Low temperature sintering ceramic material composition and process for producing the low temperature sintering ceramic
Assignee: Denso Corp
•
Filing: 1987-09-01
•
Granted: 1989-05-09
•
Expires: 2007-09-01
Abstract
Abstract A low temperature sintering ceramic material, having low temperature sinterability and excellent thermal conductivity, is particularly suitable for use in making an IC substrate of a ceramic printed plate board. This low temperature sintering ceramic material has two composition types. One is a binary composition type ceramic material consisting essentially of MgO and B 2 O 3 , and the other is a ternary composition type ceramic material composed of principal components consisting of MgO and B 2 O 3 and assisting components consisting of one or more selected from Li 2 O, Na 2 O, K 2 O, a fluoride of an alkali metal and a fluoride of an alkaline earth metal. After sintering, MgO and B 2 O 3 are respectively contained at 50 to 90 mol% and 10 to 50 mol% on 100 mol% of the total amount of MgO and B 2 O 3 .
Inventors
- 👤 Nobuaki Kawahara
- 👤 Hiroki Hoshizaki
- 👤 Hirofumi Suzuki
- 👤 Kiyomi Kobayashi
- 👤 Makoto Ohkawa
- 👤 Mitsuru Asano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 19:48
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/03; C04B35/04; C04B35/053; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
258 words
A composition for low temperature sintering ceramic materials which are used as a printed plate body composed of principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide (MgO) by calcining and a boron oxide precursor material changed to boron oxide (B 2 O 3 ) by calcining and assisting compound materials consisting essentially of one or more selected from the group consisting of a lithium oxide precursor material changed to lithium oxide (Li 2 O) by calcining, a sodium oxide precursor material changed to sodium oxide (Na 2 O) by calcining, a potassium oxide precursor material changed to potassium oxide (K 2 O) by calcining, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, wherein said principal compound materials are not more than 99 mol % and said assisting compound materials are not less than 1 mol % based on 100 mol % of a total amount of said principal and assisting compound materials, said composition is changed to a sintered body made substantially of a crystal phase by sintering and the sintered body consists essentially of magnesium oxide, boron oxide and one or more selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, and a fluoride of an alkaline earth metal and said MgO is 50 to 90 mol % and said BH 2 O 3 is 10 to 50 mol % based on 100 mol % a total amount of said principal compound materials after sintering.
Claim 2
Dependent Claim
258 words
A composition for low temperature sintering ceramic materials which are used as a printed plate body composed of principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide (MgO) by calcining and a boron oxide precursor material changed to boron oxide (B 2 O 3 ) by calcining and assisting compound materials consisting essentially of one or more selected from the group consisting of a lithium oxide precursor material changed to lithium oxide (Li 2 O) by calcining, a sodium oxide precursor material changed to sodium oxide (Na 2 O) by calcining, a potassium oxide precursor material changed to potassium oxide (K 2 O) by calcining, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, wherein said principal compound materials are not more than 99 mol % and said assisting compound materials are not less than 1 mol % based on 100 mol % of a total amount of said principal and assisting compound materials, said composition is changed to a sintered body made substantially of a crystal phase by sintering and the sintered body consists essentially of magnesium oxide, boron oxide and one or more selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, and a fluoride of an alkaline earth metal and said MgO is 50 to 90 mol % and said BH 2 O 3 is 10 to 50 mol % based on 100 mol % a total amount of said principal compound materials after sintering.
Claim 3
Dependent Claim
220 words
A composition for low temperature sintering ceramic materials which are used as a printed plate body composed of principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide (MgO) by calcining and a boron oxide precursor material changed to boron oxide (B 2 O 3 ) by calcining and assisting compound materials consisting essentially of one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, wherein said principal compound materials as 90 to 99 mol % and said assisting compound materials are 1 to 10 mol % based on 100 mol % of a total of said principal and assisting compound materials, said composition is changed to a sintered body made substantially of a crystal phase by sintering, the sintered body consists essentially of magnesium oxide, boron oxide, and one or more selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, and a fluoride of an alkaline earth metal, and said MgO is 50 to 90 mol % and said B 2 O 3 is 10 to 50 mol % based on 100 mol % of a total amount of said principal compound materials after sintering.
Claim 4
Dependent Claim
220 words
A composition for low temperature sintering ceramic materials which are used as a printed plate body composed of principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide (MgO) by calcining and a boron oxide precursor material changed to boron oxide (B 2 O 3 ) by calcining and assisting compound materials consisting essentially of one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, wherein said principal compound materials as 90 to 99 mol % and said assisting compound materials are 1 to 10 mol % based on 100 mol % of a total of said principal and assisting compound materials, said composition is changed to a sintered body made substantially of a crystal phase by sintering, the sintered body consists essentially of magnesium oxide, boron oxide, and one or more selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, and a fluoride of an alkaline earth metal, and said MgO is 50 to 90 mol % and said B 2 O 3 is 10 to 50 mol % based on 100 mol % of a total amount of said principal compound materials after sintering.
