Process for the preparation of an isocyanurate modified polyurethane foam and the resulting foam
Assignee: Lohja Oy AB
•
Filing: 1987-01-22
•
Granted: 1989-05-09
•
Expires: 2007-01-22
Abstract
Abstract The invention relates to a process for the preparation of novel isocyanurate modified polyurethane foams, which process is characterized in that an organic polyisocyanate is reacted with a polyol in the presence of a catalyst system and a blowing agent, eventually in the presence of a filler material and/or an emulsifying agent, wherein said polyol contains 5 to 100% by weight of an oil, resin or a mixture of resins originating from soft wood and/or a chemically modified resin or oil, and wherein said polyol contains in its molecular structures hydroxl groups capable of reacting with isocyanate groups, and the catalyst system contains 5 to 95% by weight of trimerization catalyst of the polyisocyanate, which catalyst causes cross-linked polyisocyanurate structures containing isocyanurate rings to be formed from the polyisocyanate in the polymer structure, and to novel isocyanurate modified polyurethane foams prepared by the process.
Inventors
- 👤 Pertti Tormala
- 👤 Timo Pohjonen
- 👤 Aimo Ihanamaki
- 👤 Eero Jormalainen
- 👤 Kauko Linna
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:48
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/30; C08G18/36; C08G18/40; C08G18/48; C08G18/4891; C08G18/64; C08G18/6492; C08G2110/00; C08G2110/0008; C08G2110/0016; C08G2110/0025; C08G2115/00; C08G2115/02; Y; Y10; Y10S; Y10S521/00; Y10S521/902
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
175 words
A process for the preparation of an isocyanurate modified polyurethane foam, characterized in that an organic polyisocyanate is reacted with a polyol in the presence of a catalyst system and a blowing agent, eventually in the presence of a material selected from the group consisting of a filler, an emulsifying agent and mixtures thereof, wherein said polyol contains 5 to 100% by weight of a material originating from soft wood selected from the group consisting of an oil, resin, mixture of resins, derivatives thereof and mixtures thereof and wherein said polyol contains in its molecular structures hydroxyl groups capable of reacting with isocyanate groups, and that the catalyst system comprises at least one polyurethane foaming catalyst and 5 to 95% by weight, based on the total amount of the catalyst system, of a trimerization catalyst of the polyisocyanate, said trimerization catalyst selected from the group consisting of an alkali metal carboxylate, 1,3,5-tris((N,N-dimethyl-3-amino)propyl)-s-hexahydrotriazene, N-(2-hydroxyethyl)-aziridine and 2,4,6-tris-(dimethylaminomethyl)phenol, which trimerization catalyst causes cross-linked polyisocyanurate structures containing isocyanurate rings to be formed from the polyisocyanate in the polymer structure.
Claim 2
Dependent Claim
175 words
A process for the preparation of an isocyanurate modified polyurethane foam, characterized in that an organic polyisocyanate is reacted with a polyol in the presence of a catalyst system and a blowing agent, eventually in the presence of a material selected from the group consisting of a filler, an emulsifying agent and mixtures thereof, wherein said polyol contains 5 to 100% by weight of a material originating from soft wood selected from the group consisting of an oil, resin, mixture of resins, derivatives thereof and mixtures thereof and wherein said polyol contains in its molecular structures hydroxyl groups capable of reacting with isocyanate groups, and that the catalyst system comprises at least one polyurethane foaming catalyst and 5 to 95% by weight, based on the total amount of the catalyst system, of a trimerization catalyst of the polyisocyanate, said trimerization catalyst selected from the group consisting of an alkali metal carboxylate, 1,3,5-tris((N,N-dimethyl-3-amino)propyl)-s-hexahydrotriazene, N-(2-hydroxyethyl)-aziridine and 2,4,6-tris-(dimethylaminomethyl)phenol, which trimerization catalyst causes cross-linked polyisocyanurate structures containing isocyanurate rings to be formed from the polyisocyanate in the polymer structure.
Claim 3
Dependent Claim
20 words
A process according to claim 1, characterized in that the polyol contains 5 to 100% by weight of tall resin.
Claim 4
Dependent Claim
21 words
A process according to claim 1, characterized in that the polyol contains 5 to 100% by weight of wood extract resin.
Claim 5
Dependent Claim
20 words
A process according to claim 1, characterized in that the polyol contains 5 to 100% by weight of gum resin.
Claim 6
Dependent Claim
22 words
A process according to claim 1, characterized in that the polyol contains 5 to 100% by weight of a mixture of resins.
Claim 7
Dependent Claim
20 words
A process according to claim 1, characterized in that the polyol contains a derivative of a resin originating from wood.
Claim 8
Dependent Claim
17 words
A process according to claim 1, characterized in that the trimerization catalyst is an alkali metal carboxylate.
Claim 9
Dependent Claim
34 words
A process according to any one of claims 1 to 7, characterized in that a powder-like mineral filler material is added to the mixture to be foamed or to one component of said mixture.
Claim 10
Dependent Claim
15 words
A process according to claim 1, characterized in that the filler material is aluminum hydroxide.
Claim 11
Dependent Claim
68 words
An isocyanurate modified polyurethane foam prepared by the process according to claim 1, characterized in that it is formed of the reaction product of an organic polyisocyanate and a polyol, the reaction product being crosslinked by said catalyst system containing said trimerization catalyst of the polyisocyanate, and eventually of a filler material, wherein said polyol contains 5 to 100% by weight of an organic material originating from wood.
Claim 12
Dependent Claim
32 words
A process according to claim 7, characterized in that the trimerization catalyst is an alkali metal carboxylate selected from the group consisting of an alkali metal acetate and an alkali metal formate.
Claim 13
Dependent Claim
40 words
A process according to claim 1, characterized in that the said at least one polyurethane foaming catalyst is selected from the group consisting of stannous compounds, amines, alkanol amines, mixtures of said stannous compounds and said amines and reactive catalysts.
Claim 14
Dependent Claim
39 words
A process according to claim 12, characterized in that said polyurethane foaming catalyst is selected from the group consisting of stannous oleate, stannous octoate, dibutyl tin laurate, triethylene diamine, dimethyl cyclohexyl amine, N,N,N',N'-tetramethyl-1,3-butane diamine, N-methylmorpholine and n-butyl acid phosphate.
Claim 15
Dependent Claim
15 words
A process according to claim 12 wherein said trimerization catalyst is an alkyl metal carboxylate.
Claim 16
Dependent Claim
15 words
A process according to claim 13 wherein said trimerization catalyst is an alkyl metal carboxylate.
References Cited (Backward Citations)
US3051601A
Cited
US3248348A
Cited
US3211674A
Cited
GB1170079A
Cited
US3423339A
Cited
US4405725A
Cited
US3637540A
Cited
GB1405434A
Cited
GB1390231A
Cited
US3860565A
Cited
GB1471842A
Cited
US4271273A
Cited
US4374204A
Cited
US4359550A
Cited
US4521544A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |