Method of making shaped ceramic articles by shape replication of an expendable pattern
Assignee: Lanxide Technology Co LP
•
Filing: 1988-06-13
•
Granted: 1989-05-16
•
Expires: 2008-06-13
Abstract
Abstract A method of producing shaped, self-supporting ceramic bodies includes preparing a mold by applying a permeable, conformable material to a shape-defining surface of an expendable pattern. The permeable, conformable material, when set or stable, provides a mold with a shaped surface which is defined by, and is therefore substantially congruent to, the shape-defining surface. Upon heating, the material of the expendable pattern combusts or volatilizes and thus establishes the shaped cavity mold. A molten parent metal is then oxidized with a vapor-phase oxidant in such a manner as to form a ceramic body which grows into the mold cavity, and is shaped by it. The ceramic body is recovered from the mold having a shaped surface replicating the shape-defining surface of the expendable pattern.
Inventors
- 👤 E. Allen LaRoche, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 09:43
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/65; C04B35/652; B; B22; B22F; B22F3/00
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
330 words
A method for producing a shaped, self-supporting ceramic component comprising the oxidation reaction product of a parent metal, said method comprising: (a) providing a body of parent metal and an expendable pattern having a shape-defining surface shaped outwardly from said body of parent metal; (b) applying a gas-permeable coating of conformable material to said shape-defining surface to form a congruent surface substantially congruent to and coextensive with said shape-defining surface and disposed oppositely from said body of parent metal such that said expendable pattern defines a volume between said parent metal and said congruent surfce, said gas-permeable coating of conformable material having, at least under the process conditions, a self-bonding support zone immediately adjacent to and coextensive with said shape-defining surface, said support zone providing sufficient cohesive strength and retaining the shape of said congruent surface upon elimination of said expendable pattern; (c) heating said parent metal in the presence of at least a vapor-phase oxidant to a temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten metal, (d) eliminating said expendable pattern to form said mold cavity; (e) at said temperature (i) reacting said molten metal with said vapor-phase oxidant to form an oxidation reaction product, which product is in contact with and extends between said body of molten metal and said vapor-phase oxidant, and (ii) transporting said molten metal through said oxidation reaction product toward said vapor-phase oxidant and gas-permeable coating of conformable material so that oxidation reaction product continues to form at an interface between said vapor-phase oxidant and previously formed oxidation reaction product, thereby forming a progressively thicker body of said oxidation reaction product into said mold cavity; (f) continuing said reacting for a time sufficient to substantially fill-up said mold cavity to said congruent surface with said oxidation reaction product, thereby producing a ceramic component having a shaped surface replicating said shape-defining surface; and (g) recovering said ceramic component having said shaped surface.
Claim 2
Independent Claim
330 words
A method for producing a shaped, self-supporting ceramic component comprising the oxidation reaction product of a parent metal, said method comprising: (a) providing a body of parent metal and an expendable pattern having a shape-defining surface shaped outwardly from said body of parent metal; (b) applying a gas-permeable coating of conformable material to said shape-defining surface to form a congruent surface substantially congruent to and coextensive with said shape-defining surface and disposed oppositely from said body of parent metal such that said expendable pattern defines a volume between said parent metal and said congruent surfce, said gas-permeable coating of conformable material having, at least under the process conditions, a self-bonding support zone immediately adjacent to and coextensive with said shape-defining surface, said support zone providing sufficient cohesive strength and retaining the shape of said congruent surface upon elimination of said expendable pattern; (c) heating said parent metal in the presence of at least a vapor-phase oxidant to a temperature above its melting point but below the melting point of said oxidation reaction product to form a body of molten metal, (d) eliminating said expendable pattern to form said mold cavity; (e) at said temperature (i) reacting said molten metal with said vapor-phase oxidant to form an oxidation reaction product, which product is in contact with and extends between said body of molten metal and said vapor-phase oxidant, and (ii) transporting said molten metal through said oxidation reaction product toward said vapor-phase oxidant and gas-permeable coating of conformable material so that oxidation reaction product continues to form at an interface between said vapor-phase oxidant and previously formed oxidation reaction product, thereby forming a progressively thicker body of said oxidation reaction product into said mold cavity; (f) continuing said reacting for a time sufficient to substantially fill-up said mold cavity to said congruent surface with said oxidation reaction product, thereby producing a ceramic component having a shaped surface replicating said shape-defining surface; and (g) recovering said ceramic component having said shaped surface.
Claim 3
Dependent Claim
85 words
The method of claim 1 including providing a filler material prior to said heating step and positioning said filler between said parent metal and said expendable pattern such that said filler is intermediately disposed between said parent metal and said congruent surface and infiltrating said filler with said oxidation reaction product prior to forming said progressively thicker body of oxidation reaction product into said mold cavity, and recovering said ceramic component having a ceramic composite formed integrally therewith and disposed oppositely from said shaped surface.
Claim 4
Dependent Claim
39 words
The method of claim 1 wherein at least a portion of said gas-permeable coating of conformable material used to establish said congruent surface comprises a barrier material, thereby inhibiting growth of said oxidation reaction product beyond said congruent surface.
