ion bombarding of at least one spherical or partially spherical target. Superconductors, as well as many other multicomponent materials, can be sputter deposited on a substrate with unchanged composition by utilizing a spherical target in a low gas or vapor pressure plasma.
Inventors
- 👤 Gottfried K. Wehner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 15:31
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0661; C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/3407; C23C14/3414; H10N60/0296; H10N60/0408; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/815; Y10S505/816
Claims Analysis
Total Claims: 46
Claim 1
Independent Claim
88 words
The method of sputter-depositing a film or coating from a substantially spherical target comprising the steps of: a. immersing a substantially spherical target in a low pressure plasma of uniform plasma density; b. providing the substantially spherical target with a metal wire or rod for applying the negative sputtering voltage, carrying the current and for holding it in the low pressure uniform plasma; and, c. positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles.
Claim 2
Independent Claim
88 words
The method of sputter-depositing a film or coating from a substantially spherical target comprising the steps of: a. immersing a substantially spherical target in a low pressure plasma of uniform plasma density; b. providing the substantially spherical target with a metal wire or rod for applying the negative sputtering voltage, carrying the current and for holding it in the low pressure uniform plasma; and, c. positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein said target is a spherical multicomponent target for replicating the target composition in the deposit.
Claim 4
Dependent Claim
23 words
The method of claim 1 comprising the step of immersing said spherical target in a uniform low pressure plasma of a triode discharge.
Claim 5
Dependent Claim
21 words
The method of claim 1 comprising the step of making the spherical target the cathode in a low pressure diode discharge.
Claim 6
Dependent Claim
20 words
The method of claim 1 comprising the step of immersing the spherical target in a low pressure RF excited plasma.
Claim 7
Dependent Claim
18 words
The method of claim 1 comprising the step of immersing the spherical target in a microwave excited plasma.
Claim 8
Dependent Claim
24 words
The method of claim 1 comprising the step of using a target comprising a sphere which is coated with the material to be sputtered.
Claim 9
Dependent Claim
22 words
The method of claim 7 wherein said target is coated with an insulator and sputtered by applying RF to the metal sphere.
Claim 10
Dependent Claim
12 words
The method of claim 1 comprising the step of cooling the target.
Claim 11
Dependent Claim
37 words
The method of claim 1 comprising the step of arranging the substrates to be coated so that the surfaces of said substrates always view a part of said spherical target surface which is uniformly bombarded with ions.
Claim 12
Dependent Claim
43 words
The method of claim 1 of using more than one spherical target, each of said targets being immersed in a low pressure uniform plasma for increasing the deposition rate and for obtaining upon the surfaces of said substrates a greater deposition thickness uniformity.
Claim 13
Dependent Claim
23 words
The method of claim 11 wherein said spherical targets are of at least one high TC superconducting material for sputter-depositing films or coatings.
Claim 14
Dependent Claim
14 words
The method of claim 12 wherein said superconductor material is a 123 ceramic superconductor.
Claim 15
Dependent Claim
50 words
The method of claim 1 comprising the steps of: a. aligning target spheres in a row, all of said spheres being immersed in a low pressure uniform plasma; b. separately and simultaneously sputtering onto the substrates; and, c. moving said substrates across this "line source" for coting large substrate areas.
Claim 16
Dependent Claim
43 words
The method of claim 1 comprising the steps of: a. arranging target spheres in a circular fashion for sputtering onto wires or rod substrates; and, b. moving said wire or rod substrates through the center of the circle for coating the substrates uniformly.
Claim 17
Dependent Claim
36 words
The method of claim 1 comprising the steps of sputtering in a low pressure mercury triode plasma where the electrons for plasma formation are supplied from cathode spots ignited and sustained on a liquid mercury pool.
Claim 18
Independent Claim
106 words
A system for sputtering a multicomponent spherical target for use in sputter deposition on substrates of coatings having the same composition as the target, comprising: a. at least one substantially spherical target element comprising a plurality of constituents, which have different angular distributions of emitted particles; b. means for positioning said target in a low pressure, uniform plasma; and, c. means for positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles, whereby the target constituents are deposited on the substrate in the same proportions as said target constituents exist in the target.
Claim 19
Independent Claim
106 words
A system for sputtering a multicomponent spherical target for use in sputter deposition on substrates of coatings having the same composition as the target, comprising: a. at least one substantially spherical target element comprising a plurality of constituents, which have different angular distributions of emitted particles; b. means for positioning said target in a low pressure, uniform plasma; and, c. means for positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles, whereby the target constituents are deposited on the substrate in the same proportions as said target constituents exist in the target.
Claim 20
Dependent Claim
39 words
A system for sputtering the target of claim 17 wherein said plasma is a low pressure mercury triode plasma where the electrons for plasma formation are supplied from cathode spots ignited and sustained on a liquid pool of mercury.
Claim 21
Dependent Claim
18 words
A system for sputtering the target of claim 17 wherein said plurality of constituents comprises a superconductor material.
Claim 22
Dependent Claim
18 words
A system for sputtering the target of claim 19 wherein said superconductor material is 123 ceramic superconductor material.
Claim 23
Independent Claim
103 words
A system for sputtering a multicomponent superconductor spherical target for use in sputter deposition on a substrate of coatings having the same composition as the targets comprising: a. at least one substantially spherical superconductor target which has different angular distributions of emitted atoms; b. means for positioning said target in a low pressure, uniform plasma; and, c. means for positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles, whereby the target superconductor material is deposited on the substrate with a composition which is identical to that of the target.
Claim 24
Independent Claim
103 words
A system for sputtering a multicomponent superconductor spherical target for use in sputter deposition on a substrate of coatings having the same composition as the targets comprising: a. at least one substantially spherical superconductor target which has different angular distributions of emitted atoms; b. means for positioning said target in a low pressure, uniform plasma; and, c. means for positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles, whereby the target superconductor material is deposited on the substrate with a composition which is identical to that of the target.
Claim 25
Dependent Claim
83 words
System for sputtering a superconductor material onto a substrate comprising: a. a substantially spherical target of a superconductor material; b. a substrate positioned such that it faces said target so that the deposited material consists of atoms which were ejected from the spherical target under all possible ejection angles; and, c. means for generating a low pressure uniform plasma about said target whereby said target superconductor material is deposited on said substrate with a composition which is identical to that of the target.
Claim 26
Dependent Claim
83 words
System for sputtering a superconductor material onto a substrate comprising: a. a substantially spherical target of a superconductor material; b. a substrate positioned such that it faces said target so that the deposited material consists of atoms which were ejected from the spherical target under all possible ejection angles; and, c. means for generating a low pressure uniform plasma about said target whereby said target superconductor material is deposited on said substrate with a composition which is identical to that of the target.
Claim 27
Dependent Claim
94 words
A multicomponent target used to sputter-deposit on a substrate films or coatings which have the same composition as the target comprising: a. a substantially spherical target comprising a plurality of uniformly distributed constituents of a superconductor, which have different angular distributions of emitted particles, said spherical target providing for interception of particles at substrates emitted from tangentially to the surface of said target through particles emitted perpendicular to the surface of said target, whereby the target constituents are deposited on the substrate in the same proportions as said target constituents exist in the target.
Claim 28
Dependent Claim
94 words
A multicomponent target used to sputter-deposit on a substrate films or coatings which have the same composition as the target comprising: a. a substantially spherical target comprising a plurality of uniformly distributed constituents of a superconductor, which have different angular distributions of emitted particles, said spherical target providing for interception of particles at substrates emitted from tangentially to the surface of said target through particles emitted perpendicular to the surface of said target, whereby the target constituents are deposited on the substrate in the same proportions as said target constituents exist in the target.
Claim 29
Independent Claim
94 words
The method of sputter-depositing a film or coating from a substantially spherical target, comprising the steps of: a. immersing a substantially spherical target of at least one high TC superconducting material in a low pressure plasma of uniform plasma density; b. providing the substantially spherical target with a metal wire or rod for applying the negative sputtering voltage, carrying the current and for holding it in the uniform plasma; and, c. positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles.