Claim 5
Dependent Claim
224 words
A composition for low temperature sintering ceramic materials which are used as a printed plate body composed of principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide (MgO) by calcining and a boron oxide precursor material changed to boron oxide (B 2 O 3 ) by calcining and assisting compound materials consisting essentially of a fluoride of an alkaline earth metal and optionally one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, and a fluoride of an alkali metal, wherein said principal compound materials are 85 to 99 mol % and said assisting compound materials are 1 to 15 mol % based on 100 mol % of a total of said principal and assisting compound materials, said composition is changed to a sintered body made substantially of a crystal phase by sintering, the sintered body consists essentially of magnesium oxide, boron oxide, and a fluoride of an alkaline earth metal and optionally one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, and said MgO is 50 to 90 mol % and said B 2 O 3 is 10 to 50 mol % based on 100 mol % of a total amount of said principal compound materials after sintering.
Claim 6
Dependent Claim
224 words
A composition for low temperature sintering ceramic materials which are used as a printed plate body composed of principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide (MgO) by calcining and a boron oxide precursor material changed to boron oxide (B 2 O 3 ) by calcining and assisting compound materials consisting essentially of a fluoride of an alkaline earth metal and optionally one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, and a fluoride of an alkali metal, wherein said principal compound materials are 85 to 99 mol % and said assisting compound materials are 1 to 15 mol % based on 100 mol % of a total of said principal and assisting compound materials, said composition is changed to a sintered body made substantially of a crystal phase by sintering, the sintered body consists essentially of magnesium oxide, boron oxide, and a fluoride of an alkaline earth metal and optionally one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, and said MgO is 50 to 90 mol % and said B 2 O 3 is 10 to 50 mol % based on 100 mol % of a total amount of said principal compound materials after sintering.
Claim 7
Dependent Claim
215 words
A process for producing a low temperature sintered ceramic body consisting essentially of magnesium oxide, boron oxide and one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, said process consisting essentially of the steps of: (1) mixing principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide by calcining and a boron oxide precursor material changed to boron oxide by calcining and assisting compound materials consisting essentially of one or more materials selected from lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, to contain 50 to 90 mol % of said magnesium oxide and 10 to 50 mol % of said boron oxide based on 100 mol % of a total amount of said principal compound materials after sintering, said principal compound materials being 90 to 99 mol % and said assisting compound materials being 1 to 10 mol % based on 100 mol % of a total of said principal and assisting compound materials, (2) calcining the obtained mixture, (3) moulding the calcined mixture under pressure, and (4) sintering at temperatures of 900° to 1100° C.
Claim 8
Dependent Claim
215 words
A process for producing a low temperature sintered ceramic body consisting essentially of magnesium oxide, boron oxide and one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, said process consisting essentially of the steps of: (1) mixing principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide by calcining and a boron oxide precursor material changed to boron oxide by calcining and assisting compound materials consisting essentially of one or more materials selected from lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal and a fluoride of an alkaline earth metal, to contain 50 to 90 mol % of said magnesium oxide and 10 to 50 mol % of said boron oxide based on 100 mol % of a total amount of said principal compound materials after sintering, said principal compound materials being 90 to 99 mol % and said assisting compound materials being 1 to 10 mol % based on 100 mol % of a total of said principal and assisting compound materials, (2) calcining the obtained mixture, (3) moulding the calcined mixture under pressure, and (4) sintering at temperatures of 900° to 1100° C.
Claim 9
Dependent Claim
218 words
A process for producing a low temperature sintered ceramic body consisting essentially of magnesium oxide, boron oxide and a fluoride of an alkaline earth metal and optionally one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide and a fluoride of an alkali metal, said process consisting essentially of the steps of: (1) mixing principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide by calcining and a boron oxide precursor material changed to boron oxide by calcining and assisting compound materials consisting essentially of a fluoride of an alkaline earth metal and optionally one or more materials selected from lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, to contain 50 to 90 mol % of said magnesium oxide and 10 to 50 mol % of said boron oxide based on 100 mol % of the total amount of said principal compound materials after sintering, said principal compound materials being 85 to 99 mol % and said assisting compound materials being 1 to 15 mol % based on 100 mol % of the total of said principal and assisting compound materials, (2) calcining the obtained mixture, (3) moulding the calcined mixture under pressure, and (4) sintering at temperatures of 900° to 1100° C.
Claim 10
Dependent Claim
218 words
A process for producing a low temperature sintered ceramic body consisting essentially of magnesium oxide, boron oxide and a fluoride of an alkaline earth metal and optionally one or more materials selected from the group consisting of lithium oxide, sodium oxide, potassium oxide and a fluoride of an alkali metal, said process consisting essentially of the steps of: (1) mixing principal compound materials consisting essentially of a magnesium oxide precursor material changed to magnesium oxide by calcining and a boron oxide precursor material changed to boron oxide by calcining and assisting compound materials consisting essentially of a fluoride of an alkaline earth metal and optionally one or more materials selected from lithium oxide, sodium oxide, potassium oxide, a fluoride of an alkali metal, to contain 50 to 90 mol % of said magnesium oxide and 10 to 50 mol % of said boron oxide based on 100 mol % of the total amount of said principal compound materials after sintering, said principal compound materials being 85 to 99 mol % and said assisting compound materials being 1 to 15 mol % based on 100 mol % of the total of said principal and assisting compound materials, (2) calcining the obtained mixture, (3) moulding the calcined mixture under pressure, and (4) sintering at temperatures of 900° to 1100° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-05-08 | 1992-11-07 | 1993-05-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-05-08 | 1996-11-07 | 1997-05-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-05-08 | 2000-11-07 | 2001-05-09 | $7700.00 | Window Closed / Lapsed |