Claim 5
Dependent Claim
70 words
The method of claim 1 wherein said gas-permeable coating of conformable material comprises a filler which is permeable to growth of said oxidation reaction product therethrough, and including growing said oxidation reaction product beyond said congruent surface and into said filler to embed at least a portion of said filler within said oxidation reaction product, whereby said ceramic component is recovered having a ceramic composite integral with said shaped surface.
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein said parent metal is selected from the group consisting of silicon, titanium, tin, zirconium, and hafnium.
Claim 7
Dependent Claim
22 words
The method of claim 2 wherein said parent metal is selected from the group consisting of silicon, titanium, tin, zirconium, and hafnium.
Claim 8
Dependent Claim
22 words
The method of claim 3 wherein said parent metal is selected from the group consisting of silicon, titanium, tin, zirconium, and hafnium.
Claim 9
Dependent Claim
22 words
The method of claim 4 wherein said parent metal is selected from the group consisting of silicon, titanium, tin, zirconium, and hafnium.
Claim 10
Dependent Claim
11 words
The method of claim 1 wherein said parent metal is aluminum.
Claim 11
Dependent Claim
11 words
The method of claim 2 wherein said parent metal is aluminum.
Claim 12
Dependent Claim
11 words
The method of claim 3 wherein said parent metal is aluminum.
Claim 13
Dependent Claim
11 words
The method of claim 4 wherein said parent metal is aluminum.
Claim 14
Dependent Claim
16 words
The method of claim 9, 10, 11 or 12 wherein said oxidant comprises an oxygen-containing gas.
Claim 15
Dependent Claim
10 words
The method of claim 13 wherein said oxidant comprises air.
Claim 16
Dependent Claim
17 words
The method of claim 14 wherein said temperature region is from about 850° C. to 1450° C.
Claim 17
Independent Claim
22 words
The method of any one of claims 5, 6, 7, or 8 including using a dopant in conjunction with said parent metal.
Claim 18
Dependent Claim
24 words
The method of claim 1 including incorporating a bonding agent into said gas-permeable coating of conformable material at least in said support zone thereof.
Claim 19
Dependent Claim
24 words
The method of claim 3 including incorporating a bonding agent into said gas-permeable coating of conformable material at least in said support zone thereof.
Claim 20
Dependent Claim
24 words
The method of claim 4 including incorporating a bonding agent into said gas-permeable coating of conformable material at least in said support zone thereof.
Claim 21
Dependent Claim
34 words
The method of claim 9 including applying a barrier material to the surface of said filler oppositely disposed from said shaped-defining surface, thereby inhibiting growth of said oxidation reaction product at said barrier material.
Claim 22
Dependent Claim
21 words
The method according to claim 20 wherein said barrier material comprises plaster of paris, Portland cement, calcium silicate, and mixtures thereof.
Claim 23
Dependent Claim
21 words
The method according to claim 18 wherein said barrier material comprises plaster of paris, Portland cement, calcium silicate, and mixtures thereof.
Claim 24
Dependent Claim
29 words
The method according to claim 1 wherein said parent metal is aluminum, said oxidant is an oxygen-containing gas, and including using a dopant in conjunction with said parent metal.
Claim 25
Dependent Claim
23 words
The method of claim 1 wherein said expendable pattern comprises a material selected from the group consisting of expanded polystyrene, polyurethane, and polyethylene.
Claim 26
Dependent Claim
26 words
The method of claim 17, 18, or 19 wherein said bonding agent comprises a material selected from the group consisting of silica, Kaolin, and mixtures thereof.
Claim 27
Dependent Claim
13 words
The method of claim 2 wherein said filler comprises alumina or silicon carbide.
Claim 28
Dependent Claim
13 words
The method of claim 4 wherein said filler comprises alumina or silicon carbide.
Claim 29
Dependent Claim
49 words
The method of claim 2 or claim 4 including providing a source of a solid oxidant and incorporating said source into said filler and reacting said source with said parent metal wherein said solid oxidant is employed in conjunction with said vapor-phase oxidant to form said oxidation reaction product.
Claim 30
Dependent Claim
49 words
The method of claim 2 or claim 4 including providing a source of a liquid oxidant and incorporating said source into said filler and reacting said source with said parent metal wherein said liquid oxidant is employed in conjunction with said vapor-phase oxidant to form said oxidation reaction product.
References Cited (Backward Citations)
US2741822A
Cited
US3255027A
Cited
US3298842A
Cited
US3296002A
Cited
US3419404A
Cited
US3473987A
Cited
US3421863A
Cited
US3437468A
Cited
US3789096A
Cited
US3473938A
Cited
US3538231A
Cited
US3864154A
Cited
US4055451A
Cited
US3973977A
Cited
EP0116809A1
Cited
EP0155831A2
Cited
US4647414A
Cited
EP0169067A2
Cited
US4657876A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-15 | 1992-11-14 | 1993-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-15 | 1996-11-14 | 1997-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-15 | 2000-11-14 | 2001-05-16 | $7700.00 | Window Closed / Lapsed |