Claim 30
Independent Claim
94 words
The method of sputter-depositing a film or coating from a substantially spherical target, comprising the steps of: a. immersing a substantially spherical target of at least one high TC superconducting material in a low pressure plasma of uniform plasma density; b. providing the substantially spherical target with a metal wire or rod for applying the negative sputtering voltage, carrying the current and for holding it in the uniform plasma; and, c. positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles.
Claim 31
Dependent Claim
21 words
The method of claim 24 wherein said target is a spherical multicomponent target for replicating the target composition in the deposit.
Claim 32
Dependent Claim
23 words
The method of claim 24 comprising the step of immersing said spherical target in a uniform low pressure plasma of a triode discharge.
Claim 33
Dependent Claim
21 words
The method of claim 24 comprising the step of making the spherical target the cathode in a low pressure diode discharge.
Claim 34
Dependent Claim
20 words
The method of claim 24 comprising the step of immersing the spherical target in a low pressure RF excited plasma.
Claim 35
Dependent Claim
18 words
The method of claim 24 comprising the step of immersing the spherical target in a microwave excited plasma.
Claim 36
Dependent Claim
24 words
The method of claim 24 comprising the step of using a target comprising a sphere which is coated with the material to be sputtered.
Claim 37
Dependent Claim
21 words
The method of claim 30 wherein said target is coated with an insulator and sputtered by applying RF to the sphere.
Claim 38
Dependent Claim
12 words
The method of claim 24 comprising the step of cooling the target.
Claim 39
Dependent Claim
37 words
The method of claim 24 comprising the step of arranging the substrates to be coated so that the surfaces of said substrates always view a part of said spherical target surface which is uniformly bombard with ions.
Claim 40
Dependent Claim
43 words
The method of claim 24 of using more than one spherical target, each of said targets being immersed in a low pressure uniform plasma for increasing the deposition rate and for obtaining upon the surfaces of said substrates a greater deposition thickness uniformity.
Claim 41
Dependent Claim
49 words
The method of claim 24 comprising the steps of: a. algining target spheres in a row, all of said spheres being immersed in a low pressure plasma; b. separately and simultaneously sputtering onto the substrates; and, c. moving said substrates across this "line source" for coating large substrate areas.
Claim 42
Dependent Claim
36 words
The method of claim 24 comprising the steps of sputtering in a low pressure mercury triode plasma where the electrons for plasma formation are supplied from cathode spots ignited and sustained on a liquid mercury pool.
Claim 43
Independent Claim
107 words
A system for sputting a multicomponent spherical target for use in sputter deposition on substrates of coatings having the same composition as the target comprising: a. at least one substantially spherical target element comprising a plurality of superconductor constituents, which have different angular distributions of emitted particles; b. means for positioning said target in a low pressure, uniform plasma; and c. means for positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles, whereby the target constituents are deposited on the substrate in the same proportions as said target constituents exist in the target.
Claim 44
Independent Claim
107 words
A system for sputting a multicomponent spherical target for use in sputter deposition on substrates of coatings having the same composition as the target comprising: a. at least one substantially spherical target element comprising a plurality of superconductor constituents, which have different angular distributions of emitted particles; b. means for positioning said target in a low pressure, uniform plasma; and c. means for positioning substrates such that the deposited material consists of atoms which were ejected from the spherical target surface under all possible ejection angles, whereby the target constituents are deposited on the substrate in the same proportions as said target constituents exist in the target.
Claim 45
Dependent Claim
35 words
The system of claim 37 wherein said plasma is a low pressure mercury triode plasma where the electrons for plasma formation are supplied from cathode spots ignited and sustained on a liquid pool of mercury.
Claim 46
Dependent Claim
16 words
The system of claim 37 wherein said superconductor material is 123(Y,Ba 2 Cu3 O 7-x ).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-29 | 1992-11-28 | 1993-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-29 | 1996-11-28 | 1997-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-29 | 2000-11-28 | 2001-05-30 | $7700.00 | Window Closed / Lapsed |